This research investigated deionized water contact angle measurement reliability with alumina powder using the Washburn method. This method relates the capillary rise of a liquid through a column of packed powder to the contact angle of the system. A reference liquid that is assumed to be perfectly wetting, such as hexane due to the low surface energy, must be used to compare to the tested liquid. Consistency was hypothesized to be achieved with more powder structure and consistency of packing between reference and test trials. The three types of packing structures explored in this study were unstructured, visually-structured (user tapped), and machine-structured tapping. It was also hypothesized that similar contact angle results would be found for different packing methods of the same powder and liquid. However, the average contact angle for unstructured packing was found to be 32.9°, while the angle for the tapped structure was only 11.7°. This large deviation between types of packing shows that there are more inconsistencies with the use of this method than just the regulation of the packing structure. There were two similar glass chromatography columns used, but the second column experienced an unknown interference that led to a delay in the hexane uptake into the powder, which then led to invalid contact angle calculations. There was no discernible relationship between the packing structure and the standard deviation between trials, so the more structured packing does not seem to affect the consistency of results. It is recommended to perform more experiments on a single packing type with different apparatuses and a narrower particle size range.
ContributorsConvery, Brittany Alexis (Author) / Emady, Heather (Thesis director) / Vajrala, Spandana (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2017-12
Description
The wettability of powders is an important characteristic for both industry and academia and is often described by the powder’s contact angle with a certain liquid. While there exist many ways to measure contact angle, it is a portion of the powder technology field that is not fully understood and requires more investigation and research. This study investigates two methods for measuring contact angle, the sessile drop method and the Washburn method, and looks to compare results to determine which method offers the most reliable data in terms of accuracy and repeatability. Two powders - microcrystalline cellulose and aluminum oxide - and three liquids - water, 50 cSt silicone oil, and 350 cSt silicone oil - were used to study the differences between the two measurement techniques as well as the effects of varying fluid viscosity on the measurements. It was found that the sessile drop method proved to be an ineffective method for measuring contact angle when liquid penetration into the powder occurred, as the contact angle changed while the drop penetrated. Initial results showed the contact angle for silicone oil on the powders to be greater than 90°, indicating nonwetting of the surface which was inconsistent with observations. The results from the Washburn method align better with other values in similar studies, but more study is needed to confirm the results gathered in this research.
ContributorsSmith, Bryan Alexander (Author) / Emady, Heather (Thesis director) / Rykaczewski, Konrad (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2016-05
Description
In the development of personalized medicine and many other clinical studies, biospecimen integrity serves as the prerequisite for not only the accurate derivation of patient- and disease-specific molecular data from biological specimens but the meaningful downstream validation of biomarkers. However, a large number of preanalytical variables may influence the quality of biospecimens in an undesired way and ultimately render the samples unsuitable for molecular analysis. The limited ability to directly reduce discrepancies caused by preanalytical variables gives rise to the need for development and retrospective application of appropriate tests for assessment of biospecimen integrity. Nevertheless, the most standard approaches to assessing biospecimen integrity involve nontrivial procedures. Thus, the need for quality control tools or tests that are readily applicable and can produce results in a straightforward way becomes critical. As one of the major ex vivo biomolecular degradation mechanisms, oxidation that occurs when blood plasma and serum samples are exposed to thawed states during storage and processing is hard to forestall and detect. In an attempt to easily detect and monitor the degree of oxidation, the technique of Fluorescence Resonance Energy Transfer (FRET) was examined to determine whether this concept could be employed to monitor exposure of samples to thawed conditions when controlled by spontaneous oxidative disulfide bonding. The intended mode of usage was envisioned as a fluorescence liquid being stored in a separate compartment but within the same test tube as archived plasma and serum samples. This would allow the assessment of sample integrity by direct visualization of fluorescence under a hand-held black light. The fluorescent dynamic range as well as kinetic control of the reaction were studied. While the addition of Cu(II) proved to facilitate excellent dynamic range with regard to fluorescence quenching, the kinetics of the reaction were too rapid for practical use. Further investigation revealed that the fluorescence quenching mechanism might have actually occurred via Intramolecular Charge Transfer (ICT) rather than FRET mediated by oxidative disulfide bond formation. Introduction of Cu(II) via copper metal slowed fluorescence quenching to the point of practical utility; facilitating demonstration that storing at room temperature, refrigerating or freezing the samples delayed fluorescence quenching to different extents. To establish better kinetic control, future works will focus on establishing controlled, thoroughly understood kinetic release of Cu(II) from copper metal.
