Matching Items (7)
Filtering by
- All Subjects: Chalcogenides
- Creators: Kozicki, Michael
- Creators: Kozicki, Michael N
- Status: Published
Description
Microwave (MW), thermal, and ultraviolet (UV) annealing were used to explore the response of Ag structures on a Ge-Se chalcogenide glass (ChG) thin film as flexible radiation sensors, and Te-Ti chalcogenide thin films as a material for diffusion barriers in microelectronics devices and processing of metallized Cu. Flexible resistive radiation sensors consisting of Ag electrodes on a Ge20Se80 ChG thin film and polyethylene naphthalate substrate were exposed to UV radiation. The sensors were mounted on PVC tubes of varying radii to induce bending strains and annealed under ambient conditions up to 150 oC. Initial sensor resistance was measured to be ~1012 Ω; after exposure to UV radiation, the resistance was ~104 Ω. Bending strain and low temperature annealing had no significant effect on the resistance of the sensors. Samples of Cu on Te-Ti thin films were annealed in vacuum for up to 30 minutes and were stable up to 500 oC as revealed using Rutherford backscattering spectrometry (RBS) and four-point-probe analysis. X-ray diffractometry (XRD) indicates Cu grain growth up to 500 oC and phase instability of the Te-Ti barrier at 600 oC. MW processing was performed in a 2.45-GHz microwave cavity on Cu/Te-Ti films for up to 30 seconds to induce oxide growth. Using a calibrated pyrometer above the sample, the temperature of the MW process was measured to be below a maximum of 186 oC. Four-point-probe analysis shows an increase in resistance with an increase in MW time. XRD indicates growth of CuO on the sample surface. RBS suggests oxidation throughout the Te-Ti film. Additional samples were exposed to 907 J/cm2 UV radiation in order to ensure other possible electromagnetically induced mechanisms were not active. There were no changes observed using XRD, RBS or four point probing.
ContributorsRoos, Benjamin, 1990- (Author) / Alford, Terry L. (Thesis advisor) / Theodore, David (Committee member) / Kozicki, Michael (Committee member) / Arizona State University (Publisher)
Created2013
Description
The dissolution of metal layers such as silver into chalcogenide glass layers such as germanium selenide changes the resistivity of the metal and chalcogenide films by a great extent. It is known that the incorporation of the metal can be achieved by ultra violet light exposure or thermal processes. In this work, the use of metal dissolution by exposure to gamma radiation has been explored for radiation sensor applications. Test structures were designed and a process flow was developed for prototype sensor fabrication. The test structures were designed such that sensitivity to radiation could be studied. The focus is on the effect of gamma rays as well as ultra violet light on silver dissolution in germanium selenide (Ge30Se70) chalcogenide glass. Ultra violet radiation testing was used prior to gamma exposure to assess the basic mechanism. The test structures were electrically characterized prior to and post irradiation to assess resistance change due to metal dissolution. A change in resistance was observed post irradiation and was found to be dependent on the radiation dose. The structures were also characterized using atomic force microscopy and roughness measurements were made prior to and post irradiation. A change in roughness of the silver films on Ge30Se70 was observed following exposure. This indicated the loss of continuity of the film which causes the increase in silver film resistance following irradiation. Recovery of initial resistance in the structures was also observed after the radiation stress was removed. This recovery was explained with photo-stimulated deposition of silver from the chalcogenide at room temperature confirmed with the re-appearance of silver dendrites on the chalcogenide surface. The results demonstrate that it is possible to use the metal dissolution effect in radiation sensing applications.
ContributorsChandran, Ankitha (Author) / Kozicki, Michael N (Thesis advisor) / Holbert, Keith E. (Committee member) / Barnaby, Hugh (Committee member) / Arizona State University (Publisher)
Created2012
Description
Chalcogenide glass (ChG) materials have gained wide attention because of their applications in conductive bridge random access memory (CBRAM), phase change memories (PC-RAM), optical rewritable disks (CD-RW and DVD-RW), microelectromechanical systems (MEMS), microfluidics, and optical communications. One of the significant properties of ChG materials is the change in the resistivity of the material when a metal such as Ag or Cu is added to it by diffusion. This study demonstrates the potential radiation-sensing capabilities of two metal/chalcogenide glass device configurations. Lateral and vertical device configurations sense the radiation-induced migration of Ag+ ions in germanium selenide glasses via changes in electrical resistance between electrodes on the ChG. Before irradiation, these devices exhibit a high-resistance `OFF-state' (in the order of 10E12) but following irradiation, with either 60-Co gamma-rays or UV light, their resistance drops to a low-resistance `ON-state' (around 10E3). Lateral devices have exhibited cyclical recovery with room temperature annealing of the Ag doped ChG, which suggests potential uses in reusable radiation sensor applications. The feasibility of producing inexpensive flexible radiation sensors has been demonstrated by studying the effects of mechanical strain and temperature stress on sensors formed on flexible polymer substrate. The mechanisms of radiation-induced Ag/Ag+ transport and reactions in ChG have been modeled using a finite element device simulator, ATLAS. The essential reactions captured by the simulator are radiation-induced carrier generation, combined with reduction/oxidation for Ag species in the chalcogenide film. Metal-doped ChGs are solid electrolytes that have both ionic and electronic conductivity. The ChG based Programmable Metallization Cell (PMC) is a technology platform that offers electric field dependent resistance switching mechanisms by formation and dissolution of nano sized conductive filaments in a ChG solid electrolyte between oxidizable and inert electrodes. This study identifies silver anode agglomeration in PMC devices following large radiation dose exposure and considers device failure mechanisms via electrical and material characterization. The results demonstrate that by changing device structural parameters, silver agglomeration in PMC devices can be suppressed and reliable resistance switching may be maintained for extremely high doses ranging from 4 Mrad(GeSe) to more than 10 Mrad (ChG).
