Matching Items (6)
Filtering by
- All Subjects: Nuclear physics and radiation
- All Subjects: tem
- Creators: Chamberlin, Ralph
Description
The research described in this dissertation has involved the use of transmission electron microcopy (TEM) to characterize the structural properties of II-VI and III-V compound semiconductor heterostructures and superlattices. The microstructure of thick ZnTe epilayers (~2.4 µm) grown by molecular beam epitaxy (MBE) under virtually identical conditions on GaSb, InAs, InP and GaAs (100) substrates were compared using TEM. High-resolution electron micrographs revealed a highly coherent interface for the ZnTe/GaSb sample, and showed extensive areas with well-separated interfacial misfit dislocations for the ZnTe/InAs sample. Lomer edge dislocations and 60o dislocations were commonly observed at the interfaces of the ZnTe/InP and ZnTe/GaAs samples. The amount of residual strain at the interfaces was estimated to be 0.01% for the ZnTe/InP sample and -0.09% for the ZnTe/GaAs sample. Strong PL spectra for all ZnTe samples were observed from 80 to 300 K. High quality GaSb grown by MBE on ZnTe/GaSb (001) virtual substrates with a temperature ramp at the beginning of the GaSb growth has been demonstrated. High-resolution X-ray diffraction (XRD) showed clear Pendellösung thickness fringes from both GaSb and ZnTe epilayers. Cross-section TEM images showed excellent crystallinity and smooth morphology for both ZnTe/GaSb and GaSb/ZnTe interfaces. Plan-view TEM image revealed the presence of Lomer dislocations at the interfaces and threading dislocations in the top GaSb layer. The defect density was estimated to be ~1 x107/cm2. The PL spectra showed improved optical properties when using the GaSb transition layer grown on ZnTe with a temperature ramp. The structural properties of strain-balanced InAs/InAs1-xSbx SLs grown on GaSb (001) substrates by metalorganic chemical vapor deposition (MOCVD) and MBE, have been studied using XRD and TEM. Excellent structural quality of the InAs/InAs1-xSbx SLs grown by MOCVD has been demonstrated. Well-defined ordered-alloy structures within individual InAs1-xSbx layers were observed for samples grown by modulated MBE. However, the ordering disappeared when defects propagating through the SL layers appeared during growth. For samples grown by conventional MBE, high-resolution images revealed that interfaces for InAs1-xSbx grown on InAs layers were sharper than for InAs grown on InAs1-xSbx layers, most likely due to a Sb surfactant segregation effect.
ContributorsOuyang, Lu (Author) / Smith, David J. (Thesis advisor) / McCartney, Martha (Committee member) / Ponce, Fernando (Committee member) / Chamberlin, Ralph (Committee member) / Menéndez, Jose (Committee member) / Arizona State University (Publisher)
Created2012
Description
Soft magnetic alloys play a significant role for magnetic recording applications and highly sensitivity magnetic field sensors. In order to sustain the magnetic areal density growth, development of new synthesis techniques and materials is necessary. In this work, the effect of oxygen incorporation during electrodeposition of CoFe alloys on magnetic properties, magnetoresistance and structural properties has been studied. Understanding the magnetic properties often required knowledge of oxygen distribution and structural properties of the grown films. Transmission electron microscopy (TEM) was a powerful tool in this study to correlate the oxygen-distribution nanostructure to the magnetic properties of deposited films. Off-axis electron holography in TEM was used to measure magnetic domain wall width in the deposited films. Elemental depth profiles of Fe, Co, O were investigated by secondary ion mass spectroscopy (SIMS). Magnetic properties have been determined by superconducting quantum interference device (SQUID) measurements. Oxygen content in the CoFe deposited films was controlled by electrolyte composition. Films were deposited on Si 100 substrates and on other substrates such as Cu and Al. However, a good film quality was achieved on Si substrate. Electron energy loss and x-ray spectroscopies showed that the low oxygen films contained intragranular Fe2+ oxide (FeO) particles and that the high oxygen films contained intergranular Fe3+ (Fe2O3) along grain boundaries. The films with oxide present at the grain boundary had significantly increased coercivity, magnetoresistance and reduced saturation magnetization relative to the lower oxygen content films with intragranular oxide. The differences in magnetic properties between low oxygen and high oxygen concentration films were attributed to stronger mobile domain wall interactions with the grain boundary oxide layers. The very high magnetoresistance values were achieved for magnetic devices with nanocontact dimension < 100 nm and oxide incorporation in this nanoconfined geometry. The content of oxide phase in nanocontact was controlled by concentration of the Fe3+ ions in the electrodeposition solution. Magnetic device integrity was improved by varying amount of additive into plating solution. These results indicated that electrodeposited CoFe nanocontact is a novel class of materials with large application for magnetic field sensors.
