Eccentric muscle action (ECC) occurs when the force exerted by a working muscle is less than that of an outside resistance. This is characterized by muscle lengthening, despite actin-myosin crossbridge formation. Research has indicated that muscles acting eccentrically are capable of producing more force when compared to muscles acting concentrically. Further, research has shown ECC muscle actions may have different fatigue patterns that CON actions. The purpose of this study was to determine if a) ECC bench press yields greater strength than concentric (CON) as measured by one-repetition maximum (1RM), b) there is a difference between the number of repetitions that can be completed concentrically and eccentrically under the same relative intensities of 1RM (90%, 80%, 70%, 60%), c) a prediction model may be able to predict ECC 1RM from CON 1RM or CON repetitions to fatigue. For this study, 30 healthy males (age = 24.63 + 5.6 years) were tested for 1RM in CON and ECC bench press, as well as the number of repetitions they were able to complete at various intensities of mode-specific 1RM. A mechanical hoist was affixed to a gantry crane and placed over a standard weightlifting bench. The hoist was connected to 45lb plates that were loaded on a standard barbell, which allowed for mechanical raising and lowering of the barbell. For CON repetitions, the weight was mechanically lowered to the chest and the participant pressed it up. For ECC repetitions, the weight was mechanically raised and the participant lowered it. Paired t-tests showed that ECC 1RM was significantly (p < 0.05) greater than CON 1RM (ECC =255.17 + 68.37lbs, CON = 205.83 + 58.43lbs). There was a significant difference (p < 0.05) between the number of repetitions completed at 90% 1RM (CON = 4.57 + 2.21 repetitions, ECC = 7.67 + 3.24 repetitions). There were no differences in repetitions completed at any other intensity 1RM. CON 1RM and the number of repetitions completed with two different absolute loads (130-150lbs and 155-175lbs) concentrically and eccentrically were valid predictors of ECC 1RM. These data indicate that ECC actions yield increased force capabilities than CON actions, there is no difference in the rate of the fatigue, and ECC 1RM may be predicted from various CON tests.
ContributorsKelly, Stephen B., Jr (Author) / Hooker, Steven (Thesis advisor) / Brown, Lee (Committee member) / Buman, Matthew (Committee member) / Gaesser, Glenn (Committee member) / Swan, Pamela (Committee member) / Arizona State University (Publisher)
Created2013
Mechanical Behavior of Meteorites: Multiscale Characterization of the Strength and Failure Mechanism
Description
In this research, the chemical and mineralogical compositions, physical and mechanical properties, and failure mechanisms of two ordinary chondrite (OCs) meteorites Aba Panu (L3) and Viñales (L6), and the iron meteorite called Gibeon (IVA) were studied. OCs are dominated by anhydrous silicates with lesser amounts of sulfides and native Fe-Ni metals, while Gibeon is primarily composed of Fe-Ni metals with scattered inclusions of graphite and troilite. The OCs were investigated to understand their response to compressive loading, using a three-dimensional (3-D) Digital Image Correlation (DIC) technique to measure full-field deformation and strain during compression. The DIC data were also used to identify the effects of mineralogical and structural heterogeneity on crack formation and growth. Even though Aba Panu and Viñales are mineralogically similar and are both classified as L ordinary chondrites, they exhibit differences in compressive strengths due to variations in chemical compositions, microstructure, and the presence of cracks and shock veins. DIC data of Aba Panu and Viñales show a brittle failure mechanism, consistent with the crack formation and growth from pre-existing microcracks and porosity. In contrast, the Fe-Ni phases of the Gibeon meteorite deform plastically without rupture during compression, whereas during tension, plastic deformations followed by necking lead to final failure. The Gibeon DIC results showed strain concentration in the tensile gauge region along the sample edge, resulting in the initiation of new damage surfaces that propagated perpendicular to the loading direction. Finally, an in-situ low-temperature testing method of iron meteorites was developed to study the response of their unique microstructure and failure mechanism.
ContributorsRabbi, Md Fazle (Author) / Chattopadhyay, Aditi (Thesis advisor) / Garvie, Laurence A.J. (Thesis advisor) / Liu, Yongming (Committee member) / Fard, Masoud Yekani (Committee member) / Cotto-Figueroa, Desiree (Committee member) / Arizona State University (Publisher)
Created2023