Matching Items (23)
Description
Fluctuation Electron Microscopy (FEM) has become an effective materials' structure characterization technique, capable of probing medium-range order (MRO) that may be present in amorphous materials. Although its sensitivity to MRO has been exercised in numerous studies, FEM is not yet a quantitative technique. The holdup has been the discrepancy between the computed kinematical variance and the experimental variance, which previously was attributed to source incoherence. Although high-brightness, high coherence, electron guns are now routinely available in modern electron microscopes, they have not eliminated this discrepancy between theory and experiment. The main objective of this thesis was to explore, and to reveal, the reasons behind this conundrum.
The study was started with an analysis of the speckle statistics of tilted dark-field TEM images obtained from an amorphous carbon sample, which confirmed that the structural ordering is sensitively detected by FEM. This analysis also revealed the inconsistency between predictions of the source incoherence model and the experimentally observed variance.
FEM of amorphous carbon, amorphous silicon and ultra nanocrystalline diamond samples was carried out in an attempt to explore the conundrum. Electron probe and sample parameters were varied to observe the scattering intensity variance behavior. Results were compared to models of probe incoherence, diffuse scattering, atom displacement damage, energy loss events and multiple scattering. Models of displacement decoherence matched the experimental results best.
Decoherence was also explored by an interferometric diffraction method using bilayer amorphous samples, and results are consistent with strong displacement decoherence in addition to temporal decoherence arising from the electron source energy spread and energy loss events in thick samples.
It is clear that decoherence plays an important role in the long-standing discrepancy between experimental FEM and its theoretical predictions.
The study was started with an analysis of the speckle statistics of tilted dark-field TEM images obtained from an amorphous carbon sample, which confirmed that the structural ordering is sensitively detected by FEM. This analysis also revealed the inconsistency between predictions of the source incoherence model and the experimentally observed variance.
FEM of amorphous carbon, amorphous silicon and ultra nanocrystalline diamond samples was carried out in an attempt to explore the conundrum. Electron probe and sample parameters were varied to observe the scattering intensity variance behavior. Results were compared to models of probe incoherence, diffuse scattering, atom displacement damage, energy loss events and multiple scattering. Models of displacement decoherence matched the experimental results best.
Decoherence was also explored by an interferometric diffraction method using bilayer amorphous samples, and results are consistent with strong displacement decoherence in addition to temporal decoherence arising from the electron source energy spread and energy loss events in thick samples.
It is clear that decoherence plays an important role in the long-standing discrepancy between experimental FEM and its theoretical predictions.
ContributorsRezikyan, Aram (Author) / Treacy, Michael M.J. (Thesis advisor) / Smith, David J. (Committee member) / McCartney, Martha R. (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2015
Raman spectroscopy characterization of anharmonicity and alloying effects in semiconductor materials
Description
The chemical sensitivity and spatial resolution of Raman spectroscopy, combined with the sensitivity of modern systems that can easily detect single atomic layers, have made this technique a preferred choice for the strain characterization of complex systems such as nanoscale complementary metal-oxide-semiconductor - CMOS - devices. A disadvantage of Raman spectroscopy, however, is that the shifts associated with strain are not related to the geometrical deformations in any obvious way, so that careful calibrations are needed to determine the anharmonic coefficients (p, q and r) that relate strain to Raman shifts. A new set of measurements of the Raman shift in strained Ge films grown on relaxed SiGe buffer layers deposited on Si substrates is presented, and thereby, a new consistent set of values for the parameters p and q for Ge has been proposed. In this dissertation the study of the vibrational properties of Ge1-xSnx alloys has also been reported. The temperature dependence of the Raman spectrum of Ge-rich Ge1-x Snx and Ge1-x-ySi xSny alloys has been determined in the 10 K - 450 K range. The Raman line shift and width changes as a function of temperature are found to be virtually identical to those observed in bulk Ge. This result shows that the anharmonic decay process responsible for the temperature dependence is extremely robust against the alloy perturbation.