ContributorsElhalawaty, Shereen (Author) / Carpenter, Ray (Thesis advisor) / Chamberlin, Ralph (Committee member) / McCartney, Martha (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2012
Description
Seeking an upper limit of the Neutron Electric Dipole Moment (nEDM) is a test of charge-parity (CP) violation beyond the Standard Model. The present experimentally tested nEDM upper limit is 3x10^(26) e cm. An experiment to be performed at the Oak Ridge National Lab Spallation Neutron Source (SNS) facility seeks to reach the 3x10^(28) e cm limit. The experiment is designed to probe for a dependence of the neutron's Larmor precession frequency on an applied electric eld. The experiment will use polarized helium-3
(3He) as a comagnetometer, polarization analyzer, and detector.
Systematic influences on the nEDM measurement investigated in this thesis include (a) room temperature measurements on polarized 3He in a measurement cell made from the same materials as the nEDM experiment, (b) research and development of the Superconducting QUantum Interference Devices (SQUID) which will be used in the nEDM experiment, (c) design contributions for an experiment with nearly all the same conditions as will be present in the nEDM experiment, and (d) scintillation studies in superfluid helium II generated from alpha particles which are fundamentally similar to the nEDM scintillation process. The result of this work are steps toward achievement of a new upper limit for the nEDM experiment at the SNS facility.
(3He) as a comagnetometer, polarization analyzer, and detector.
Systematic influences on the nEDM measurement investigated in this thesis include (a) room temperature measurements on polarized 3He in a measurement cell made from the same materials as the nEDM experiment, (b) research and development of the Superconducting QUantum Interference Devices (SQUID) which will be used in the nEDM experiment, (c) design contributions for an experiment with nearly all the same conditions as will be present in the nEDM experiment, and (d) scintillation studies in superfluid helium II generated from alpha particles which are fundamentally similar to the nEDM scintillation process. The result of this work are steps toward achievement of a new upper limit for the nEDM experiment at the SNS facility.
ContributorsDipert, Robert (Author) / Alarcon, Ricardo (Thesis advisor) / Chamberlin, Ralph (Committee member) / Golub, Robert (Committee member) / Chen, Tingyong (Committee member) / Schmidt, Kevin (Committee member) / Arizona State University (Publisher)
Created2019
Description
The challenge of radiation therapy is to maximize the dose to the tumor while simultaneously minimizing the dose elsewhere. Proton therapy is well suited to this challenge due to the way protons slow down in matter. As the proton slows down, the rate of energy loss per unit path length continuously increases leading to a sharp dose near the end of range. Unlike conventional radiation therapy, protons stop inside the patient, sparing tissue beyond the tumor. Proton therapy should be superior to existing modalities, however, because protons stop inside the patient, there is uncertainty in the range. “Range uncertainty” causes doctors to take a conservative approach in treatment planning, counteracting the advantages offered by proton therapy. Range uncertainty prevents proton therapy from reaching its full potential.
