Matching Items (3)
Description
It is the intent of this research to determine the feasibility of utilizing industrial byproducts in cementitious systems in lieu of Portland Cement to reduce global CO2 emissions. Class C and Class F Fly Ash (CFA and FFA, respectively) derived from industrial coal combustion were selected as the replacement materials for this study. Sodium sulfate and calcium oxide were used as activators. In Part 1 of this study, focus was placed on high volume replacement of OPC using sodium sulfate as the activator. Despite improvements in heat generation for both CFA and FFA systems in the presence of sulfate, sodium sulfate was found to have adverse effects on the compressive strength of CFA mortars. In the CFA mixes, strength improved significantly with sulfate addition, but began to decrease in strength around 14 days due to expansive ettringite formation. Conversely, the addition of sulfate led to improved strength for FFA mixes such that the 28 day strength was comparable to that of the CFA mixes with no observable strength loss. Maximum compressive strengths achieved for the high volume replacement mixes was around 40 MPa, which is considerably lower than the baseline OPC mix used for comparison. In Part 2 of the study, temperature dependency and calcium oxide addition were studied for sodium sulfate activated systems composed of 100% Class F fly ash. In the presence of sulfate, added calcium increased reactivity and compressive strength at early ages, particularly at elevated temperatures. It is believed that sulfate and calcium react with alumina from fly ash to form ettringite, while heat overcomes the activation energy barrier of fly ash. The greatest strengths were obtained for mixes containing the maximum allowed quantity of calcium oxide (5%) and sodium sulfate (3%), and were around 12 MPa. This is a very low compressive strength relative to OPC and would therefore be an inadequate substitute for OPC needs.
ContributorsTweedley, Shannon Elizabeth (Author) / Neithalath, Narayanan (Thesis director) / Mamlouk, Michael (Committee member) / Civil, Environmental and Sustainable Engineering Programs (Contributor) / Barrett, The Honors College (Contributor) / School of Sustainable Engineering and the Built Environment (Contributor)
Created2014-05
Description
As green buildings become more popular, the challenge of structural engineer is to move beyond simply green to develop sustainable, and high-performing buildings that are more than just environmentally friendly. For decades, Portland cement-based products have been known as the most commonly used construction materials in the world, and as a result, cement production is a significant source of global carbon dioxide (CO2) emissions, and environmental impacts at all stages of the process. In recent years, the increasing cost of energy and resource supplies, and concerns related to greenhouse gas emissions and environmental impacts have ignited more interests in utilizing waste and by-product materials as the primary ingredient to replace ordinary Portland cement in concrete systems. The environmental benefits of cement replacement are enormous, including the diversion of non-recycled waste from landfills for useful applications, the reduction in non-renewable energy consumption for cement production, and the corresponding emission of greenhouse gases. In the vast available body of literature, concretes consisting activated fly ash or slag as the binder have been shown to have high compressive strengths, and resistance to fire and chemical attack. This research focuses to utilize fly ash, by-product of coal fired power plant along with different alkaline solutions to form a final product with comparable properties to or superior than those of ordinary Portland cement concrete. Fly ash mortars using different concentration of sodium hydroxide and waterglass were dry and moist cured at different temperatures prior subjecting to uniaxial compressive loading condition. Since moist curing continuously supplies water for the hydration process of activated fly ash mortars while preventing thermal shrinkage and cracking, the samples were more durable and demonstrated a noticeably higher compressive strength. The influence of the concentration of the activating agent (4, or 8 M sodium hydroxide solution), and activator-to-binder ratio of 0.40 on the compressive strengths of concretes containing Class F fly ash as the sole binder is analyzed. Furthermore, liquid sodium silicate (waterglass) with silica modulus of 1.0 and 2.0 along with activator-to-binder ratio of 0.04 and 0.07 was also studied to understand its performance in contributing to the strength development of the activated fly ash concrete. Statistical analysis of the compressive strength results show that the available alkali concentration has a larger influence on the compressive strengths of activated concretes made using fly ash than the influence of curing parameters (elevated temperatures, condition, and duration).
ContributorsBanh, Kingsten Chi (Author) / Neithalath, Narayanan (Thesis director) / Rajan, Subramaniam (Committee member) / Mobasher, Barzin (Committee member) / Civil, Environmental and Sustainable Engineering Programs (Contributor) / Barrett, The Honors College (Contributor)
Created2013-05
Description
Alkali-activated aluminosilicates, commonly known as "geopolymers", are being increasingly studied as a potential replacement for Portland cement. These binders use an alkaline activator, typically alkali silicates, alkali hydroxides or a combination of both along with a silica-and-alumina rich material, such as fly ash or slag, to form a final product with properties comparable to or better than those of ordinary Portland cement. The kinetics of alkali activation is highly dependent on the chemical composition of the binder material and the activator concentration. The influence of binder composition (slag, fly ash or both), different levels of alkalinity, expressed using the ratios of Na2O-to-binders (n) and activator SiO2-to-Na2O ratios (Ms), on the early age behavior in sodium silicate solution (waterglass) activated fly ash-slag blended systems is discussed in this thesis. Optimal binder composition and the n values are selected based on the setting times. Higher activator alkalinity (n value) is required when the amount of slag in the fly ash-slag blended mixtures is reduced. Isothermal calorimetry is performed to evaluate the early age hydration process and to understand the reaction kinetics of the alkali activated systems. The differences in the calorimetric signatures between waterglass activated slag and fly ash-slag blends facilitate an understanding of the impact of the binder composition on the reaction rates. Kinetic modeling is used to quantify the differences in reaction kinetics using the Exponential as well as the Knudsen method. The influence of temperature on the reaction kinetics of activated slag and fly ash-slag blends based on the hydration parameters are discussed. Very high compressive strengths can be obtained both at early ages as well as later ages (more than 70 MPa) with waterglass activated slag mortars. Compressive strength decreases with the increase in the fly ash content. A qualitative evidence of leaching is presented through the electrical conductivity changes in the saturating solution. The impact of leaching and the strength loss is found to be generally higher for the mixtures made using a higher activator Ms and a higher n value. Attenuated Total Reflectance-Fourier Transform Infrared Spectroscopy (ATR-FTIR) is used to obtain information about the reaction products.
ContributorsChithiraputhiran, Sundara Raman (Author) / Neithalath, Narayanan (Thesis advisor) / Rajan, Subramaniyam D (Committee member) / Mobasher, Barzin (Committee member) / Arizona State University (Publisher)
Created2012