Structural details of phosphonic acid functionalized nanomaterials and protic ionic liquids (PILs) were characterized using nuclear magnetic resonance (NMR) spectroscopy. It is well known that ligands play a critical role in the synthesis and properties of nanomaterials. Therefore, elucidating the details of ligand-surface and ligand-ligand interactions is crucial to

Structural details of phosphonic acid functionalized nanomaterials and protic ionic liquids (PILs) were characterized using nuclear magnetic resonance (NMR) spectroscopy. It is well known that ligands play a critical role in the synthesis and properties of nanomaterials. Therefore, elucidating the details of ligand-surface and ligand-ligand interactions is crucial to understanding nanomaterial systems more completely.

In an effort to further the understanding of ligand-surface interactions, a combination of multi-nuclear (1H, 29Si, 31P) and multi-dimensional solid-state NMR techniques were utilized to characterize the phosphonic acid functionalization of fumed silica nanoparticles using methyl phosphonic acid (MPA) and phenyl phosphonic acid (PPA). Quantitative 31P MAS solid-state NMR measurements indicate that ligands favor a monodentate binding mode. Furthermore, 1H-1H single quantum-double quantum (SQ-DQ) back-to-back (BABA) 2D NMR spectra of silica functionalized with MPA and PPA indicate that the MPA and PPA are within 4.2±0.2 Å on the surface of the nanomaterial.

The ligand capping of phosphonic acid (PA) functionalized CdSe/ZnS core-shell quantum dots (QDs) was investigated with a combination of ligand exchange, solution and solid-state 31P NMR spectroscopy. In order to quantify the ligand populations on the surface of the QDs, ligand exchange facilitated by PPA resulted in the displacement of the PAs, and allowed for quantification of the free ligands using 31P liquid state NMR.

In addition to characterizing nanomaterials, the ionicity and transport properties of a series of diethylmethylamine (DEMA) based protic ionic liquids (PILs) were characterized, principally utilizing NMR. Gas phase proton affinity was shown to be a better predictor for the extent of proton transfer, and in turn the ionicity of the PIL, than using ∆pKa. Furthermore, pulsed field gradient (PFG) NMR was used to determine that the exchangeable proton diffuses with the cation or the anion based on the strength of the acid used to generate the PILs.
ContributorsDavidowski, Stephen (Author) / Yarger, Jeffery L. (Thesis advisor) / Holland, Gregory P (Thesis advisor) / Angell, Charles A. (Committee member) / Buttry, Daniel A. (Committee member) / Arizona State University (Publisher)
Created2015
153840-Thumbnail Image.png
Description
In this research work, the process optimization of silver iodide-silver meta phosphate ionic glass molding for solid state super ionic stamping was performed. Solid state super ionic stamping is a process of all solid ambient condition electrochemical nano patterning technique. In solid state super ionic stamping, anodic dissolution on a

In this research work, the process optimization of silver iodide-silver meta phosphate ionic glass molding for solid state super ionic stamping was performed. Solid state super ionic stamping is a process of all solid ambient condition electrochemical nano patterning technique. In solid state super ionic stamping, anodic dissolution on a solid electrolyte –metal interface and subsequent charge-mass transport in the solid electrolyte is used for obtaining nanometer features on the metallic surface. The solid electrolyte referred to as the stamp is pre-patterned with features to be obtained on the metallic surface. This research developed the process for obtaining stamp with specific dimensions by making use of compression molding. The compression molding process was optimized by varying the five process parameters-temperature, pressure, holding time, pressing time and cooling time. The objective of the process optimization was to obtain best geometrical features for the stamp including flatness and surface roughness and by optimizing the compression molding process, stamp with minimum flatness and surface roughness was obtained. After the experimental optimization of the process was completed, statistical analysis was performed to understand the relative significance of the process parameters and the interaction of the process parameters on the flatness and surface roughness values of the molded stamp. Structural characterization was performed to obtain the variation of average domain size of ionic glass particles within the molded glass disk by varying the process parameters of holding time, pressing time and cooling time.
ContributorsPanikkar, Gautam (Author) / Hsu, Keng H (Thesis advisor) / Chan, Candace (Committee member) / Jiang, Hanqing (Committee member) / Arizona State University (Publisher)
Created2015