Fluctuation Electron Microscopy (FEM) has become an effective materials' structure characterization technique, capable of probing medium-range order (MRO) that may be present in amorphous materials. Although its sensitivity to MRO has been exercised in numerous studies, FEM is not yet a quantitative technique. The holdup has been the discrepancy between the computed kinematical variance and the experimental variance, which previously was attributed to source incoherence. Although high-brightness, high coherence, electron guns are now routinely available in modern electron microscopes, they have not eliminated this discrepancy between theory and experiment. The main objective of this thesis was to explore, and to reveal, the reasons behind this conundrum.
The study was started with an analysis of the speckle statistics of tilted dark-field TEM images obtained from an amorphous carbon sample, which confirmed that the structural ordering is sensitively detected by FEM. This analysis also revealed the inconsistency between predictions of the source incoherence model and the experimentally observed variance.
FEM of amorphous carbon, amorphous silicon and ultra nanocrystalline diamond samples was carried out in an attempt to explore the conundrum. Electron probe and sample parameters were varied to observe the scattering intensity variance behavior. Results were compared to models of probe incoherence, diffuse scattering, atom displacement damage, energy loss events and multiple scattering. Models of displacement decoherence matched the experimental results best.
Decoherence was also explored by an interferometric diffraction method using bilayer amorphous samples, and results are consistent with strong displacement decoherence in addition to temporal decoherence arising from the electron source energy spread and energy loss events in thick samples.
It is clear that decoherence plays an important role in the long-standing discrepancy between experimental FEM and its theoretical predictions.
The study was started with an analysis of the speckle statistics of tilted dark-field TEM images obtained from an amorphous carbon sample, which confirmed that the structural ordering is sensitively detected by FEM. This analysis also revealed the inconsistency between predictions of the source incoherence model and the experimentally observed variance.
FEM of amorphous carbon, amorphous silicon and ultra nanocrystalline diamond samples was carried out in an attempt to explore the conundrum. Electron probe and sample parameters were varied to observe the scattering intensity variance behavior. Results were compared to models of probe incoherence, diffuse scattering, atom displacement damage, energy loss events and multiple scattering. Models of displacement decoherence matched the experimental results best.
Decoherence was also explored by an interferometric diffraction method using bilayer amorphous samples, and results are consistent with strong displacement decoherence in addition to temporal decoherence arising from the electron source energy spread and energy loss events in thick samples.
It is clear that decoherence plays an important role in the long-standing discrepancy between experimental FEM and its theoretical predictions.
ContributorsRezikyan, Aram (Author) / Treacy, Michael M.J. (Thesis advisor) / Smith, David J. (Committee member) / McCartney, Martha R. (Committee member) / Rez, Peter (Committee member) / Arizona State University (Publisher)
Created2015
Description
Zeolites are a class of microporous materials that are immensely useful as molecular sieves and catalysts. While there exist millions of hypothetical zeolite topologies, only 206 have been recognized to exist in nature, and the question remains: What distinguishes known zeolite topologies from their hypothetical counterparts? It has been found that all 206 of the known zeolites can be represented as networks of rigid perfect tetrahedra that hinge freely at the connected corners. The range of configurations over which the corresponding geometric constraints can be met has been termed the "flexibility window". Only a small percentage of hypothetical types exhibit a flexibility window, and it is thus proposed that this simple geometric property, the existence of a flexibility window, provides a reliable benchmark for distinguishing potentially realizable hypothetical structures from their infeasible counterparts. As a first approximation of the behavior of real zeolite materials, the flexibility window provides additional useful insights into structure and composition. In this thesis, various methods for locating and exploring the flexibility window are discussed. Also examined is the assumption that the tetrahedral corners are force-free. This is a reasonable approximation in silicates for Si-O-Si angles above ~135°. However, the approximation is poor for germanates, where Ge-O-Ge angles are constrained to the range ~120°-145°. Lastly, a class of interesting low-density hypothetical zeolites is evaluated based on the feasibility criteria introduced.
