Matching Items (5)
Filtering by
- All Subjects: Silicon
- Creators: Materials Science and Engineering Program
Description
Dry and steam NanoBonding™ are conceived and researched to bond Si-based surfaces, via nucleation and growth of a two-dimensional SiOxHy or hydrated SiOxHy interphase connecting surfaces at the nanoscale across macroscopic domains. The motivation is to create strong, long lasting, hermetically bonded sensors with their electronics for the development of an artificial pancreas and to bond solar cells to glass panels for robust photovoltaic technology. The first step in NanoBonding™ is to synthesize smooth surfaces with 20 nm wide atomic terraces via a precursor phase, ß-cSiO2 on Si(100) and oxygen-deficient SiOx on the silica using the Herbots-Atluri process and Entrepix’s spin etching. Smooth precursor phases act as geometric and chemical template to nucleate and grow macroscopic contacting domains where cross bridging occurs via arrays of molecular strands in the hydrated SiOxHy interphase. Steam pressurization is found to catalyze NanoBonding™ consistently, eliminating the need for direct mechanical compression that limits the size and shape of wafers to be bonded in turn, reducing the cost of processing. Total surface energy measurements via 3 Liquids Contact Angle Analysis (3L CAA) enables accurate quantitative analysis of the total surface energy and each of its components. 3L CAA at each step in the process shows that surface energy drops to 42.4 ± 0.6 mJ/m2 from 57.5 ± 1.4 mJ/m2 after the Herbots-Atluri clean of an “As Received” wafer. 3L CAA after steam pressurization Nanobonding™ shows almost complete elimination from 13.8 mJ/m2 ± 1.0 to 0.002 ±- 0.0002 mJ/m2 in the contribution of acceptors to the total free surface energy, and an increase from 0.2 ± .03 to 23.8± 1.6 mJ/m2 in the contribution of donors. This is consistent with an increase in hydroxylation of the ß-cSiO2 surface as a consistent precursor phase for cross-bridging. This research optimizes the use of glycerin, water, and α-bromo-naphtalene in the use of 3L CAA to effectively quantify the components of total free surface energy which helps to better understand the most consistent method for NanoBonding™.
ContributorsBennett-Kennett, Ross Buchanan (Author) / Culbertson, Robert (Thesis director) / Herbots, Nicole (Committee member) / Foy, Joseph (Committee member) / Barrett, The Honors College (Contributor) / Materials Science and Engineering Program (Contributor) / Department of Physics (Contributor) / School of Historical, Philosophical and Religious Studies (Contributor)
Created2013-05
Description
Proposed and tested were three different methods to deposit important layers of Silicon heterojunction solar cells (SHJs). If there were a shortage of Silver, Aluminum could be substituted for the contacts. If there were a shortage of Indium, Yttrium Zinc Oxide could be substituted. To improve the solar cell, the p and n type layers can be grown with hydrogenated nanocrystallline Silicon (nc-Si:H). 40% and 50% nc-Si:H has shown a maximum absorbance reduction of 5 times compared to hydrogenated amorphous Silicon (a-Si). The substitutions offer alternatives which increase the total possible amount of solar cell production, advancing toward completion of the Terrawatt challenge.
ContributorsCarpenter, Joe Victor (Author) / Alford, Terry (Thesis director) / Holman, Zachary (Committee member) / Barrett, The Honors College (Contributor) / Chemical Engineering Program (Contributor) / Materials Science and Engineering Program (Contributor)
Created2014-05
DescriptionThere is a growing market for lightweight firearm barrels. Currently this market is dominated by Aluminum and Carbon fiber barrels, however, Gunwright, LLC proposes an innovative new way to manufacture Titanium firearm barrels. This report offers insight into potential customers and existing competitors.
