In view of the current interest in porous geopolymers for non-traditional applications, it is becoming increasingly important to develop synthetic techniques to introduce interconnected pores into the geopolymers. This study presents a simple synthetic route to produce hierarchically porous geopolymers via a reactive emulsion templating process utilizing triglyceride oil. In this new method, highly alkaline geopolymer resin is mixed with canola oil to form a homogeneous viscous emulsion which, when cured at 60 °C, gives a hard monolithic material. During the process, the oil in the alkaline emulsion undergoes a saponification reaction to decompose into water-soluble soap and glycerol molecules which are extracted to yield porous geopolymers. Nitrogen sorption studies indicates the presence of mesopores, whereas the SEM studies reveals that the mesoporous geopolymer matrix is dotted with spherical macropores. The method exhibits flexibility in that the pore structure of the final porous geopolymers products can be adjusted by varying the precursor composition.
In a second method, the geopolymerization process is modified to produce highly dispersible geopolymer particles, by activating metakaolin with sodium silicate solutions containing excess alkali, and curing for short duration under moist conditions. The produced geopolymer particles exhibit morphology similar to carbon blacks and structured silicas, while also being stable over a wide pH range.
Finally, highly crystalline hierarchical faujasite zeolites are prepared by yet another modification of the geopolymerization process. In this technique, the second method is combined with a saponification reaction of triglyceride oil. The resulting hierarchical zeolites exhibit superior CO2-sorption properties compared to equivalent commercially available and currently reported materials. Additionally, the simplicity of all three of these techniques means they are readily scalable.
Large-scale, sodium-ion batteries are seen as global solutions to providing undisrupted electricity from sustainable, but power-fluctuating, energy production in the near future. Foreseen ideal advantages are lower cost without sacrifice of desired high-energy densities relative to present lithium-ion and lead-acid battery systems. Na/NiCl2 (ZEBRA) and Na/S battery chemistries, suffer from high operation temperature (>300ºC) and safety concerns following major fires consequent of fuel mixing after cell-separator rupturing. Initial interest was utilizing low-melting organic ionic liquid, [EMI+][AlCl4-], with well-known molten salt, NaAlCl4, to create a low-to-moderate operating temperature version of ZEBRA batteries; which have been subject of prior sodium battery research spanning decades. Isothermal conductivities of these electrolytes revealed a fundamental kinetic problem arisen from "alkali cation-trapping effect" yet relived by heat-ramping >140ºC.
Battery testing based on [EMI+][FeCl4-] with NaAlCl4 functioned exceptional (range 150-180ºC) at an impressive energy efficiency >96%. Newly prepared inorganic ionic liquid, [PBr4+][Al2Br7-]:NaAl2Br7, melted at 94ºC. NaAl2Br7 exhibited super-ionic conductivity 10-1.75 Scm-1 at 62ºC ensued by solid-state rotator phase transition. Also improved thermal stability when tested to 265ºC and less expensive chemical synthesis. [PBr4+][Al2Br7-] demonstrated remarkable, ionic decoupling in the liquid-state due to incomplete bromide-ion transfer depicted in NMR measurements.
Fuel cells are electrochemical devices generating electrical energy reacting hydrogen/oxygen gases producing water vapor. Principle advantage is high-energy efficiency of up to 70% in contrast to an internal combustion engine <40%. Nafion-based fuel cells are prone to carbon monoxide catalytic poisoning and polymer membrane degradation unless heavily hydrated under cell-pressurization. This novel "SiPOH" solid-electrolytic gel (originally liquid-state) operated in the fuel cell at 121oC yielding current and power densities high as 731mAcm-2 and 345mWcm-2, respectively. Enhanced proton conduction significantly increased H2 fuel efficiency to 89.7% utilizing only 3.1mlmin-1 under dry, unpressurized testing conditions. All these energy devices aforementioned evidently have future promise; therefore in early developmental stages.
In an effort to further the understanding of ligand-surface interactions, a combination of multi-nuclear (1H, 29Si, 31P) and multi-dimensional solid-state NMR techniques were utilized to characterize the phosphonic acid functionalization of fumed silica nanoparticles using methyl phosphonic acid (MPA) and phenyl phosphonic acid (PPA). Quantitative 31P MAS solid-state NMR measurements indicate that ligands favor a monodentate binding mode. Furthermore, 1H-1H single quantum-double quantum (SQ-DQ) back-to-back (BABA) 2D NMR spectra of silica functionalized with MPA and PPA indicate that the MPA and PPA are within 4.2±0.2 Å on the surface of the nanomaterial.