ContributorsBagchi, Sampriti (Author) / Menéndez, Jose (Thesis advisor) / Treacy, Michael (Committee member) / Ponce, Fernando (Committee member) / Tsen, Kong-Thon (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2011
Description
In this work, a new method, "Nanobonding" [1,2] is conceived and researched to bond Si-based surfaces, via nucleation and growth of a 2 D silicon oxide SiOxHx interphase connecting the surfaces at the nanoscale across macroscopic domains. Nanobonding cross-bridges two smooth surfaces put into mechanical contact in an O2/H2O mixed ambient below T <200 °C via arrays of SiOxHx molecules connecting into a continuous macroscopic bonding interphase. Nano-scale surface planarization via wet chemical processing and new spin technology are compared via Tapping Mode Atomic Force Microscopy (TMAFM) , before and after nano-bonding. Nanobonding uses precursor phases, 2D nano-films of beta-cristobalite (beta-c) SiO2, nucleated on Si(100) via the Herbots-Atluri (H-A) method [1]. beta-c SiO2 on Si(100) is ordered and flat with atomic terraces over 20 nm wide, well above 2 nm found in native oxides. When contacted with SiO2 this ultra-smooth nanophase can nucleate and grow domains with cross-bridging molecular strands of hydroxylated SiOx, instead of point contacts. The high density of molecular bonds across extended terraces forms a strong bond between Si-based substrates, nano- bonding [2] the Si and silica. A new model of beta-cristobalite SiO2 with its <110> axis aligned along Si[100] direction is simulated via ab-initio methods in a nano-bonded stack with beta-c SiO2 in contact with amorphous SiO2 (a-SiO2), modelling cross-bridging molecular bonds between beta-c SiO2 on Si(100) and a-SiO2 as during nanobonding. Computed total energies are compared with those found for Si(100) and a-SiO2 and show that the presence of two lattice cells of !-c SiO2 on Si(100) and a-SiO2 lowers energy when compared to Si(100)/ a-SiO2 Shadow cone calculations on three models of beta-c SiO2 on Si(100) are compared with Ion Beam Analysis of H-A processed Si(100). Total surface energy measurements via 3 liquid contact angle analysis of Si(100) after H-A method processing are also compared. By combining nanobonding experiments, TMAFM results, surface energy data, and ab-initio calculations, an atomistic model is derived and nanobonding is optimized. [1] US Patent 6,613,677 (9/2/03), 7,851,365 (12/14/10), [2] Patent Filed: 4/30/09, 10/1/2011
ContributorsWhaley, Shawn D (Author) / Culbertson, Robert J. (Thesis advisor) / Herbots, Nicole (Committee member) / Rez, Peter (Committee member) / Marzke, Robert F (Committee member) / Lindsay, Stuart (Committee member) / Chamberlin, Ralph V (Committee member) / Arizona State University (Publisher)
Created2011
Description
One of the most important issues in femtosecond free electron laser X-ray diraction is to reconstruct the 3D charge density of molecule from a mass of diraction snapshots. In order to determine the orientation of single molecule from diraction patterns, we rst determine the moments and products of inertia of this from 2D experiment data (diraction patterns or EM images to obtain the elements of the inertia tensor. If diraction patterns from uniformly random orientations or some preferred orientations are collected, the principal axes of the molecule can be extracted, together with the Euler angles which relate the principal axes of the molecule to the laboratory frame axes. This is achieved by nding the maximum and minimum values for the measured moments from many single-molecule patterns. Simulations for GroEL protein indicates that the calculation of the autocorrelation help eliminate the Poisson noise in Cryo- EM images and can make correct orientation determination. The eect of water jacket surrounding the protein molecule is studied based on molecular dynamics simulation result. The intensities from water and interference is found to suppress those from protein itself. A method is