ContributorsDawson, Colby (Author) / Treacy, Michael M. J. (Thesis advisor) / O'Keeffe, Michael (Committee member) / Thorpe, Michael F. (Committee member) / Rez, Peter (Committee member) / Bennett, Peter (Committee member) / Arizona State University (Publisher)
Created2013
Description
Interfacial interactions between materials in complex heterostructures can dominate the material's response in manymodern-day energy-related devices and processes. Considerable research has been dedicated towards addressing
the profound effects of interfaces. Here, first-principles-based quantum mechanical simulations are discussed to
characterize the interfacial materials properties of two systems. First, density-functional theory (DFT) calculations
were performed for ceramic oxide grain boundaries in undoped and doped CeO2. Second, the development,
theoretical framework, and utilization of high-throughput, workflow-based, DFT calculations are presented to model
the synthesis of two-dimensional (2D) heterostructured materials. Utilizing this workflow, predictive machine learning
models were created to elucidate key interface-property relationships in 2D heterostructured materials. The DFT simulations reveal that the Σ3(111)/[101] grain boundary was energetically more stable than theΣ3(121)/[101]grain boundary due to the larger atomic coherency in the Σ3(111)/[101] grain boundary plane. The
alkaline-earth metal-doped grain boundary energies demonstrate a parabolic dependence on the size of the
solutes, interfacial strain, and packing density of the grain boundary. The grain boundary energies were stabilized
upon Ca, Sr, and Ba doping whereas Be and Mg render them energetically unstable. The electronic density of states
reveals that no defect states were present in/above the band gap. The thermodynamic trapping of oxygen
vacancies in the near grain boundary region was not significantly impacted by the presence of Ca-solute ions.
However, the migration energy barriers within the grain boundary core were dramatically reduced with high local
Ca-solute concentrations, around 0.3 eV-0.5 eV. Chapter 5 and Chapter 6 discusses the development of the open-source, high-throughput computational "synthesis"based workflow package Hetero2d and the application of Hetero2d using 52 Janus 2D materials and 19 metallic,
cubic phase, elemental substrates. The 438 Janus 2D-substrate pairs were analyzed by identifying substrate
surfaces that stabilize metastable Janus 2D materials, characterizing their effects on the post-adsorbed 2D
materials, and identifying the bonding between the 2D material and substrate. Machine learning models were
applied to predict the binding energy, z-separation, and charge transfer of the Janus 2D-substrate pairs providing
insight into the critical properties which factor into these properties.
ContributorsBoland, Tara Maria (Author) / Crozier, Peter A (Thesis advisor) / Singh, Arunima K (Thesis advisor) / Rez, Peter (Committee member) / Muhich, Christopher (Committee member) / Dholabhai, Pratik (Committee member) / Arizona State University (Publisher)
Created2022
Description
Multifunctional oxide thin-films grown on silicon and several oxide substrates have been characterized using High Resolution (Scanning) Transmission Electron Microscopy (HRTEM), Energy-Dispersive X-ray Spectroscopy (EDX), and Electron Energy-Loss Spectroscopy (EELS). Oxide thin films grown on SrTiO3/Si pseudo-substrate showed the presence of amorphised SrTiO3 (STO) at the STO/Si interface. Oxide/oxide interfaces were observed to be atomically clean with very few defects.
Al-doped SrTiO3 thin films grown on Si were of high crystalline quality. The Ti/O ratio estimated from EELS line scans revealed that substitution of Ti by Al created associated O vacancies. The strength of the crystal field in STO was measured using EELS, and decreased by ~1.0 eV as Ti4+ was substituted by Al3+. The damping of O-K EELS peaks confirmed the rise in oxygen vacancies. For Co-substituted STO films grown on Si, the EDS and EELS spectra across samples showed Co doping was quite random. The substitution of Ti4+ with Co3+ or Co2+ created associated oxygen vacancies for charge balance. Presence of oxygen vacancies was also confirmed by shift of Ti-L EELS peaks towards lower energy by ~0.4 eV. The crystal-field strength decreased by ~0.6 eV as Ti4+ was partially substituted by Co3+ or Co2+.
Spinel Co3O4 thin films grown on MgAl2O4 (110) were observed to have excellent crystalline quality. The structure of the Co3O4/MgAl2O4 interface was determined using HRTEM and image simulations. It was found that MgAl2O4 substrate is terminated with Al and oxygen. Stacking faults and associated strain fields in spinel Co3O4 were found along [111], [001], and [113] using Geometrical Phase Analysis.
