Description
Nanoporous crystalline oxides with high porosity and large surface areas are promising in catalysis, clean energy technologies and environmental applications all which require efficient chemical reactions at solid-solid, solid-liquid, and/or solid-gas interfaces. Achieving the balance between open porosity and structural stability is an ongoing challenge when synthesizing such porous materials. Increasing porosity while maintaining an open porous network usually comes at the cost of fragility, as seen for example in ultra low density, highly random porous aerogels. It has become increasingly important to develop synthetic techniques that produce materials with these desired properties while utilizing low cost precursors and increasing their structural strength. Based on non-alkoxide sol-gel chemistry, two novel synthetic methods for nanoporous metal oxides have been developed. The first is a high temperature combustion method that utilizes biorenewable oil, affording gamma alumina (Al2O3) with a surface area over 300 cm3/g and porosity over 80% and controllable pore sizes (average pore width 8 to 20 nm). The calcined crystalline products exhibit an aerogel-like textural mesoporosity. To demonstrate the versatility of the new method, it was used to synthesize highly porous amorphous silica (SiO2) which exhibited increased mechanical robustness while achieving a surface area of 960 m2/g and porosity of 85%. The second method utilizes sequential gelation of inorganic and organic precursors forming an interpenetrating inorganic/organic gel network. The method affords yttria-stabilized zirconia with surface area over 90 cm3/g and porosity over 60% and controllable pore sizes (average pore width 6 to 12 nm). X-ray diffraction, gas sorption analysis, Raman spectroscopy, nuclear magnetic resonance spectroscopy and electron microscopy were all used to characterize the structure, morphology, and the chemical structure of the newly afforded materials. Both novel methods produce products that show superior pore properties and robustness compared to equivalent commercially available and currently reported materials.
ContributorsLadd, Danielle (Author) / Seo, Don (Thesis advisor) / Häussermann, Ulrich (Committee member) / Petuskey, William (Committee member) / Arizona State University (Publisher)
Created2012
Description
Within recent years, metal-organic frameworks, or MOF’s, have gained a lot of attention in the materials research community. These micro-porous materials are constructed of a metal oxide core and organic linkers, and have a wide-variety of applications due to their extensive material characteristic possibilities. The focus of this study is the MOF-5 material, specifically its chemical stability in air. The MOF-5 material has a large pore size of 8 Å, and aperture sizes of 15 and 12 Å. The pore size, pore functionality, and physically stable structure makes MOF-5 a desirable material. MOF-5 holds applications in gas/liquid separation, catalysis, and gas storage. The main problem with the MOF-5 material, however, is its instability in atmospheric air. This inherent instability is due to the water in air binding to the zinc-oxide core, effectively changing the material and its structure. Because of this material weakness, the MOF-5 material is difficult to be utilized in industrial applications. Through the research efforts proposed by this study, the stability of the MOF-5 powder and membrane were studied. MOF-5 powder and a MOF-5 membrane were synthesized and characterized using XRD analysis. In an attempt to improve the stability of MOF-5 in air, methyl groups were added to the organic linker in order to hinder the interaction of water with the Zn4O core. This was done by replacing the terepthalic acid organic linker with 2,5-dimethyl terephthalic acid in the powder and membrane synthesis steps. The methyl-modified MOF-5 powder was found to be stable after several days of exposure to air while the MOF-5 powder exhibited significant crystalline change. The methyl-modified membrane was found to be unstable when synthesized using the same procedure as the MOF-5 membrane.
ContributorsAnderson, Anthony David (Author) / Lin, Jerry Y.S. (Thesis director) / Ibrahim, Amr (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2016-05
Description
Metal-organic frameworks (MOFs) are a new set of porous materials comprised of metals or metal clusters bonded together in a coordination system by organic linkers. They are becoming popular for gas separations due to their abilities to be tailored toward specific applications. Zirconium MOFs in particular are known for their high stability under standard temperature and pressure due to the strength of the Zirconium-Oxygen coordination bond. However, the acid modulator needed to ensure long range order of the product also prevents complete linker deprotonation. This leads to a powder product that cannot easily be incorporated into continuous MOF membranes. This study therefore implemented a new bi-phase synthesis technique with a deprotonating agent to achieve intergrowth in UiO-66 membranes. Crystal intergrowth will allow for effective gas separations and future permeation testing. During experimentation, successful intergrown UiO-66 membranes were synthesized and characterized. The degree of intergrowth and crystal orientations varied with changing deprotonating agent concentration, modulator concentration, and ligand:modulator ratios. Further studies will focus on achieving the same results on porous substrates.