A new method of delivering protons, pencil-beam scanning (PBS), has become the new standard for treatment over the past few years. PBS utilizes magnets to raster scan a thin proton beam across the tumor at discrete locations and using many discrete pulses of typically 10 ms duration each. The depth is controlled by changing the beam energy. The discretization in time of the proton delivery allows for new methods of dose verification, however few devices have been developed which can meet the bandwidth demands of PBS.
In this work, two devices have been developed to perform dose verification and monitoring with an emphasis placed on fast response times. Measurements were performed at the Mayo Clinic. One detector addresses range uncertainty by measuring prompt gamma-rays emitted during treatment. The range detector presented in this work is able to measure the proton range in-vivo to within 1.1 mm at depths up to 11 cm in less than 500 ms and up to 7.5 cm in less than 200 ms. A beam fluence detector presented in this work is able to measure the position and shape of each beam spot. It is hoped that this work may lead to a further maturation of detection techniques in proton therapy, helping the treatment to reach its full potential to improve the outcomes in patients.
A new method of delivering protons, pencil-beam scanning (PBS), has become the new standard for treatment over the past few years. PBS utilizes magnets to raster scan a thin proton beam across the tumor at discrete locations and using many discrete pulses of typically 10 ms duration each. The depth is controlled by changing the beam energy. The discretization in time of the proton delivery allows for new methods of dose verification, however few devices have been developed which can meet the bandwidth demands of PBS.
In this work, two devices have been developed to perform dose verification and monitoring with an emphasis placed on fast response times. Measurements were performed at the Mayo Clinic. One detector addresses range uncertainty by measuring prompt gamma-rays emitted during treatment. The range detector presented in this work is able to measure the proton range in-vivo to within 1.1 mm at depths up to 11 cm in less than 500 ms and up to 7.5 cm in less than 200 ms. A beam fluence detector presented in this work is able to measure the position and shape of each beam spot. It is hoped that this work may lead to a further maturation of detection techniques in proton therapy, helping the treatment to reach its full potential to improve the outcomes in patients.
ContributorsHolmes, Jason M (Author) / Alarcon, Ricardo (Thesis advisor) / Bues, Martin (Committee member) / Galyaev, Eugene (Committee member) / Chamberlin, Ralph (Committee member) / Arizona State University (Publisher)
Created2019
Description
Multifunctional oxide thin-films grown on silicon and several oxide substrates have been characterized using High Resolution (Scanning) Transmission Electron Microscopy (HRTEM), Energy-Dispersive X-ray Spectroscopy (EDX), and Electron Energy-Loss Spectroscopy (EELS). Oxide thin films grown on SrTiO3/Si pseudo-substrate showed the presence of amorphised SrTiO3 (STO) at the STO/Si interface. Oxide/oxide interfaces were observed to be atomically clean with very few defects.
Al-doped SrTiO3 thin films grown on Si were of high crystalline quality. The Ti/O ratio estimated from EELS line scans revealed that substitution of Ti by Al created associated O vacancies. The strength of the crystal field in STO was measured using EELS, and decreased by ~1.0 eV as Ti4+ was substituted by Al3+. The damping of O-K EELS peaks confirmed the rise in oxygen vacancies. For Co-substituted STO films grown on Si, the EDS and EELS spectra across samples showed Co doping was quite random. The substitution of Ti4+ with Co3+ or Co2+ created associated oxygen vacancies for charge balance. Presence of oxygen vacancies was also confirmed by shift of Ti-L EELS peaks towards lower energy by ~0.4 eV. The crystal-field strength decreased by ~0.6 eV as Ti4+ was partially substituted by Co3+ or Co2+.
Spinel Co3O4 thin films grown on MgAl2O4 (110) were observed to have excellent crystalline quality. The structure of the Co3O4/MgAl2O4 interface was determined using HRTEM and image simulations. It was found that MgAl2O4 substrate is terminated with Al and oxygen. Stacking faults and associated strain fields in spinel Co3O4 were found along [111], [001], and [113] using Geometrical Phase Analysis.