ContributorsZhang, Zihan (Author) / Borges, Chad (Thesis director) / Emady, Heather (Committee member) / Williams, Peter (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2018-12
Description
The role of robotics mobility is essential in the world of research because it allows humans to perform jobs that are dull, dirty, or dangerous without being physically present. A typical robot environment is one that is smooth and predictable. Screw-powered vehicles (SPV's) have commonly been used in these predictable environment situations such as terrestrial applications like mud and snow. However, a gap remains in SPV's traversing complex environments, particularly debris and granular material. The goal is to study the characteristics of how a SPV might move and generate force in such a granular environment for Earth and space. In our study, the chosen granular environment is soda-lime glass beads for easy characterization. This study with glass beads focuses on two separate approaches. The first approach is using a single screw rotating while the apparatus remains static and analyzing the forces that impact the screw. The second approach includes using a full body craft with two double helix screws and analyzing the translational velocity of the craft. This study presents both experimental and computational results using simulations with Multi-Body Dynamics (MBD) and Discrete Element Method (DEM) software packages to investigate the trends of SPV's in a granular environment.
ContributorsRamirez, Sierra Monique (Author) / Marvi, Hamid (Thesis director) / Emady, Heather (Committee member) / Thoesen, Andrew (Committee member) / Mechanical and Aerospace Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2018-05
Description
In industrial applications, rotary drums are poorly understood and preform suboptimally when used to process particulates. In order to better understand how these drums work, a statistical experiment was designed to measure the effects of the fill level and rotation rate on the final temperature of the particle bed. A steel rotary drum was set up to be headed by three external heat guns, simulating the conditions under which standard rotary drums are operated. By measuring the bed temperature at steady state, and recording the combination of factors in each run, a regression analysis was run to determine the factor's effects. Fill level was seen to have a small positive effect, rotation rate was seen to have a small negative effect, and the interaction of the two was shown to have a large positive effect. This led the team to conclude that the flow profile of the bed may be the most important factor in heat transfer, and that further research should be done to isolate and study the effect of the flow profile.
ContributorsBeairsto, Cole James (Author) / Emady, Heather (Thesis director) / Adepu, Manogna (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2018-05
Description
In today's high demand energy industry, oil shale is becoming an increasingly sought-after fossil fuel source, deviating from the more conventional fuel sources. Investigating imbibition, which is the uptake of liquids into porous material, provides potential solutions to common industry issues that occur during hydraulic fracturing of shale rock. Particle characterization tests were performed on industrial shale samples cleaned with methanol only, chloroform only, and a mixture of methanol and chloroform. The purposes of these chemicals were for salt extraction, hydrocarbon extraction, and the extraction of both impurities respectively. These characterization tests included bulk and tap density tests, Malvern Mor- phologi G3SE tests for circle equivalent diameter (particle size distribution), high sensitivity circularity, and elongation, Freeman Technology FT4 Powder Rheometer tests for bulk flowability and compressibil- ity, and sessile drop experiments using deionized water, hexane, and silicone oil for hydrophobicity and contact angle measurements. Results show that the methanol cleaned sample had the largest particle size distribution and largest number of symmetrical particles while the chloroform and methanol/chloroform cleaned samples showed similar results with a smaller particle size distribution and more elliptically shaped particles. Based on this, the methanol cleaned sample had the highest compressibility due to the large number of void fractions between the large particles and the smaller particles fitting within these voids. All three samples were highly hydrophobic and showed similar behaviors in the sessile drop tests.
ContributorsKam, Alvina (Author) / Emady, Heather (Thesis director) / Vajrala, Spandana (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2018-05
Description
Rotary equipment has been used widely in the processing of particulates for the last century, but low thermal efficiency and poor effluent uniformity continue to plague its performance. Consequently, these technologies contribute largely to modern energy waste, environmental pollution, and price inflation of products dependent on particulates in their manufacture. Large industries like pharmaceuticals and oil are impacted, yet minimal research has been conducted into optimizing the equipment because of costs associated with process shut-downs necessary to enable study. Recent works bypassed this constraint with simulations and scaled-down replicates to observe impact of common design parameters, fill level and rotation speed, on heating. This thesis supplanted these studies by investigating particle diameter as a control parameter to optimize heating. The thesis investigated methodologies to study a stainless-steel rotary drum model facilitating the conductive heating of a silica bed by external heat guns. Diameter was varied 2-4 mm at controlled fill levels and rotation speeds, and radial temperature profiles were measured with thermocouples. Heating performance was evaluated for efficiency and uniformity; the former by analyzing thermal time constants and average temperature progression across 70 minutes of operation, and the latter with corresponding radial temperature variances. It was theorized that the direct influence of size on transport properties would implicate an inverse correlation between diameter and performance, but results demonstrated no significance. The apparatus and methodology were still under development, so results were preliminary. From results, the study proposed setup modifications to refine results and future directions to guide follow-up research.