ContributorsClose, Emily Charlotte (Author) / Mu, Bin (Thesis director) / Shan, Bohan (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2016-12
Description
New sol-gel routes were developed to fabricate transparent conducting oxide coatings for energy applications. Sol-gel synthesis was chosen because the metal oxide products have high surface area and porosity. Titanium sol-gel chemistry was the main focus of the studies, and the synthesis of macroporous antimony-doped tin oxide was also explored. The surface chemistry and band characteristics of anatase TiO2 show promise for solar energy purposes as photoelectrodes in DSSCs and as photocatalysts to degrade organic dyes and to split water. Modifying the band structure by increasing the conduction band edge energy is specifically of interest for reducing protons in water. To this end, a new sol-gel method was developed for incorporating Zr-dopant in nanoporous anatase TiO2. The products follow Vegard’s law up to 20 atom%, exhibiting surface area of 79 m2/g and pore volume of 0.20 cm3/g with average pore diameter of 10.3 nm; the conduction band edge energy increased by 0.22 eV and the band gap increased by 0.1 eV.
In pursuit of a greener sol-gel route for TiO2 materials, a solution of TiOSO4 in water was explored. Success in obtaining a gel came by utilizing hydrogen peroxide as a ligand that suppressed precipitation reactions. Through modifying this sol-gel chemistry to obtain a solid acid, the new material hydrogen titanium phosphate sulfate, H1-xTi2(PO4)3-x(SO4)x, (0 < x < 0.5) was synthesized and characterized for the first time. From the reported synthetic route, this compound took the form of macroscopic agglomerates of nanoporous aggregates of nanoparticles around 20 nm and the product calcined at 600 °C exhibited surface area of 78 m2/g, pore volume of 0.22 cm3/g and an average pore width of 11 nm. This solid acid exhibits complete selectivity for the non-oxidative dehydrogenation of methanol to formaldehyde and hydrogen gas, with >50% conversion at 300 °C.
Finally, hierarchically meso-macroporous antimony doped tin oxide was synthesized with regular macropore size around 210 nm, determined by statistical dye trajectory tracking, and also with larger pores up to micrometers in size. The structure consisted of nanoparticles around 4 nm in size, with textural mesopores around 20 nm in diameter.
In pursuit of a greener sol-gel route for TiO2 materials, a solution of TiOSO4 in water was explored. Success in obtaining a gel came by utilizing hydrogen peroxide as a ligand that suppressed precipitation reactions. Through modifying this sol-gel chemistry to obtain a solid acid, the new material hydrogen titanium phosphate sulfate, H1-xTi2(PO4)3-x(SO4)x, (0 < x < 0.5) was synthesized and characterized for the first time. From the reported synthetic route, this compound took the form of macroscopic agglomerates of nanoporous aggregates of nanoparticles around 20 nm and the product calcined at 600 °C exhibited surface area of 78 m2/g, pore volume of 0.22 cm3/g and an average pore width of 11 nm. This solid acid exhibits complete selectivity for the non-oxidative dehydrogenation of methanol to formaldehyde and hydrogen gas, with >50% conversion at 300 °C.
Finally, hierarchically meso-macroporous antimony doped tin oxide was synthesized with regular macropore size around 210 nm, determined by statistical dye trajectory tracking, and also with larger pores up to micrometers in size. The structure consisted of nanoparticles around 4 nm in size, with textural mesopores around 20 nm in diameter.
ContributorsMieritz, Daniel (Author) / Seo, Dong-Kyun (Thesis advisor) / Petuskey, William (Committee member) / Herckes, Pierre (Committee member) / Arizona State University (Publisher)
Created2016