NbO2 films on STO (111) were observed to be tetragonal with lattice parameter of 13.8 Å and NbO films on LSAT (111) were observed to be cubic with lattice parameter of 4.26 Å. HRTEM showed formation of high quality NbOx films and excellent coherent interface. HRTEM of SrAl4 on LAO (001) confirmed an island growth mode. The SrAl4 islands were highly crystalline with excellent epitaxial registry with LAO. By comparing HRTEM images with image simulations, the interface structure was determined to consist of Sr-terminated SrAl4 (001) on AlO2-terminated LAO (001).
Al-doped SrTiO3 thin films grown on Si were of high crystalline quality. The Ti/O ratio estimated from EELS line scans revealed that substitution of Ti by Al created associated O vacancies. The strength of the crystal field in STO was measured using EELS, and decreased by ~1.0 eV as Ti4+ was substituted by Al3+. The damping of O-K EELS peaks confirmed the rise in oxygen vacancies. For Co-substituted STO films grown on Si, the EDS and EELS spectra across samples showed Co doping was quite random. The substitution of Ti4+ with Co3+ or Co2+ created associated oxygen vacancies for charge balance. Presence of oxygen vacancies was also confirmed by shift of Ti-L EELS peaks towards lower energy by ~0.4 eV. The crystal-field strength decreased by ~0.6 eV as Ti4+ was partially substituted by Co3+ or Co2+.
Spinel Co3O4 thin films grown on MgAl2O4 (110) were observed to have excellent crystalline quality. The structure of the Co3O4/MgAl2O4 interface was determined using HRTEM and image simulations. It was found that MgAl2O4 substrate is terminated with Al and oxygen. Stacking faults and associated strain fields in spinel Co3O4 were found along [111], [001], and [113] using Geometrical Phase Analysis.
NbO2 films on STO (111) were observed to be tetragonal with lattice parameter of 13.8 Å and NbO films on LSAT (111) were observed to be cubic with lattice parameter of 4.26 Å. HRTEM showed formation of high quality NbOx films and excellent coherent interface. HRTEM of SrAl4 on LAO (001) confirmed an island growth mode. The SrAl4 islands were highly crystalline with excellent epitaxial registry with LAO. By comparing HRTEM images with image simulations, the interface structure was determined to consist of Sr-terminated SrAl4 (001) on AlO2-terminated LAO (001).
ContributorsDhamdhere, Ajit (Author) / Smith, David J. (Thesis advisor) / McCartney, Martha R. (Committee member) / Chamberlin, Ralph (Committee member) / Ponce, Fernando (Committee member) / Arizona State University (Publisher)
Created2015
Description
Precision measurements of kinematic correlation parameters of free neutron decayserve as a powerful probe of the Standard Model of particle physics. A wide array
of Beyond the Standard Model physics theories can be probed by precision neutron
physics. The Nab experiment will measure a, the electron-neutrino correlation coefficient, and b, the Fierz interference term. a is amongst the most sensitive decay
parameters to λ = gA/gV , the ratio of the axial-vector and vector coupling constants
in the weak force. Two important systematic considerations for the Nab experiment
are average detector timing bias, which must be held to ≤ 0.3 ns, and energy calibration and linearity, which must be held to 1 part in 104
. Both systematics require an
in depth understanding of charge collection in Nab’s Si detectors. Simulation of Si
charge collection using numerical methods and the Shockley-Ramo Theorem has been
completed. A variety of detector tests, including detector and amplification electronics acceptance testing have also been completed. Also included in this dissertation is
my work with the Nab ultra-high vacuum and cryogenic system.
ContributorsRandall, Glenn (Author) / Alarcon, Ricardo (Thesis advisor) / Chamberlin, Ralph (Committee member) / Dugger, Michael (Committee member) / Lebed, Richard (Committee member) / Arizona State University (Publisher)
Created2021