In the interest of expediting future pilot line start-ups for solar cell research, the development of Arizona State University's student-led pilot line at the Solar Power Laboratory is discussed extensively within this work. Several experiments and characterization techniques used to formulate and optimize a series of processes for fabricating diffused-junction,

In the interest of expediting future pilot line start-ups for solar cell research, the development of Arizona State University's student-led pilot line at the Solar Power Laboratory is discussed extensively within this work. Several experiments and characterization techniques used to formulate and optimize a series of processes for fabricating diffused-junction, screen-printed silicon solar cells are expounded upon. An experiment is conducted in which the thickness of a PECVD deposited anti-reflection coating (ARC) is varied across several samples and modeled as a function of deposition time. Using this statistical model in tandem with reflectance measurements for each sample, the ARC thickness is optimized to increase light trapping in the solar cells. A response surface model (RSM) experiment is conducted in which 3 process parameters are varied on the PECVD tool for the deposition of the ARCs on several samples. A contactless photoconductance decay (PCD) tool is used to measure the dark saturation currents of these samples. A statistical analysis is performed using JMP in which optimum deposition parameters are found. A separate experiment shows an increase in the passivation quality of the a-SiNx:H ARCs deposited on the solar cells made on the line using these optimum parameters. A RSM experiment is used to optimize the printing process for a particular silver paste in a similar fashion, the results of which are confirmed by analyzing the series resistance of subsequent cells fabricated on the line. An in-depth explanation of a more advanced analysis using JMP and PCD measurements on the passivation quality of 3 aluminum back-surface fields (BSF) is given. From this experiment, a comparison of the means is conducted in order to choose the most effective BSF paste for cells fabricated on the line. An experiment is conducted in parallel which confirms the results via Voc measurements. It is shown that in a period of 11 months, the pilot line went from producing a top cell efficiency of 11.5% to 17.6%. Many of these methods used for the development of this pilot line are equally applicable to other cell structures, and can easily be applied to other solar cell pilot lines.
ContributorsPickett, Guy (Author) / Bowden, Stuart (Thesis advisor) / Honsberg, Christiana (Committee member) / Bertoni, Mariana (Committee member) / Arizona State University (Publisher)
Created2014
153902-Thumbnail Image.png
Description
The aim of this thesis research is the development of thin silicon heterojunction solar cells with high open circuit voltage (Voc). Heterojunction solar cells are higher in efficiency than diffused junction c-Si solar cells, and they are less vulnerable to light degradation. Furthermore, the low temperature processing of heterojunction cells

The aim of this thesis research is the development of thin silicon heterojunction solar cells with high open circuit voltage (Voc). Heterojunction solar cells are higher in efficiency than diffused junction c-Si solar cells, and they are less vulnerable to light degradation. Furthermore, the low temperature processing of heterojunction cells favour a decrease in production costs and improve cell performance at the same time. Since about 30 % of the module cost is a result of substrate cost, thin solar cells are of economic advantage than their thicker counterparts. This lead to the research for development of thin heterojunction solar cells. For high cell efficiencies and performance, it is important for cells to have a high operating voltage and Voc. Development of heterojunction cells with high Voc required a stable and repeatable baseline process on which further improvements could be made. Therefore a baseline process for heterojunction solar cells was developed and demonstrated as a pilot line at the Solar Power Lab at ASU. All the processes involved in fabrication of cells with the baseline process were optimized to have a stable and repeatable process. The cells produced with the baseline process were 19-20% efficient. The baseline process was further used as a backbone to improve and develop thin cells with even higher Voc. The process recipe was optimized with an aim to explore the limits of Voc that could be achieved with this structure on a much thinner substrate than used for the baseline process. A record Voc greater than 760mV was recorded at SPL using Suns-Voc tester on a 50 microns thick heterojunction cell without metallization. Furthermore, Voc of 754.2 mV was measured on a 50 microns thick cell with metallization by National Renewable Energy Laboratory (NREL), which is a record for Voc for heterojunction cells with metallization. High Voc corresponds to high cell efficiency and therefore, higher module voltage and power with using the same number of cells as compared to other c-Si solar cells.
ContributorsMonga, Tanmay (Author) / Bowden, Stuart (Thesis advisor) / Dauksher, William (Committee member) / Tracy, Clarence (Committee member) / Arizona State University (Publisher)
Created2015
156761-Thumbnail Image.png
Description
The objective of this thesis is to achieve a detailed understanding of the loss mechanisms in SHJ solar cells. The working principles of these cells and what affects the cell operation, e.g. the IV characteristics at the maximum power point (MPP) and the correspondingly ll factor (FF) are investigated. Dierent

The objective of this thesis is to achieve a detailed understanding of the loss mechanisms in SHJ solar cells. The working principles of these cells and what affects the cell operation, e.g. the IV characteristics at the maximum power point (MPP) and the correspondingly ll factor (FF) are investigated. Dierent loss sources are analyzed separately, and the weight of each in the total loss at the MPP are evaluated. The total series resistance is measured and then compared with the value obtained through summation over each of its components. In other words, series resistance losses due to recombination, vertical and lateral carrier transport, metalization, etc, are individually evaluated, and then by adding all these components together, the total loss is calculated. The concept of ll factor and its direct dependence on the loss mechanisms at the MPP of the device is explained, and its sensitivity to nearly every processing step of the cell fabrication is investigated. This analysis provides a focus lens to identify the main source of losses in SHJ solar cells and pave the path for further improvements in cell efficiency.

In this thesis, we provide a detailed understanding of the FF concept; we explain how it can be directly measured; how it can be calculated and what expressions can better approximate its value and under what operating conditions. The relation between FF and cell operating condition at the MPP is investigated. We separately analyzed the main FF sources of losses including recombination, sheet resistance, contact resistance and metalization. We study FF loss due to recombination and its separate components which include the Augur, radiative and SRH recombination is investigated. We study FF loss due to contact resistance and its separate components which include the contact resistance of dierent interfaces, e.g. between the intrinsic and doped a-Si layers, TCO and a-Si layers. We also study FF loss due to lateral transport and its components that including the TCO sheet resistance, the nger and the busbars resistances.
ContributorsLeilaeioun, Mohammadmehdi (Ashling) (Author) / Goodnick, Stephen (Thesis advisor) / Goryll, Michael (Thesis advisor) / Bertoni, Mariana (Committee member) / Bowden, Stuart (Committee member) / Stuckelberger, Michael (Committee member) / Arizona State University (Publisher)
Created2018