Matching Items (21)
Description
This dissertation research has involved microscopic characterization of magnetic nanostructures using off-axis electron holography and Lorentz microscopy. The nanostructures investigated have included Co nanoparticles (NPs), Au/Fe/GaAs shell/core nanowires (NWs), carbon spirals with magnetic cores, magnetic nanopillars, Ni-Zn-Co spinel ferrite and CoFe/Pd multilayers. The studies have confirmed the capability of holography to describe the behavior of magnetic structures at the nanoscale.
The phase changes caused by the fringing fields of chains consisting of Co NPs were measured and calculated. The difference between chains with different numbers of Co NPs followed the trend indicated by calculations. Holography studies of Au/Fe/GaAs NWs grown on (110) GaAs substrates with rotationally non-uniform coating confirmed that Fe was present in the shell and that the shell behaved as a bar magnet. No fringing field was observed from NWs with cylindrical coating grown on (111)B GaAs substrates. The most likely explanation is that magnetic fields are confined within the shells and form closed loops. The multiple-magnetic-domain structure of iron carbide cores in carbon spirals was imaged using phase maps of the fringing fields. The strength and range of this fringing field was insufficient for manipulating the carbon spirals with an external applied magnetic field. No magnetism was revealed for CoPd/Fe/CoPd magnetic nanopillars. Degaussing and MFM scans ruled out the possibility that saturated magnetization and sample preparation had degraded the anisotropy, and the magnetism, respectively. The results suggested that these nanopillars were not suitable as candidates for prototypical bit information storage devices.
Observations of Ni-Zn-Co spinel ferrite thin films in plan-view geometry indicated a multigrain magnetic domain structure and the magnetic fields were oriented in-plane only with no preferred magnetization distribution. This domain structure helps explain this ferrite's high permeability at high resonance frequency, which is an unusual character.
Perpendicular magnetic anisotropy (PMA) of CoFe/Pd multilayers was revealed using holography. Detailed microscopic characterization showed structural factors such as layer waviness and interdiffusion that could contribute to degradation of the PMA. However, these factors are overwhelmed by the dominant effect of the CoFe layer thickness, and can be ignored when considering magnetic domain structure.
The phase changes caused by the fringing fields of chains consisting of Co NPs were measured and calculated. The difference between chains with different numbers of Co NPs followed the trend indicated by calculations. Holography studies of Au/Fe/GaAs NWs grown on (110) GaAs substrates with rotationally non-uniform coating confirmed that Fe was present in the shell and that the shell behaved as a bar magnet. No fringing field was observed from NWs with cylindrical coating grown on (111)B GaAs substrates. The most likely explanation is that magnetic fields are confined within the shells and form closed loops. The multiple-magnetic-domain structure of iron carbide cores in carbon spirals was imaged using phase maps of the fringing fields. The strength and range of this fringing field was insufficient for manipulating the carbon spirals with an external applied magnetic field. No magnetism was revealed for CoPd/Fe/CoPd magnetic nanopillars. Degaussing and MFM scans ruled out the possibility that saturated magnetization and sample preparation had degraded the anisotropy, and the magnetism, respectively. The results suggested that these nanopillars were not suitable as candidates for prototypical bit information storage devices.
Observations of Ni-Zn-Co spinel ferrite thin films in plan-view geometry indicated a multigrain magnetic domain structure and the magnetic fields were oriented in-plane only with no preferred magnetization distribution. This domain structure helps explain this ferrite's high permeability at high resonance frequency, which is an unusual character.
Perpendicular magnetic anisotropy (PMA) of CoFe/Pd multilayers was revealed using holography. Detailed microscopic characterization showed structural factors such as layer waviness and interdiffusion that could contribute to degradation of the PMA. However, these factors are overwhelmed by the dominant effect of the CoFe layer thickness, and can be ignored when considering magnetic domain structure.