ContributorsDeBruin, Dylan (Author) / Emady, Heather (Thesis director) / Adepu, Manogna (Committee member) / Chemical Engineering Program (Contributor, Contributor) / Barrett, The Honors College (Contributor)
Created2017-05
Description
Characterization of particulate process and product design is a difficult field because of the unique bulk properties and behaviors of particles that differ from gasses and liquids. The purpose of this research is to develop an equation to relate the angle of repose and flowability, the ability of the particle to flow as it pertains to particulate processes and product design. This research is important in multiple industries such as pharmaceuticals and food processes.
ContributorsNugent, Emily Rose (Author) / Emady, Heather (Thesis director) / Marvi, Hamidreza (Committee member) / Materials Science and Engineering Program (Contributor) / Dean, W.P. Carey School of Business (Contributor) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2019-05
Description
This thesis investigates the effects of differing diameters, removal of antistatic forces, and varying moisture content on the shear stress properties of granular glass beads through use of a Freeman FT4 Powder Rheometer. A yield locus results from plotting the experimental shear stress values (kPa) vs. the applied normal stress value (kPa). From these yield loci, Mohr’s Circles are constructed to quantitatively describe flowability of tested materials in terms of a flow function parameter.
By testing 120-180 µm, 120-350 µm, 250-350 µm, and 430-600 µm dry glass bead ranges, an increase in diameter size is seen to result in both higher shear stress values and an increasing slope of plotted shear stress vs. applied normal stress. From constructed Mohr’s Circles, it is observed that flow function is quite high amongst tested dry materials, all yielding values above 20. A high flow function value (>10) is indicative of a good flow.1 Flow function was observed to increase with increasing diameter size until a slight drop was observed at the 430-600 µm range, possibly due to material quality or being near the size limitation of testing within the FT4, where materials must be less than 1000 µm in diameter.However, no trend could be observed in flowability as diameter size was increased.
Through the use of an antistatic solution, the effect of electrostatic forces generated by colliding particles was tested. No significant effect on the shear stress properties was observed.
Wet material testing occurred with the 120-180 µm glass bead range using a deionized water content of 0%, 1%, 5%, 15%, and 20% by mass. The results of such testing yielded an increase in shear stress values at applied normal stress values as moisture content is increased, as well as a decrease in the resulting flow function parameter. However, this trend changed as 20% moisture content was achieved; the wet material became a consistent paste, and a large drop in shear stress values occurred along with an increase in flowability.
By testing 120-180 µm, 120-350 µm, 250-350 µm, and 430-600 µm dry glass bead ranges, an increase in diameter size is seen to result in both higher shear stress values and an increasing slope of plotted shear stress vs. applied normal stress. From constructed Mohr’s Circles, it is observed that flow function is quite high amongst tested dry materials, all yielding values above 20. A high flow function value (>10) is indicative of a good flow.1 Flow function was observed to increase with increasing diameter size until a slight drop was observed at the 430-600 µm range, possibly due to material quality or being near the size limitation of testing within the FT4, where materials must be less than 1000 µm in diameter.However, no trend could be observed in flowability as diameter size was increased.
Through the use of an antistatic solution, the effect of electrostatic forces generated by colliding particles was tested. No significant effect on the shear stress properties was observed.
Wet material testing occurred with the 120-180 µm glass bead range using a deionized water content of 0%, 1%, 5%, 15%, and 20% by mass. The results of such testing yielded an increase in shear stress values at applied normal stress values as moisture content is increased, as well as a decrease in the resulting flow function parameter. However, this trend changed as 20% moisture content was achieved; the wet material became a consistent paste, and a large drop in shear stress values occurred along with an increase in flowability.
ContributorsKleppe, Cameron Nicholas (Author) / Emady, Heather (Thesis director) / Vajrala, Spandana (Committee member) / Chemical Engineering Program (Contributor, Contributor) / Barrett, The Honors College (Contributor)
Created2018-12
Description
This report investigates the effects of autolyzing, fermentation medium, fermentation temperature, and proofing medium on the growth and porosity of 50% whole wheat sourdough bread. A model was designed using a 24 statistical design of experiment with replicates to screen and quantify the individual and combined effects of the aforementioned factors on the area of a 1 cm cross-sectional cut from each loaf. Fermentation temperature had the single largest effect, with colder fermented loaves being on average 10 cm2 larger than their warmer fermented counter parts. Autolyzing had little individual effect, but the strengthened gluten network abated some of the degassing and overproofing that is a consequent handling the dough or letting it ferment too much. This investigation quantifies how to maximize gluten development and yeast growth to create the airiest whole wheat sourdough, a healthier and easier to digest bread than many commercially available.
ContributorsLay, Michael Loren (Author) / Emady, Heather (Thesis director) / Adepu, Manogna (Committee member) / School of Sustainability (Contributor) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2018-05