Matching Items (2)
154288-Thumbnail Image.png
Description
Characterization and modeling of deformation and failure in metallic materials under extreme conditions, such as the high loads and strain rates found under shock loading due to explosive detonation and high velocity-impacts, are extremely important for a wide variety of military and industrial applications. When a shock wave causes stress

Characterization and modeling of deformation and failure in metallic materials under extreme conditions, such as the high loads and strain rates found under shock loading due to explosive detonation and high velocity-impacts, are extremely important for a wide variety of military and industrial applications. When a shock wave causes stress in a material that exceeds the elastic limit, plasticity and eventually spallation occur in the material. The process of spall fracture, which in ductile materials stems from strain localization, void nucleation, growth and coalescence, can be caused by microstructural heterogeneity. The analysis of void nucleation performed from a microstructurally explicit simulation of a spall damage evolution in a multicrystalline copper indicated triple junctions as the preferred sites for incipient damage nucleation revealing 75% of them with at least two grain boundaries with misorientation angle between 20-55°. The analysis suggested the nature of the boundaries connecting at a triple junction is an indicator of their tendency to localize spall damage. The results also showed that damage propagated preferentially into one of the high angle boundaries after voids nucleate at triple junctions. Recently the Rayleigh-Taylor Instability (RTI) and the Richtmyer-Meshkov Instability (RMI) have been used to deduce dynamic material strength at very high pressures and strain rates. The RMI is used in this work since it allows using precise diagnostics such as Transient Imaging Displacement Interferometry (TIDI) due to its slower linear growth rate. The Preston-Tonks-Wallace (PTW) model is used to study the effects of dynamic strength on the behavior of samples with a fed-thru RMI, induced via direct laser drive on a perturbed surface, on stability of the shock front and the dynamic evolution of the amplitudes and velocities of the perturbation imprinted on the back (flat) surface by the perturbed shock front. Simulation results clearly showed that the amplitude of the hydrodynamic instability increases with a decrease in strength and vice versa and that the amplitude of the perturbed shock front produced by the fed-thru RMI is also affected by strength in the same way, which provides an alternative to amplitude measurements to study strength effects under dynamic conditions. Simulation results also indicate the presence of second harmonics in the surface perturbation after a certain time, which were also affected by the material strength.
ContributorsGautam, Sudrishti (Author) / Peralta, Pedro (Thesis advisor) / Oswald, Jay (Committee member) / Solanki, Kiran (Committee member) / Arizona State University (Publisher)
Created2016
155622-Thumbnail Image.png
Description
Laboratory testing was conducted to quantify strain concentrations adjacent to seams and scratches in high density polyethylene (HDPE) geomembranes. The tensile strain profile of remnants meeting the ASTM criteria for wide-width tensile testing from samples of field seams recovered for construction quality assurance testing was evaluated using digital image correlation

Laboratory testing was conducted to quantify strain concentrations adjacent to seams and scratches in high density polyethylene (HDPE) geomembranes. The tensile strain profile of remnants meeting the ASTM criteria for wide-width tensile testing from samples of field seams recovered for construction quality assurance testing was evaluated using digital image correlation (DIC). Strains adjacent to scratches on laboratory prepared samples loaded in tension were also measured using DIC. The tensile strain in the zone adjacent to a seam and the tensile strain adjacent to a scratch were compared to the tensile strains calculated using theoretical strain concentration factors. The relationship between the maximum tensile strain adjacent to a seam and the global nominal strain in the sample was quantified for textured and smooth geomembranes of common thicknesses. Using statistical analysis of the data, bounds were developed for the allowable nominal tensile strain expected to induce maximum tensile strains adjacent to the seam less than or equal to the typical yield strain of HDPE geomembranes, at several confidence levels. Where nominal strain is the global or average strain applied to the sample and maximum strain is the largest tensile strain induced in the sample.

The reduction in the nominal yield strain due to a scratch in a HDPE geomembrane was also quantified. The yield strain was approximately the same as predicted using theoretical strain concentration factors. The difference in the average measured maximum strains adjacent to the seams of textured and smooth HDPE geomembranes was found to be statistically insignificant. However, maximum strains adjacent to extrusion welded seams were somewhat greater than adjacent to fusion welded seams for nominal strains on the order of 3% to 4%. The results of the testing program suggest that the nominal tensile strain should be limited to 4% around dual hot wedge seams and 3% around extrusion fillet seams to avoid maximum strains equal to 11%, a typical yield strain for HDPE geomembranes.
ContributorsAndresen, Jake (Author) / Kavazanjian, Edward (Thesis advisor) / Houston, Sandra (Committee member) / Zapata, Claudia (Committee member) / Arizona State University (Publisher)
Created2017