ContributorsZhang, Desai (Author) / Mccartney, Martha R (Thesis advisor) / Smith, David J. (Thesis advisor) / Crozier, Peter A. (Committee member) / Petusky, William T (Committee member) / Chamberlin, Ralph V (Committee member) / Arizona State University (Publisher)
Created2015
Description
Group III-nitride semiconductors have attracted much attention for applications on high brightness light-emitting diodes (LEDs) and laser diodes (LDs) operating in the visible and ultra-violet spectral range using indium gallium nitride in the active layer. However, the device efficiency in the green to red range is limited by quantum-confined Stark effects resulting from the lattice mismatch between GaN and InGaN. In this dissertation, the optical and micro-structural properties of GaN-based light emitting structures have been analyzed and correlated by utilizing cathodoluminescence and transmission electron microscopy techniques. In the first section, optimization of the design of GaN-based lasers diode structures is presented. The thermal strain present in the GaN underlayer grown on sapphire substrates causes a strain-induced wavelength shift. The insertion of an InGaN waveguide mitigates the mismatch strain at the interface between the InGaN quantum well and the GaN quantum barrier. The second section of the thesis presents a study of the characteristics of thick non-polar m-plane InGaN films and of LED structures containing InGaN quantum wells, which minimize polarization-related electric fields. It is found that in some cases the in-plane piezoelectric fields can still occur due to the existence of misfit dislocations which break the continuity of the film. In the final section, the optical and structural properties of InGaAlN quaternary alloys are analyzed and correlated. The composition of the components of the film is accurately determined by Rutherford backscattering spectroscopy.
ContributorsHuang, Yu (Author) / Ponce, Fernando A. (Thesis advisor) / Tsen, Kong-Thon (Committee member) / Treacy, Michael (Committee member) / Drucker, Jeffery (Committee member) / Culbertson, Robert (Committee member) / Arizona State University (Publisher)
Created2011
Raman spectroscopy characterization of anharmonicity and alloying effects in semiconductor materials
Description
The chemical sensitivity and spatial resolution of Raman spectroscopy, combined with the sensitivity of modern systems that can easily detect single atomic layers, have made this technique a preferred choice for the strain characterization of complex systems such as nanoscale complementary metal-oxide-semiconductor - CMOS - devices. A disadvantage of Raman spectroscopy, however, is that the shifts associated with strain are not related to the geometrical deformations in any obvious way, so that careful calibrations are needed to determine the anharmonic coefficients (p, q and r) that relate strain to Raman shifts. A new set of measurements of the Raman shift in strained Ge films grown on relaxed SiGe buffer layers deposited on Si substrates is presented, and thereby, a new consistent set of values for the parameters p and q for Ge has been proposed. In this dissertation the study of the vibrational properties of Ge1-xSnx alloys has also been reported. The temperature dependence of the Raman spectrum of Ge-rich Ge1-x Snx and Ge1-x-ySi xSny alloys has been determined in the 10 K - 450 K range. The Raman line shift and width changes as a function of temperature are found to be virtually identical to those observed in bulk Ge. This result shows that the anharmonic decay process responsible for the temperature dependence is extremely robust against the alloy perturbation.