ContributorsDandamudi, Pradeep (Author) / Kozicki, Michael N (Thesis advisor) / Barnaby, Hugh J (Committee member) / Holbert, Keith E. (Committee member) / Goryll, Michael (Committee member) / Arizona State University (Publisher)
Created2013
Description
Total dose sensing systems (or radiation detection systems) have many applications,
ranging from survey monitors used to supervise the generated radioactive waste at
nuclear power plants to personal dosimeters which measure the radiation dose
accumulated in individuals. This dissertation work will present two different types of
novel devices developed at Arizona State University for total dose sensing applications.
The first detector technology is a mechanically flexible metal-chalcogenide glass (ChG)
based system which is fabricated on low cost substrates and are intended as disposable
total dose sensors. Compared to existing commercial technologies, these thin film
radiation sensors are simpler in form and function, and cheaper to produce and operate.
The sensors measure dose through resistance change and are suitable for applications
such as reactor dosimetry, radiation chemistry, and clinical dosimetry. They are ideal for
wearable devices due to the lightweight construction, inherent robustness to resist
breaking when mechanically stressed, and ability to attach to non-flat objects. Moreover,
their performance can be easily controlled by tuning design variables and changing
incorporated materials. The second detector technology is a wireless dosimeter intended
for remote total dose sensing. They are based on a capacitively loaded folded patch
antenna resonating in the range of 3 GHz to 8 GHz for which the load capacitance varies
as a function of total dose. The dosimeter does not need power to operate thus enabling
its use and implementation in the field without requiring a battery for its read-out. As a
result, the dosimeter is suitable for applications such as unattended detection systems
destined for covert monitoring of merchandise crossing borders, where nuclear material
tracking is a concern. The sensitive element can be any device exhibiting a known
variation of capacitance with total ionizing dose. The sensitivity of the dosimeter is
related to the capacitance variation of the radiation sensitive device as well as the high
frequency system used for reading. Both technologies come with the advantage that they
are easy to manufacture with reasonably low cost and sensing can be readily read-out.
ranging from survey monitors used to supervise the generated radioactive waste at
nuclear power plants to personal dosimeters which measure the radiation dose
accumulated in individuals. This dissertation work will present two different types of
novel devices developed at Arizona State University for total dose sensing applications.
The first detector technology is a mechanically flexible metal-chalcogenide glass (ChG)
based system which is fabricated on low cost substrates and are intended as disposable
total dose sensors. Compared to existing commercial technologies, these thin film
radiation sensors are simpler in form and function, and cheaper to produce and operate.
The sensors measure dose through resistance change and are suitable for applications
such as reactor dosimetry, radiation chemistry, and clinical dosimetry. They are ideal for
wearable devices due to the lightweight construction, inherent robustness to resist
breaking when mechanically stressed, and ability to attach to non-flat objects. Moreover,
their performance can be easily controlled by tuning design variables and changing
incorporated materials. The second detector technology is a wireless dosimeter intended
for remote total dose sensing. They are based on a capacitively loaded folded patch
antenna resonating in the range of 3 GHz to 8 GHz for which the load capacitance varies
as a function of total dose. The dosimeter does not need power to operate thus enabling
its use and implementation in the field without requiring a battery for its read-out. As a
result, the dosimeter is suitable for applications such as unattended detection systems
destined for covert monitoring of merchandise crossing borders, where nuclear material
tracking is a concern. The sensitive element can be any device exhibiting a known
variation of capacitance with total ionizing dose. The sensitivity of the dosimeter is
related to the capacitance variation of the radiation sensitive device as well as the high
frequency system used for reading. Both technologies come with the advantage that they
are easy to manufacture with reasonably low cost and sensing can be readily read-out.
ContributorsMahmud, Adnan, Ph.D (Author) / Barnaby, Hugh J. (Thesis advisor) / Kozicki, Michael N (Committee member) / Gonzalez-Velo, Yago (Committee member) / Goryll, Michael (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2017
Description
Counterfeiting of goods is a widespread epidemic that is affecting the world economy. The conventional labeling techniques are proving inadequate to thwart determined counterfeiters equipped with sophisticated technologies. There is a growing need of a secure labeling that is easy to manufacture and analyze but extremely difficult to copy. Programmable metallization cell technology operates on a principle of controllable reduction of a metal ions to an electrodeposit in a solid electrolyte by application of bias. The nature of metallic electrodeposit is unique for each instance of growth, moreover it has a treelike, bifurcating fractal structure with high information capacity. These qualities of the electrodeposit can be exploited to use it as a physical unclonable function. The secure labels made from the electrodeposits grown in radial structure can provide enhanced authentication and protection from counterfeiting and tampering.