proposed and applied to the simulation data to show the possibility for it to overcome the water background problem. The scattering between Bragg re ections from nanocrystals is used to aid solution of the phase problem. We describe a method for reconstructing the charge density of a typical molecule within a single unit cell, if suciently nely-sampled diraction data are available from many nanocrystals of dierent sizes lying in the same orientations without knowledge of the distribution of particle size or requiring atomic-resolution data. Triple correlation of the diraction patterns are made use of to reconiii
ContributorsWang, Xiaoyu (Author) / Spence, John C.H. (Thesis advisor) / Schmidt, Kevin (Committee member) / Doak, R. Bruce (Committee member) / Weierstall, Uwe (Committee member) / Ros, Robert (Committee member) / Arizona State University (Publisher)
Created2011
Description
Many species e.g. sea urchin form amorphous calcium carbonate (ACC) precursor phases that subsequently transform into crystalline CaCO3. It is certainly possible that the biogenic ACC might have more than 10 wt% Mg and ∼ 3 wt% of water. The structure of ACC and the mechanisms by which it transforms to crystalline phase are still poorly understood. In this dissertation our goal is to determine an atomic structure model that is consistent with diffraction and IR measurements of ACC. For this purpose a calcite supercell with 24 formula units, containing 120 atoms, was constructed. Various configurations with substitution of Ca by 6 Mg ions (6 wt.%) and insertion of 3-5 H2O molecules (2.25-3.75 wt.%) in the interstitial positions of the supercell, were relaxed using a robust density function code VASP. The most noticeable effects were the tilts of CO3 groups and the distortion of Ca sub-lattice, especially in the hydrated case. The distributions of Ca-Ca nearest neighbor distance and CO3 tilts were extracted from various configurations. The same methods were also applied to aragonite. Sampling from the calculated distortion distributions, we built models for amorphous calcite/aragonite of size ∼ 1700 nm3 based on a multi-scale modeling scheme. We used these models to generate diffraction patterns and profiles with our diffraction code. We found that the induced distortions were not enough to generate a diffraction profile typical of an amorphous material. We then studied the diffraction profiles from several nano-crystallites as recent studies suggest that ACC might be a random array of nanocryatallites. It was found that the generated diffraction profile from a nano-crystallite of size ∼ 2 nm3 is similar to that from the ACC.
ContributorsSinha, Sourabh (Author) / Rez, Peter (Thesis advisor) / Bearat, Hamdallah A. (Committee member) / Bennett, Peter A. (Committee member) / McCartney, Martha R. (Committee member) / Peng, Xihong (Committee member) / Arizona State University (Publisher)
Created2012
Description
A system for illuminating a sample in situ with visible and UV light inside a transmission electron microscope was devised to study photocatalysts. There are many factors which must be considered when designing and building such a system. These include both mechanical, optical, and electron optical considerations. Some of the restrictions posed by the electron microscope column are significant, and care must be taken not to degrade the microscope's electron optical performance, or to unduly restrict the other current capabilities of the microscope. The nature of these various design considerations is discussed in detail. A description of the system that has been added to the microscope at ASU, an FEI Tecnai F20 environmental transmission electron microscope is also given. The system includes a high brightness broadband light source with optical filters, a fiber to guide the light to the sample, and a system for precisely aligning the fiber tip. The spatial distribution and spectrum of the light reaching the sample has been characterized, and is described in detail.