ContributorsBagchi, Sampriti (Author) / Menéndez, Jose (Thesis advisor) / Treacy, Michael (Committee member) / Ponce, Fernando (Committee member) / Tsen, Kong-Thon (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2011
Description
In this work, a new method, "Nanobonding" [1,2] is conceived and researched to bond Si-based surfaces, via nucleation and growth of a 2 D silicon oxide SiOxHx interphase connecting the surfaces at the nanoscale across macroscopic domains. Nanobonding cross-bridges two smooth surfaces put into mechanical contact in an O2/H2O mixed ambient below T <200 °C via arrays of SiOxHx molecules connecting into a continuous macroscopic bonding interphase. Nano-scale surface planarization via wet chemical processing and new spin technology are compared via Tapping Mode Atomic Force Microscopy (TMAFM) , before and after nano-bonding. Nanobonding uses precursor phases, 2D nano-films of beta-cristobalite (beta-c) SiO2, nucleated on Si(100) via the Herbots-Atluri (H-A) method [1]. beta-c SiO2 on Si(100) is ordered and flat with atomic terraces over 20 nm wide, well above 2 nm found in native oxides. When contacted with SiO2 this ultra-smooth nanophase can nucleate and grow domains with cross-bridging molecular strands of hydroxylated SiOx, instead of point contacts. The high density of molecular bonds across extended terraces forms a strong bond between Si-based substrates, nano- bonding [2] the Si and silica. A new model of beta-cristobalite SiO2 with its <110> axis aligned along Si[100] direction is simulated via ab-initio methods in a nano-bonded stack with beta-c SiO2 in contact with amorphous SiO2 (a-SiO2), modelling cross-bridging molecular bonds between beta-c SiO2 on Si(100) and a-SiO2 as during nanobonding. Computed total energies are compared with those found for Si(100) and a-SiO2 and show that the presence of two lattice cells of !-c SiO2 on Si(100) and a-SiO2 lowers energy when compared to Si(100)/ a-SiO2 Shadow cone calculations on three models of beta-c SiO2 on Si(100) are compared with Ion Beam Analysis of H-A processed Si(100). Total surface energy measurements via 3 liquid contact angle analysis of Si(100) after H-A method processing are also compared. By combining nanobonding experiments, TMAFM results, surface energy data, and ab-initio calculations, an atomistic model is derived and nanobonding is optimized. [1] US Patent 6,613,677 (9/2/03), 7,851,365 (12/14/10), [2] Patent Filed: 4/30/09, 10/1/2011
ContributorsWhaley, Shawn D (Author) / Culbertson, Robert J. (Thesis advisor) / Herbots, Nicole (Committee member) / Rez, Peter (Committee member) / Marzke, Robert F (Committee member) / Lindsay, Stuart (Committee member) / Chamberlin, Ralph V (Committee member) / Arizona State University (Publisher)
Created2011
Description
Group III-nitride semiconductors have wide application in optoelectronic devices. Spontaneous and piezoelectric polarization effects have been found to be critical for electric and optical properties of group III-nitrides. In this dissertation, firstly, the crystal orientation dependence of the polarization is calculated and in-plane polarization is revealed. The in-plane polarization is sensitive to the lateral characteristic dimension determined by the microstructure. Specific semi-polar plane growth is suggested for reducing quantum-confined Stark effect. The macroscopic electrostatic field from the polarization discontinuity in the heterostructures is discussed, b ased on that, the band diagram of InGaN/GaN quantum well/barrier and AlGaN/GaN heterojunction is obtained from the self-consistent solution of Schrodinger and Poisson equations. New device design such as triangular quantum well with the quenched polarization field is proposed. Electron holography in the transmission electron microscopy is used to examine the electrostatic potential under polarization effects. The measured potential energy profiles of heterostructure are compared with the band simulation, and evidences of two-dimensional hole gas (2DHG) in a wurtzite AlGaN/ AlN/ GaN superlattice, as well as quasi two-dimensional electron gas (2DEG) in a zinc-blende AlGaN/GaN are found. The large polarization discontinuity of AlN/GaN is the main source of the 2DHG of wurtzite nitrides, while the impurity introduced during the growth of AlGaN layer provides the donor states that to a great extent balance the free electrons in zinc-blende nitrides. It is also found that the quasi-2DEG concentration in zinc-blende AlGaN/GaN is about one order of magnitude lower than the wurtzite AlGaN/GaN, due to the absence of polarization. Finally, the InAlN/GaN lattice-matched epitaxy, which ideally has a zero piezoelectric polarization and strong spontaneous polarization, is experimentally studied. The breakdown in compositional homogeneity is triggered by threading dislocations with a screw component propagating from the GaN underlayer, which tend to open up into V-grooves at a certain thickness of the InxAl1-xN layer. The V-grooves coalesce at 200 nm and are filled with material that exhibits a significant drop in indium content and a broad luminescence peak. The structural breakdown is due to heterogeneous nucleation and growth at the facets of the V-grooves.
