ure of merit (zT) due to quantum connement eects. Improving the eciency of
thermoelectric devices allows for the development of better, more economical waste
heat recovery systems. Such systems may be used as bottoming or co-generation
cycles in conjunction with conventional power cycles to recover some of the wasted
heat. Thermal conductivity measurement systems are an important part of the char-
acterization processes of thermoelectric materials. These systems must possess the
capability of accurately measuring the thermal conductivity of both bulk and thin-lm
samples at dierent ambient temperatures.
This paper discusses the construction, validation, and improvement of a thermal
conductivity measurement platform based on the 3-Omega technique. Room temperature
measurements of thermal conductivity done on control samples with known properties
such as undoped bulk silicon (Si), bulk gallium arsenide (GaAs), and silicon dioxide
(SiO2) thin lms yielded 150 W=m􀀀K, 50 W=m􀀀K, and 1:46 W=m􀀀K respectively.
These quantities were all within 8% of literature values. In addition, the thermal
conductivity of bulk SiO2 was measured as a function of temperature in a Helium-
4 cryostat from 75K to 250K. The results showed good agreement with literature
values that all fell within the error range of each measurement. The uncertainty in
the measurements ranged from 19% at 75K to 30% at 250K. Finally, the system
was used to measure the room temperature thermal conductivity of a nanocomposite
composed of cadmium selenide, CdSe, nanocrystals in an indium selenide, In2Se3,
matrix as a function of the concentration of In2Se3. The observed trend was in
qualitative agreement with the expected behavior.
i
The current method of measuring thermal conductivity requires flat plates. For most common civil engineering materials, creating or extracting such samples is difficult. A prototype thermal conductivity experiment had been developed at Arizona State University (ASU) to test cylindrical specimens but proved difficult for repeated testing. In this study, enhancements to both testing methods were made. Additionally, test results of cylindrical testing were correlated with the results from identical materials tested by the Guarded Hot&ndashPlate; method, which uses flat plate specimens. In validating the enhancements made to the Guarded Hot&ndashPlate; and Cylindrical Specimen methods, 23 tests were ran on five different materials. The percent difference shown for the Guarded Hot&ndashPlate; method was less than 1%. This gives strong evidence that the enhanced Guarded Hot-Plate apparatus in itself is now more accurate for measuring thermal conductivity. The correlation between the thermal conductivity values of the Guarded Hot&ndashPlate; to those of the enhanced Cylindrical Specimen method was excellent. The conventional concrete mixture, due to much higher thermal conductivity values compared to the other mixtures, yielded a P&ndashvalue; of 0.600 which provided confidence in the performance of the enhanced Cylindrical Specimen Apparatus. Several recommendations were made for the future implementation of both test methods. The work in this study fulfills the research community and industry desire for a more streamlined, cost effective, and inexpensive means to determine the thermal conductivity of various civil engineering materials.