ContributorsMiller, Benjamin (Author) / Crozier, Peter A. (Thesis advisor) / McCartney, Martha (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2012
Description
The goal of this theoretical study of infrared spectra was to ascertain to what degree molecules may be identified from their IR spectra and which spectral regions are best suited for this purpose. The frequencies considered range from the lowest frequency molecular vibrations in the far-IR, terahertz region (below ~3 THz or 100 cm-1) up to the highest frequency vibrations (~120 THz or 4000 cm-1). An emphasis was placed on the IR spectra of chemical and biological threat molecules in the interest of detection and prevention. To calculate IR spectra, the technique of normal mode analysis was applied to organic molecules ranging in size from 8 to 11,352 atoms. The IR intensities of the vibrational modes were calculated in terms of the derivative of the molecular dipole moment with respect to each normal coordinate. Three sets of molecules were studied: the organophosphorus G- and V-type nerve agents and chemically related simulants (15 molecules ranging in size from 11 to 40 atoms); 21 other small molecules ranging in size from 8 to 24 atoms; and 13 proteins ranging in size from 304 to 11,352 atoms. Spectra for the first two sets of molecules were calculated using quantum chemistry software, the last two sets using force fields. The "middle" set used both methods, allowing for comparison between them and with experimental spectra from the NIST/EPA Gas-Phase Infrared Library. The calculated spectra of proteins, for which only force field calculations are practical, reproduced the experimentally observed amide I and II bands, but they were shifted by approximately +40 cm-1 relative to experiment. Considering the entire spectrum of protein vibrations, the most promising frequency range for differentiating between proteins was approximately 600-1300 cm-1 where water has low absorption and the proteins show some differences.
ContributorsMott, Adam J (Author) / Rez, Peter (Thesis advisor) / Ozkan, Banu (Committee member) / Shumway, John (Committee member) / Thorpe, Michael (Committee member) / Vaiana, Sara (Committee member) / Arizona State University (Publisher)
Created2012
Description
Photosystem II (PSII) is a large protein-cofactor complex. The first step in
photosynthesis involves the harvesting of light energy from the sun by the antenna (made
of pigments) of the PSII trans-membrane complex. The harvested excitation energy is
transferred from the antenna complex to the reaction center of the PSII, which leads to a
light-driven charge separation event, from water to plastoquinone. This phenomenal
process has been producing the oxygen that maintains the oxygenic environment of our
planet for the past 2.5 billion years.
The oxygen molecule formation involves the light-driven extraction of 4 electrons
and protons from two water molecules through a multistep reaction, in which the Oxygen
Evolving Center (OEC) of PSII cycles through 5 different oxidation states, S0 to S4.
Unraveling the water-splitting mechanism remains as a grant challenge in the field of
photosynthesis research. This requires the development of an entirely new capability, the
ability to produce molecular movies. This dissertation advances a novel technique, Serial
Femtosecond X-ray crystallography (SFX), into a new realm whereby such time-resolved
molecular movies may be attained. The ultimate goal is to make a “molecular movie” that
reveals the dynamics of the water splitting mechanism using time-resolved SFX (TRSFX)
experiments and the uniquely enabling features of X-ray Free-Electron Laser
(XFEL) for the study of biological processes.
This thesis presents the development of SFX techniques, including development of
new methods to analyze millions of diffraction patterns (~100 terabytes of data per XFEL
experiment) with the goal of solving the X-ray structures in different transition states.
ii
The research comprises significant advancements to XFEL software packages (e.g.,
Cheetah and CrystFEL). Initially these programs could evaluate only 8-10% of all the
data acquired successfully. This research demonstrates that with manual optimizations,
the evaluation success rate was enhanced to 40-50%. These improvements have enabled
TR-SFX, for the first time, to examine the double excited state (S3) of PSII at 5.5-Å. This
breakthrough demonstrated the first indication of conformational changes between the
ground (S1) and the double-excited (S3) states, a result fully consistent with theoretical
predictions.
The power of the TR-SFX technique was further demonstrated with proof-of principle
experiments on Photoactive Yellow Protein (PYP) micro-crystals that high
temporal (10-ns) and spatial (1.5-Å) resolution structures could be achieved.
In summary, this dissertation research heralds the development of the TR-SFX
technique, protocols, and associated data analysis methods that will usher into practice a
new era in structural biology for the recording of ‘molecular movies’ of any biomolecular
process.
photosynthesis involves the harvesting of light energy from the sun by the antenna (made
of pigments) of the PSII trans-membrane complex. The harvested excitation energy is
transferred from the antenna complex to the reaction center of the PSII, which leads to a
light-driven charge separation event, from water to plastoquinone. This phenomenal
process has been producing the oxygen that maintains the oxygenic environment of our
planet for the past 2.5 billion years.