ContributorsWei, Qiyuan (Author) / Ponce, Fernando A. (Thesis advisor) / Tsen, Kong-Thon (Committee member) / Shumway, John (Committee member) / Menéndez, Jose (Committee member) / Smith, David (Committee member) / Arizona State University (Publisher)
Created2012
Description
III-nitride alloys are wide band gap semiconductors with a broad range of applications in optoelectronic devices such as light emitting diodes and laser diodes. Indium gallium nitride light emitting diodes have been successfully produced over the past decade. But the progress of green emission light emitting devices has been limited by the incorporation of indium in the alloy, mainly due to phase separation. This difficulty could be addressed by studying the growth and thermodynamics of these alloys. Knowledge of thermodynamic phase stabilities and of pressure - temperature - composition phase diagrams is important for an understanding of the boundary conditions of a variety of growth techniques. In this dissertation a study of the phase separation of indium gallium nitride is conducted using a regular solution model of the ternary alloy system. Graphs of Gibbs free energy of mixing were produced for a range of temperatures. Binodal and spinodal decomposition curves show the stable and unstable regions of the alloy in equilibrium. The growth of gallium nitride and indium gallium nitride was attempted by the reaction of molten gallium - indium alloy with ammonia at atmospheric pressure. Characterization by X-ray diffraction, photoluminescence, and secondary electron microscopy show that the samples produced by this method contain only gallium nitride in the hexagonal phase. The instability of indium nitride at the temperatures required for activation of ammonia accounts for these results. The photoluminescence spectra show a correlation between the intensity of a broad green emission, related to native defects, and indium composition used in the molten alloy. A different growth method was used to grow two columnar-structured gallium nitride films using ammonium chloride and gallium as reactants and nitrogen and ammonia as carrier gasses. Investigation by X-ray diffraction and spatially-resolved cathodoluminescence shows the film grown at higher temperature to be primarily hexagonal with small quantities of cubic crystallites, while the one grown at lower temperature to be pure hexagonal. This was also confirmed by low temperature photoluminescence measurements. The results presented here show that cubic and hexagonal crystallites can coexist, with the cubic phase having a much sharper and stronger luminescence. Controlled growth of the cubic phase GaN crystallites can be of use for high efficiency light detecting and emitting devices. The ammonolysis of a precursor was used to grow InGaN powders with different indium composition. High purity hexagonal GaN and InN were obtained. XRD spectra showed complete phase separation for samples with x < 30%, with ~ 9% indium incorporation in the 30% sample. The presence of InGaN in this sample was confirmed by PL measurements, where luminescence from both GaN and InGaN band edge are observed. The growth of higher indium compositions samples proved to be difficult, with only the presence of InN in the sample. Nonetheless, by controlling parameters like temperature and time may lead to successful growth of this III-nitride alloy by this method.
ContributorsHill, Arlinda (Author) / Ponce, Fernando A. (Thesis advisor) / Chamberlin, Ralph V (Committee member) / Sankey, Otto F (Committee member) / Smith, David J. (Committee member) / Tsen, Kong-Thon (Committee member) / Arizona State University (Publisher)
Created2011
Description
Raman scattering from Ge-Si core-shell nanowires is investigated theoretically and experimentally. A theoretical model that makes it possible to extract quantitative strain information from the measured Raman spectra is presented for the first time. Geometrical and elastic simplifications are introduced to keep the model analytical, which facilitates comparison with experimental results. In particular, the nanowires are assumed to be cylindrical, and their elastic constants isotropic. The simple analytical model is subsequently validated by performing numerical calculations using realistic nanowire geometries and cubic, anisotropic elastic constants. The comparison confirms that the analytic model is an excellent approximation that greatly facilitates quantitative Raman work, with expected errors in the strain determination that do not exceed 10%. Experimental Raman spectra of a variety of core-shell nanowires are presented, and the strain in the nanowires is assessed using the models described above. It is found that all structures present a significant degree of strain relaxation relative to ideal, fully strained Ge-Si core-shell structures. The analytical models are modified to quantify this strain relaxation.