NbO2 films on STO (111) were observed to be tetragonal with lattice parameter of 13.8 Å and NbO films on LSAT (111) were observed to be cubic with lattice parameter of 4.26 Å. HRTEM showed formation of high quality NbOx films and excellent coherent interface. HRTEM of SrAl4 on LAO (001) confirmed an island growth mode. The SrAl4 islands were highly crystalline with excellent epitaxial registry with LAO. By comparing HRTEM images with image simulations, the interface structure was determined to consist of Sr-terminated SrAl4 (001) on AlO2-terminated LAO (001).
Al-doped SrTiO3 thin films grown on Si were of high crystalline quality. The Ti/O ratio estimated from EELS line scans revealed that substitution of Ti by Al created associated O vacancies. The strength of the crystal field in STO was measured using EELS, and decreased by ~1.0 eV as Ti4+ was substituted by Al3+. The damping of O-K EELS peaks confirmed the rise in oxygen vacancies. For Co-substituted STO films grown on Si, the EDS and EELS spectra across samples showed Co doping was quite random. The substitution of Ti4+ with Co3+ or Co2+ created associated oxygen vacancies for charge balance. Presence of oxygen vacancies was also confirmed by shift of Ti-L EELS peaks towards lower energy by ~0.4 eV. The crystal-field strength decreased by ~0.6 eV as Ti4+ was partially substituted by Co3+ or Co2+.
Spinel Co3O4 thin films grown on MgAl2O4 (110) were observed to have excellent crystalline quality. The structure of the Co3O4/MgAl2O4 interface was determined using HRTEM and image simulations. It was found that MgAl2O4 substrate is terminated with Al and oxygen. Stacking faults and associated strain fields in spinel Co3O4 were found along [111], [001], and [113] using Geometrical Phase Analysis.
NbO2 films on STO (111) were observed to be tetragonal with lattice parameter of 13.8 Å and NbO films on LSAT (111) were observed to be cubic with lattice parameter of 4.26 Å. HRTEM showed formation of high quality NbOx films and excellent coherent interface. HRTEM of SrAl4 on LAO (001) confirmed an island growth mode. The SrAl4 islands were highly crystalline with excellent epitaxial registry with LAO. By comparing HRTEM images with image simulations, the interface structure was determined to consist of Sr-terminated SrAl4 (001) on AlO2-terminated LAO (001).
ContributorsDhamdhere, Ajit (Author) / Smith, David J. (Thesis advisor) / McCartney, Martha R. (Committee member) / Chamberlin, Ralph (Committee member) / Ponce, Fernando (Committee member) / Arizona State University (Publisher)
Created2015
Description
Vibrational spectroscopy is a ubiquitous characterization tool in elucidating atomic structure at the bulk and nanoscale. The ability to perform high spatial resolution vibrational spectroscopy in a scanning transmission electron microscope (STEM) with electron energy-loss spectroscopy (EELS) has the potential to affect a variety of materials science problems. Since 2014, instrumentation development has pushed for incremental improvements in energy resolution, with the current best being 4.2 meV. Although this is poor in comparison to what is common in photon or neutron vibrational spectroscopies, the spatial resolution offered by vibrational EELS is equal to or better than the best of these other techniques.
The major objective of this research program is to investigate the spatial resolution of the monochromated energy-loss signal in the transmission-beam mode and correlate it to the excitation mechanism of the associated vibrational mode. The spatial variation of dipole vibrational signals in SiO2 is investigated as the electron probe is scanned across an atomically abrupt SiO2/Si interface. The Si-O bond stretch signal has a spatial resolution of 2 – 20 nm, depending on whether the interface, bulk, or surface contribution is chosen. For typical TEM specimen thicknesses, coupled surface modes contribute strongly to the spectrum. These coupled surface modes are phonon polaritons, whose intensity and spectral positions are strongly specimen geometry dependent. In a SiO2 thin-film patterned with a 2x2 array, dielectric theory simulations predict the simultaneous excitation of parallel and uncoupled surface polaritons and a very weak excitation of the orthogonal polariton.
It is demonstrated that atomic resolution can be achieved with impact vibrational signals from optical and acoustic phonons in a covalently bonded material like Si. Sub-nanometer resolution mapping of the Si-O symmetric bond stretch impact signal can also be performed in an ionic material like SiO2. The visibility of impact energy-loss signals from excitation of Brillouin zone boundary vibrational modes in hexagonal BN is seen to be a strong function of probe convergence, but not as strong a function of spectrometer collection angles. Some preliminary measurements to detect adsorbates on catalyst nanoparticle surfaces with minimum radiation damage in the aloof-beam mode are also presented.