So far only microscale radial structures and electrodeposits have been fabricated which limits their use to labeling only high value items due to high cost associated with their fabrication and analysis. Therefore, there is a need for a simple recipe for fabrication of macroscale structure that does not need sophisticated lithography tools and cleanroom environment. Moreover, the growth kinetics and material characteristics of such macroscale electrodeposits need to be investigated. In this thesis, a recipe for fabrication of centimeter scale radial structure for growing Ag electrodeposits using simple fabrication techniques was proposed. Fractal analysis of an electrodeposit suggested information capacity of 1.27 x 1019. The kinetics of growth were investigated by electrical characterization of the full cell and only solid electrolyte at different temperatures. It was found that mass transport of ions is the rate limiting process in the growth. Materials and optical characterization techniques revealed that the subtle relief like structure and consequently distinct optical response of the electrodeposit provides an added layer of security. Thus, the enormous information capacity, ease of fabrication and simplicity of analysis make macroscale fractal electrodeposits grown in radial programmable metallization cells excellent candidates for application as physical unclonable functions.
So far only microscale radial structures and electrodeposits have been fabricated which limits their use to labeling only high value items due to high cost associated with their fabrication and analysis. Therefore, there is a need for a simple recipe for fabrication of macroscale structure that does not need sophisticated lithography tools and cleanroom environment. Moreover, the growth kinetics and material characteristics of such macroscale electrodeposits need to be investigated. In this thesis, a recipe for fabrication of centimeter scale radial structure for growing Ag electrodeposits using simple fabrication techniques was proposed. Fractal analysis of an electrodeposit suggested information capacity of 1.27 x 1019. The kinetics of growth were investigated by electrical characterization of the full cell and only solid electrolyte at different temperatures. It was found that mass transport of ions is the rate limiting process in the growth. Materials and optical characterization techniques revealed that the subtle relief like structure and consequently distinct optical response of the electrodeposit provides an added layer of security. Thus, the enormous information capacity, ease of fabrication and simplicity of analysis make macroscale fractal electrodeposits grown in radial programmable metallization cells excellent candidates for application as physical unclonable functions.
ContributorsChamele, Ninad (Author) / Kozicki, Michael (Thesis advisor) / Barnaby, Hugh (Thesis advisor) / Newman, Nathan (Committee member) / Arizona State University (Publisher)
Created2017
Description
This is a test plan document for Team Aegis' capstone project that has the goal of mitigating single event upsets in NAND flash memory caused by space radiation.
ContributorsForman, Oliver Ethan (Co-author) / Smith, Aiden (Co-author) / Salls, Demetra (Co-author) / Kozicki, Michael (Thesis director) / Hodge, Chris (Committee member) / Electrical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2021-05
Description
Lateral programmable metallization cells (PMC) utilize the properties of electrodeposits grown over a solid electrolyte channel. Such devices have an active anode and an inert cathode separated by a long electrodeposit channel in a coplanar arrangement. The ability to transport large amount of metallic mass across the channel makes these devices attractive for various More-Than-Moore applications. Existing literature lacks a comprehensive study of electrodeposit growth kinetics in lateral PMCs. Moreover, the morphology of electrodeposit growth in larger, planar devices is also not understood. Despite the variety of applications, lateral PMCs are not embraced by the semiconductor industry due to incompatible materials and high operating voltages needed for such devices. In this work, a numerical model based on the basic processes in PMCs – cation drift and redox reactions – is proposed, and the effect of various materials parameters on the electrodeposit growth kinetics is reported. The morphology of the electrodeposit growth and kinetics of the electrodeposition process are also studied in devices based on Ag-Ge30Se70 materials system. It was observed that the electrodeposition process mainly consists of two regimes of growth – cation drift limited regime and mixed regime. The electrodeposition starts in cation drift limited regime at low electric fields and transitions into mixed regime as the field increases. The onset of mixed regime can be controlled by applied voltage which also affects the morphology of electrodeposit growth. The numerical model was then used to successfully predict the device kinetics and onset of mixed regime. The problem of materials incompatibility with semiconductor manufacturing was solved by proposing a novel device structure. A bilayer structure using semiconductor foundry friendly materials was suggested as a candidate for solid electrolyte. The bilayer structure consists of a low resistivity oxide shunt layer on top of a high resistivity ion carrying oxide layer. Devices using Cu2O as the low resistivity shunt on top of Cu doped WO3 oxide were fabricated. The bilayer devices provided orders of magnitude improvement in device performance in the context of operating voltage and switching time. Electrical and materials characterization revealed the structure of bilayers and the mechanism of electrodeposition in these devices.
ContributorsChamele, Ninad (Author) / Kozicki, Michael (Thesis advisor) / Barnaby, Hugh (Committee member) / Newman, Nathan (Committee member) / Gonzalez-Velo, Yago (Committee member) / Arizona State University (Publisher)
Created2020