ContributorsSingh, Rachna (Author) / Menéndez, Jose (Thesis advisor) / Drucker, Jeffery (Committee member) / Ponce, Fernando (Committee member) / Tsen, Kong-Thon (Committee member) / Bennett, Peter (Committee member) / Arizona State University (Publisher)
Created2011
Description
A theoretical study of a three-dimensional (3D) N/S interface with arbitrary spin
polarization and interface geometry is presented. The 3D model gives the same intrinsic
spin polarization and superconducting gap dependence as the 1D model. This
demonstrates that the 1D model can be use to t 3D data.
Using this model, a Heusler alloy is investigated. Andreev reflection measurements
show that the spin polarization is 80% in samples sputtered on unheated MgO(100)
substrates and annealed at high temperatures. However, the spin polarization is
considerably smaller in samples deposited on heated substrates.
Ferromagnetic FexSix alloys have been proposed as potential spin injectors into
silicon with a substantial spin polarization. Andreev Reflection Spectroscopy (ARS) is
utilized to determine the spin polarization of both amorphous and crystalline Fe65Si35
alloys. The amorphous phase has a significantly higher spin polarization than that of
the crystalline phase.
In this thesis, (1111) Fe SmO0:82F0:18FeAs and Pb superconductors are used to
measure the spin polarization of a highly spin-polarized material, La0:67Sr0:33MnO3.
Both materials yield the same intrinsic spin polarization, therefore, Fe-superconductors
can be used in ARS. Based on the behavior of the differential conductance for highly
spin polarized LSMO and small polarization of Au, it can be concluded that the Fe-Sc
is not a triplet superconductor.
Zero bias anomaly (ZBA), in point contact Andreev reflection (PCAR), has been
utilized as a characteristic feature to reveal many novel physics. Complexities at a
normal metal/superconducting interface often cause nonessential ZBA-like features,
which may be mistaken as ZBA. In this work, it is shown that an extrinsic ZBA,
which is due to the contact resistance, cannot be suppressed by a highly spin-polarized
current while a nonessential ZBA cannot be affected the contact resistance.
Finally, Cu/Cu multilayer GMR structures were fabricated and the GMR% measured
at 300 K and 4.5 K gave responses of 63% and 115% respectively. Not only
do the GMR structures have a large enhancement of resistance, but by applying an
external magnetic eld it is shown that, unlike most materials, the spin polarization
can be tuned to values of 0.386 to 0.415 from H = 0 kOe to H = 15 kOe.
polarization and interface geometry is presented. The 3D model gives the same intrinsic
spin polarization and superconducting gap dependence as the 1D model. This
demonstrates that the 1D model can be use to t 3D data.
Using this model, a Heusler alloy is investigated. Andreev reflection measurements
show that the spin polarization is 80% in samples sputtered on unheated MgO(100)
substrates and annealed at high temperatures. However, the spin polarization is
considerably smaller in samples deposited on heated substrates.
Ferromagnetic FexSix alloys have been proposed as potential spin injectors into
silicon with a substantial spin polarization. Andreev Reflection Spectroscopy (ARS) is
utilized to determine the spin polarization of both amorphous and crystalline Fe65Si35
alloys. The amorphous phase has a significantly higher spin polarization than that of
the crystalline phase.
In this thesis, (1111) Fe SmO0:82F0:18FeAs and Pb superconductors are used to
measure the spin polarization of a highly spin-polarized material, La0:67Sr0:33MnO3.