The ligand capping of phosphonic acid (PA) functionalized CdSe/ZnS core-shell quantum dots (QDs) was investigated with a combination of ligand exchange, solution and solid-state 31P NMR spectroscopy. In order to quantify the ligand populations on the surface of the QDs, ligand exchange facilitated by PPA resulted in the displacement of the PAs, and allowed for quantification of the free ligands using 31P liquid state NMR.
In addition to characterizing nanomaterials, the ionicity and transport properties of a series of diethylmethylamine (DEMA) based protic ionic liquids (PILs) were characterized, principally utilizing NMR. Gas phase proton affinity was shown to be a better predictor for the extent of proton transfer, and in turn the ionicity of the PIL, than using ∆pKa. Furthermore, pulsed field gradient (PFG) NMR was used to determine that the exchangeable proton diffuses with the cation or the anion based on the strength of the acid used to generate the PILs.
Despite the great strides being made in the areas of alternative energy and solar-energy conversion, consumption of fossil fuels for energy generation will likely continue into the foreseeable future. This is primarily motivated by economic factors inasmuch as fossil fuels are a proven resource base with robust harvesting and distribution infrastructure.2 Presently, there are more than 8,000 stationary CO2 emission sources with an annual output of 13,466 megatons of CO2 per year.2 In this context, development of systems that ameliorate the output of greenhouse gasses from stationary CO2 sources, such as coal and natural gas burning power plants, is urgently needed.
In this document the utility of sulfur nucleophiles for CCS schemes is explored. The main thrust of the research has been utilizing electrogenerated sulfur nucleophiles to capture CO2, which can be electrochemically recovered from the resulting thiocarbonates while concomitantly regenerating the masked capture agent. Further, a temperature swing CO2 capture scheme that employs benzylthiolate as the CO2 sorbent is proposed and methods of manipulating the release temperature and kinetics were investigated. These reports represent the first application of organosulfur compounds toward CCS technologies and there are a number of newly reported compounds. The appendix deviates from the theme of the first four chapters to describe the functionalization of poly(2,6-dimethyl-1,4-phenylene oxide) with ferrocene moieties by the copper catalyzed azide-alkyne coupling reaction. This material is discussed within the context of anion recognition and sensing applications.
In pursuit of a greener sol-gel route for TiO2 materials, a solution of TiOSO4 in water was explored. Success in obtaining a gel came by utilizing hydrogen peroxide as a ligand that suppressed precipitation reactions. Through modifying this sol-gel chemistry to obtain a solid acid, the new material hydrogen titanium phosphate sulfate, H1-xTi2(PO4)3-x(SO4)x, (0 < x < 0.5) was synthesized and characterized for the first time. From the reported synthetic route, this compound took the form of macroscopic agglomerates of nanoporous aggregates of nanoparticles around 20 nm and the product calcined at 600 °C exhibited surface area of 78 m2/g, pore volume of 0.22 cm3/g and an average pore width of 11 nm. This solid acid exhibits complete selectivity for the non-oxidative dehydrogenation of methanol to formaldehyde and hydrogen gas, with >50% conversion at 300 °C.
Finally, hierarchically meso-macroporous antimony doped tin oxide was synthesized with regular macropore size around 210 nm, determined by statistical dye trajectory tracking, and also with larger pores up to micrometers in size. The structure consisted of nanoparticles around 4 nm in size, with textural mesopores around 20 nm in diameter.
Despite comprising a variety of bioactive compounds that can be utilized as effective synthetic precursors, the construction of halogenated arenes often relies on hazardous reagents and conditions that pose regioselectivity issues in complex systems. Halodecarboxylation using vanadium-dependent haloperoxidases (VHPOs) has emerged as a sustainable alternative for the synthesis of halogenated arenes. In the Biegasiewicz group, we recently discovered that VHPOs can furnish 3-bromooxindoles from 3-carboxyindoles through a decarboxylation event, followed by oxidation. While this tandem process was exciting, the intermediates of this process, 3- bromoindoles are independently valuable reagents, which necessitated further investigation. Herein we examine the biocatalytic access to bromoindoles for which we addressed the major challenge of undesired oxidation event. The first preventative approach acylated the indole nitrogen, resulting in 1-acetylindole-3-CO2H. This could then be subjected to optimized enzymatic bromination conditions to produce 1-acetyl-3-bromoindole in 98% yield with CiVCPO. The second preventative approach was to modify the reaction conditions, furnishing 1-methyl-3-bromoindole in 73% yield from 1-methylindole-3- CO2H with AmVBPO.