The oxygen molecule formation involves the light-driven extraction of 4 electrons
and protons from two water molecules through a multistep reaction, in which the Oxygen
Evolving Center (OEC) of PSII cycles through 5 different oxidation states, S0 to S4.
Unraveling the water-splitting mechanism remains as a grant challenge in the field of
photosynthesis research. This requires the development of an entirely new capability, the
ability to produce molecular movies. This dissertation advances a novel technique, Serial
Femtosecond X-ray crystallography (SFX), into a new realm whereby such time-resolved
molecular movies may be attained. The ultimate goal is to make a “molecular movie” that
reveals the dynamics of the water splitting mechanism using time-resolved SFX (TRSFX)
experiments and the uniquely enabling features of X-ray Free-Electron Laser
(XFEL) for the study of biological processes.
This thesis presents the development of SFX techniques, including development of
new methods to analyze millions of diffraction patterns (~100 terabytes of data per XFEL
experiment) with the goal of solving the X-ray structures in different transition states.
ii
The research comprises significant advancements to XFEL software packages (e.g.,
Cheetah and CrystFEL). Initially these programs could evaluate only 8-10% of all the
data acquired successfully. This research demonstrates that with manual optimizations,
the evaluation success rate was enhanced to 40-50%. These improvements have enabled
TR-SFX, for the first time, to examine the double excited state (S3) of PSII at 5.5-Å. This
breakthrough demonstrated the first indication of conformational changes between the
ground (S1) and the double-excited (S3) states, a result fully consistent with theoretical
predictions.
The power of the TR-SFX technique was further demonstrated with proof-of principle
experiments on Photoactive Yellow Protein (PYP) micro-crystals that high
temporal (10-ns) and spatial (1.5-Å) resolution structures could be achieved.
In summary, this dissertation research heralds the development of the TR-SFX
technique, protocols, and associated data analysis methods that will usher into practice a
new era in structural biology for the recording of ‘molecular movies’ of any biomolecular
process.
ContributorsBasu, Shibom, 1988- (Author) / Fromme, Petra (Thesis advisor) / Spence, John C.H. (Committee member) / Wolf, George (Committee member) / Ros, Robert (Committee member) / Fromme, Raimund (Committee member) / Arizona State University (Publisher)
Created2015
Description
In this dissertation, various characterization techniques have been used to investigate many aspects of the properties of III-nitride materials and devices for optoelectronic applications.
The first part of this work is focused on the evolution of microstructures of BAlN thin films. The films were grown by flow-modulated epitaxy at 1010 oC, with B/(B+Al) gas-flow ratios ranging from 0.06 to 0.18. The boron content obtained from X-ray diffraction (XRD) patterns ranges from x = 0.02 to 0.09, while Rutherford backscattering spectrometry (RBS) measures x = 0.06 to 0.16. Transmission electron microscopy indicates the sole presence of the wurtzite crystal structure in the BAlN films, and a tendency towards twin formation and finer microstructure for B/(B+Al) gas-flow ratios greater than 0.15. The RBS data suggest that the incorporation of B is highly efficient, while the XRD data indicate that the epitaxial growth may be limited by a solubility limit in the crystal phase at about 9%. Electron energy loss spectroscopy has been used to profile spatial variations in the composition of the films. It has also located point defects in the films with nanometer resolution. The defects are identified as B and Al interstitials and N vacancies by comparison of the observed energy thresholds with results of density functional theory calculations.
The second part of this work investigates dislocation clusters observed in thick InxGa1-xN films with 0.07 ≤ x ≤ 0.12. The clusters resemble baskets with a higher indium content at their interior. Threading dislocations at the basket boundaries are of the misfit edge type, and their separation is consistent with misfit strain relaxation due the difference in indium content between the baskets and the surrounding matrix. The base of the baskets exhibits no observable misfit dislocations connected to the threading dislocations, and often no net displacements like those due to stacking faults. It is argued that the origin of these threading dislocation arrays is associated with misfit dislocations at the basal plane that dissociate, forming stacking faults. When the stacking faults form simultaneously satisfying the crystal symmetry, the sum of their translation vectors does add up to zero, consistent with our experimental observations.