Both materials yield the same intrinsic spin polarization, therefore, Fe-superconductors
can be used in ARS. Based on the behavior of the differential conductance for highly
spin polarized LSMO and small polarization of Au, it can be concluded that the Fe-Sc
is not a triplet superconductor.
Zero bias anomaly (ZBA), in point contact Andreev reflection (PCAR), has been
utilized as a characteristic feature to reveal many novel physics. Complexities at a
normal metal/superconducting interface often cause nonessential ZBA-like features,
which may be mistaken as ZBA. In this work, it is shown that an extrinsic ZBA,
which is due to the contact resistance, cannot be suppressed by a highly spin-polarized
current while a nonessential ZBA cannot be affected the contact resistance.
Finally, Cu/Cu multilayer GMR structures were fabricated and the GMR% measured
at 300 K and 4.5 K gave responses of 63% and 115% respectively. Not only
do the GMR structures have a large enhancement of resistance, but by applying an
external magnetic eld it is shown that, unlike most materials, the spin polarization
can be tuned to values of 0.386 to 0.415 from H = 0 kOe to H = 15 kOe.
ContributorsGifford, Jessica Anna (Author) / Chen, Tingyong (Thesis advisor) / Bennett, Peter (Committee member) / Nemanich, Robert (Committee member) / Tsen, Kong-Thon (Committee member) / Arizona State University (Publisher)
Created2015
Description
Doping and alloying agents are commonly used to engineer the properties of magnetic materials. This study investigates the effects of doping manganese in thin films of Ni80Fe20 (permalloy) and Ni65Fe15Co20 magnetic systems for low power memory technologies, including those that operate at low temperature.
Elemental manganese is anti-ferromagnetic with a Neel temperature of 100 K. When used as a dopant in a magnetic material, it is found to often align its moment in an antiferromagnetic direction. Thus, the addition of manganese might be expected to reduce the overall saturation magnetization (MS) of the magnetic system. In this study, we show that the use of manganese dopants in Ni80Fe20 (permalloy) and Ni65Fe15Co20 thin films can reduce their saturation magnetization and still retain excellent switching properties.
Magnetic properties and transport properties were determined using Vibrating Sample Magnetometer. A 19% decrease in the MS of (Ni80Fe20)1-xMnx thin films and a 36% decrease for (Ni65Fe15Co20)1-xMnx thin films for dopant levels of x = 30%. The impact of depositing a ruthenium (Ru) under-layer for (Ni65Fe15Co20)1-xMnx system was also studied.
The structural (lattice parameters and phases), surface (roughness and topography) and electrical properties (resistivity and mean free path) of the Mn-doped Ni65Fe15Co20 films were determined with X-Ray Diffraction, Atomic Force Microscopy and Four-Point probe technique respectively.
The properties were analyzed and Ni65Fe15Co20 system with Ru- under-layer with 20 at. % Mn content was found to exhibit the following low-field switching properties at 10 K; MS~700 emu.cm-3, easy axis coercivity ~10 Oe and hard axis coercivity ~5 Oe, easy axis squareness ~0.9 and anisotropy field ~12 Oe, that are deemed useful for low-power memory applications that could be used at cryogenic temperatures.
To determine the transport properties thought these magnetic layers for use in superconductor/ferromagnetic memory structures, a study of the oxidation conditions of Al films was performed in order to produce a reliable aluminum oxide tunnel barrier on top of these films. The production of N-I-F-S (Normal metal-Insulator-Ferromagnet-Superconductor) tunnel junctions will allow for the investigation of the tunneling density of states as a function of ferromagnetic layer thickness, allowing for the determination of important transport parameters relevant to magnetic barrier Josephson junction devices.