The major objective of this research program is to investigate the spatial resolution of the monochromated energy-loss signal in the transmission-beam mode and correlate it to the excitation mechanism of the associated vibrational mode. The spatial variation of dipole vibrational signals in SiO2 is investigated as the electron probe is scanned across an atomically abrupt SiO2/Si interface. The Si-O bond stretch signal has a spatial resolution of 2 – 20 nm, depending on whether the interface, bulk, or surface contribution is chosen. For typical TEM specimen thicknesses, coupled surface modes contribute strongly to the spectrum. These coupled surface modes are phonon polaritons, whose intensity and spectral positions are strongly specimen geometry dependent. In a SiO2 thin-film patterned with a 2x2 array, dielectric theory simulations predict the simultaneous excitation of parallel and uncoupled surface polaritons and a very weak excitation of the orthogonal polariton.
It is demonstrated that atomic resolution can be achieved with impact vibrational signals from optical and acoustic phonons in a covalently bonded material like Si. Sub-nanometer resolution mapping of the Si-O symmetric bond stretch impact signal can also be performed in an ionic material like SiO2. The visibility of impact energy-loss signals from excitation of Brillouin zone boundary vibrational modes in hexagonal BN is seen to be a strong function of probe convergence, but not as strong a function of spectrometer collection angles. Some preliminary measurements to detect adsorbates on catalyst nanoparticle surfaces with minimum radiation damage in the aloof-beam mode are also presented.
ContributorsVenkatraman, Kartik (Author) / Crozier, Peter (Thesis advisor) / Rez, Peter (Committee member) / Wang, Robert (Committee member) / Tongay, Sefaattin (Committee member) / Arizona State University (Publisher)
Created2020
Description
Recent improvements in energy resolution for electron energy-loss spectroscopy in the scanning transmission electron microscope (STEM-EELS) allow novel effects in the low-loss region of the electron energy-loss spectrum to be observed. This dissertation explores what new information can be obtained with the combination of meV EELS energy resolution and atomic spatial resolution in the STEM. To set up this up, I review nanoparticle shape effects in the electrostatic approximation and compare the “classical” and “quantum” approaches to EELS simulation. Past the electrostatic approximation, the imaging of waveguide-type modes is modeled in ribbons and cylinders (in “classical" and “quantum" approaches, respectively), showing how the spatial variations of such modes can now be imaged using EELS. Then, returning to the electrostatic approximation, I present microscopic applications of low-loss STEM-EELS. I develop a “classical” model coupling the surface plasmons of a sharp metallic nanoparticle to the dipolar vibrations of an adsorbate molecule, which allows expected molecular signal enhancements to be quantified and the resultant Fano-type asymmetric spectral line shapes to be explained, and I present “quantum” modelling for the charged nitrogen-vacancy (NV-) and neutral silicon-vacancy (SiV0) color centers in diamond, including cross-sections and spectral maps from density functional theory. These results are summarized before concluding.
Many of these results have been previously published in Physical Review B. The main results of Ch. 2 and Ch. 4 were packaged as “Enhanced vibrational electron energy-loss spectroscopy of adsorbate molecules” (99, 104110), and much of Ch. 5 appeared as “Prospects for detecting individual defect centers using spatially resolved electron energy loss spectroscopy” (100, 134103). The results from Ch. 3 are being prepared for a forthcoming article in the Journal of Chemical Physics.
Many of these results have been previously published in Physical Review B. The main results of Ch. 2 and Ch. 4 were packaged as “Enhanced vibrational electron energy-loss spectroscopy of adsorbate molecules” (99, 104110), and much of Ch. 5 appeared as “Prospects for detecting individual defect centers using spatially resolved electron energy loss spectroscopy” (100, 134103). The results from Ch. 3 are being prepared for a forthcoming article in the Journal of Chemical Physics.
ContributorsKordahl, David Daniel (Author) / Dwyer, Christian (Thesis advisor) / Rez, Peter (Committee member) / Spence, John C.H. (Committee member) / Sukharev, Maxim (Committee member) / Arizona State University (Publisher)
Created2020