The first part of this work is focused on the evolution of microstructures of BAlN thin films. The films were grown by flow-modulated epitaxy at 1010 oC, with B/(B+Al) gas-flow ratios ranging from 0.06 to 0.18. The boron content obtained from X-ray diffraction (XRD) patterns ranges from x = 0.02 to 0.09, while Rutherford backscattering spectrometry (RBS) measures x = 0.06 to 0.16. Transmission electron microscopy indicates the sole presence of the wurtzite crystal structure in the BAlN films, and a tendency towards twin formation and finer microstructure for B/(B+Al) gas-flow ratios greater than 0.15. The RBS data suggest that the incorporation of B is highly efficient, while the XRD data indicate that the epitaxial growth may be limited by a solubility limit in the crystal phase at about 9%. Electron energy loss spectroscopy has been used to profile spatial variations in the composition of the films. It has also located point defects in the films with nanometer resolution. The defects are identified as B and Al interstitials and N vacancies by comparison of the observed energy thresholds with results of density functional theory calculations.
The second part of this work investigates dislocation clusters observed in thick InxGa1-xN films with 0.07 ≤ x ≤ 0.12. The clusters resemble baskets with a higher indium content at their interior. Threading dislocations at the basket boundaries are of the misfit edge type, and their separation is consistent with misfit strain relaxation due the difference in indium content between the baskets and the surrounding matrix. The base of the baskets exhibits no observable misfit dislocations connected to the threading dislocations, and often no net displacements like those due to stacking faults. It is argued that the origin of these threading dislocation arrays is associated with misfit dislocations at the basal plane that dissociate, forming stacking faults. When the stacking faults form simultaneously satisfying the crystal symmetry, the sum of their translation vectors does add up to zero, consistent with our experimental observations.
ContributorsWang, Shuo, Ph.D (Author) / Ponce, Fernando A. (Thesis advisor) / Menéndez, Jose (Committee member) / Rez, Peter (Committee member) / McCartney, Martha (Committee member) / Arizona State University (Publisher)
Created2018
Description
Climate change is one of the biggest challenges facing today's society.Since the late 19th century, the global average temperature has been rising. In order to minimize the temperature increase of the earth, it is necessary to develop alternative energy technologies that do not depend on fossil fuels. Solar fuels are one potential energy source for the future. Solar fuel technologies use catalysts to convert low energy molecules into fuels via artificial photosynthesis. TiO2, or titania, is an important model photocatalyst for studying these reactions. It is also important to use remaining fossil fuel resources efficiently and with the lowest possible greenhouse gas emissions. Fuel cells are electrochemical devices that aim to accomplish this goal and CeO2, or ceria, is an important material used in these devices. One way to observe the atomic structure of a material is with a transmission electron microscope (TEM). A traditional transmission electron microscope employs a beam of fast electrons to form atomic resolution images of a material. While imaging gives information about the positions of the atoms in the material, spectroscopy gives information about the composition and bonding of the material. A type of spectroscopy that can be performed inside the transmission electron microscope is electron energy loss spectroscopy (EELS), which provides a fundamental understanding of the electronic structure of a material. The energy loss spectrum also contains information on the chemical bonding in the material, and theoretical calculations that model the spectra are essential to correctly interpreting this bonding information. FEFF is a software that performs EELS calculations. Calculations of the oxygen K edges of TiO2 and CeO2 were made using FEFF in order to understand the changes that occur in the spectrum when oxygen vacancies are introduced as well as the changes near a grain boundary.
ContributorsHussaini, Zahra (Author) / Crozier, Peter (Thesis director) / Rez, Peter (Committee member) / Jorissen, Kevin (Committee member) / Barrett, The Honors College (Contributor) / School of Mathematical and Statistical Sciences (Contributor) / Materials Science and Engineering Program (Contributor) / Department of Physics (Contributor)
Created2013-12