Elemental manganese is anti-ferromagnetic with a Neel temperature of 100 K. When used as a dopant in a magnetic material, it is found to often align its moment in an antiferromagnetic direction. Thus, the addition of manganese might be expected to reduce the overall saturation magnetization (MS) of the magnetic system. In this study, we show that the use of manganese dopants in Ni80Fe20 (permalloy) and Ni65Fe15Co20 thin films can reduce their saturation magnetization and still retain excellent switching properties.
Magnetic properties and transport properties were determined using Vibrating Sample Magnetometer. A 19% decrease in the MS of (Ni80Fe20)1-xMnx thin films and a 36% decrease for (Ni65Fe15Co20)1-xMnx thin films for dopant levels of x = 30%. The impact of depositing a ruthenium (Ru) under-layer for (Ni65Fe15Co20)1-xMnx system was also studied.
The structural (lattice parameters and phases), surface (roughness and topography) and electrical properties (resistivity and mean free path) of the Mn-doped Ni65Fe15Co20 films were determined with X-Ray Diffraction, Atomic Force Microscopy and Four-Point probe technique respectively.
The properties were analyzed and Ni65Fe15Co20 system with Ru- under-layer with 20 at. % Mn content was found to exhibit the following low-field switching properties at 10 K; MS~700 emu.cm-3, easy axis coercivity ~10 Oe and hard axis coercivity ~5 Oe, easy axis squareness ~0.9 and anisotropy field ~12 Oe, that are deemed useful for low-power memory applications that could be used at cryogenic temperatures.
To determine the transport properties thought these magnetic layers for use in superconductor/ferromagnetic memory structures, a study of the oxidation conditions of Al films was performed in order to produce a reliable aluminum oxide tunnel barrier on top of these films. The production of N-I-F-S (Normal metal-Insulator-Ferromagnet-Superconductor) tunnel junctions will allow for the investigation of the tunneling density of states as a function of ferromagnetic layer thickness, allowing for the determination of important transport parameters relevant to magnetic barrier Josephson junction devices.
ContributorsBoochakravarthy, Ashwin Agathya (Author) / Newman, Nathan (Thesis advisor) / Alford, Terry L. (Committee member) / Singh, Rakesh K. (Committee member) / Chamberlin, Ralph V (Committee member) / Arizona State University (Publisher)
Created2018
Description
What makes living systems different than non-living ones? Unfortunately this question is impossible to answer, at least currently. Instead, we must face computationally tangible questions based on our current understanding of physics, computation, information, and biology. Yet we have few insights into how living systems might quantifiably differ from their non-living counterparts, as in a mathematical foundation to explain away our observations of biological evolution, emergence, innovation, and organization. The development of a theory of living systems, if at all possible, demands a mathematical understanding of how data generated by complex biological systems changes over time. In addition, this theory ought to be broad enough as to not be constrained to an Earth-based biochemistry. In this dissertation, the philosophy of studying living systems from the perspective of traditional physics is first explored as a motivating discussion for subsequent research. Traditionally, we have often thought of the physical world from a bottom-up approach: things happening on a smaller scale aggregate into things happening on a larger scale. In addition, the laws of physics are generally considered static over time. Research suggests that biological evolution may follow dynamic laws that (at least in part) change as a function of the state of the system. Of the three featured research projects, cellular automata (CA) are used as a model to study certain aspects of living systems in two of them. These aspects include self-reference, open-ended evolution, local physical universality, subjectivity, and information processing. Open-ended evolution and local physical universality are attributed to the vast amount of innovation observed throughout biological evolution. Biological systems may distinguish themselves in terms of information processing and storage, not outside the theory of computation. The final research project concretely explores real-world phenomenon by means of mapping dominance hierarchies in the evolution of video game strategies. Though the main question of how life differs from non-life remains unanswered, the mechanisms behind open-ended evolution and physical universality are revealed.
ContributorsAdams, Alyssa M (Author) / Walker, Sara I (Thesis advisor) / Davies, Paul CW (Committee member) / Pavlic, Theodore P (Committee member) / Chamberlin, Ralph V (Committee member) / Arizona State University (Publisher)