ContributorsKeberle, Katelyn Frances (Author) / Adams, Jim (Thesis director) / Newman, Nathan (Committee member) / Barrett, The Honors College (Contributor) / Materials Science and Engineering Program (Contributor)
Created2014-05
Description
Lithium-ion batteries are one of the most widely used energy storage solutions today. As renewable energy sources proliferate to meet growth in worldwide energy consumption, it is important that lithium-ion batteries be improved to help capture this energy for use when the demand arises. One way to boost the performance of lithium-ion batteries is to replace the electrode active materials with materials of higher specific capacity. Silicon is one material that has been widely touted as a potential replacement for the graphite used in commercial anodes with a theoretical capacity of 3500 mAh/g as opposed to graphite's 372 mAh/g. However, bulk silicon is known to pulverize after experiencing large strains during lithiation. Here, silicon clathrates are investigated as a potential structure for accommodation of these strains. Silicon clathrates consist of covalently bonded silicon host cages surrounding a guest alkali or alkaline earth metal ion. Previous work has looked at silicon clathrates for their superconducting and thermoelectric properties. In this study, electrochemical properties of type I and II silicon clathrates with sodium guest ions (NaxSi46 and NaxSi136) and type I silicon clathrates with copper framework substitution and barium guest ions (Ba8CuxSi46-x) are examined. Sodium clathrates showed very high capacities during initial lithiation (>2500 mAh/g), but rapidly lost capacity thereafter. X-ray diffraction after lithiation showed conversion of the clathrate phase to lithium silicide and then to amorphous silicon after delithiation, indicating destruction of the clathrate structure as a possible explanation for the rapid capacity fade. Ba8CuxSi46-x clathrates were found to have their structures completely intact after 50 cycles. However, they had very low reversible capacities (<100 mAh/g) and potentially might not be electrochemically active. Further work is needed to better understand exactly how lithium is inserted into clathrates and if copper impurities detected during wavelength-dispersive X-ray spectroscopy could be inhibiting lithium transport into the clathrates.
ContributorsWagner, Nicholas Adam (Author) / Chan, Candace (Thesis director) / Sieradzki, Karl (Committee member) / Barrett, The Honors College (Contributor) / Materials Science and Engineering Program (Contributor)
Created2014-05
Description
How can we change what it means to be a human? Products can be used that will allow for near-instantaneous communication with one’s friends and family wherever they are: and the newest devices do not have to be even carried around, as they can be worn instead. Wearable electronics are quickly becoming very popular, with 232.0 million wearable devices sold in 2015. This report provides an overview of current and developing wearable devices, investigates the characteristics of the average buyer for these different types of devices. Finally, marketing strategies are suggested. This work was completed in conjunction with a capstone project with Intel, where three objectives were achieved: First, a universal strain tester that could strain samples cyclically in a manner similar to the body was designed. This equipment was especially designed to be flexible in the testing conditions it could be exposed to, so samples could be tested at elevated temperatures or even underwater. Next, dogbone shaped samples for the testing of Young’s Modulus and elongation to failure were produced, and the cut quality of laser, water-jet, and die-cutting was compared in order to select the most defect-free method for reliable testing. Polydimethylsiloxane (PDMS) is a fantastic candidate material for wearable electronics, however there is some discrepancies in the literature—such as from Eleni et. al—about the impact of ultraviolet radiation on the mechanical properties. By conducting accelerated aging tests simulating up to five years exposure to the sun, it was determined that ultraviolet-induced cross-linking of the polymer chains does occur, leading to severe embrittlement (strain to failure reduced from 3.27 to 0.06 in some cases, reduction to approximately 0.21 on average). As simulated tests of possible usage conditions required strains of at least 0.50-0.70, a variety of solutions were suggested to reduce this embrittlement. This project can lead to standardization of wearables electronics testing methods for more reliable predictions about the device behavior, whether that device is a simple pedometer or something that allows the visually impaired to “see”, such as Toyota’s Blaid.
ContributorsNiebroski, Alexander Wayne (Author) / Adams, James (Thesis director) / Anwar, Shahriar (Committee member) / Materials Science and Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2016-05