Matching Items (4)
Filtering by

Clear all filters

147871-Thumbnail Image.png
Description

Supported catalytic nanoparticles undergo rapid structural transformations faster than many transmission electron microscopes (TEMs) can track. This is the case with platinum nanoparticles supported on cerium oxide (Pt/CeO2) in a CO and O2 gaseous environment. By furthering our understanding of the structural dynamics of the Pt/CeO2 system, improved catalyst design

Supported catalytic nanoparticles undergo rapid structural transformations faster than many transmission electron microscopes (TEMs) can track. This is the case with platinum nanoparticles supported on cerium oxide (Pt/CeO2) in a CO and O2 gaseous environment. By furthering our understanding of the structural dynamics of the Pt/CeO2 system, improved catalyst design principles may be derived to enhance the efficiency of this catalyst. Developing static models of a 2 nm Pt nanoparticle supported on CeO2 and simulating TEM images of the models was found to create similar images to those seen in experimental TEM time-resolved series of the system. Rotations of static models on a ceria support provides a way to understand the experimental samples in three dimensions, which is difficult in two dimensional TEM images. This project expands the possibilities of interpreting TEM images of catalytic systems.

ContributorsBlock, Claire (Author) / Crozier, Peter (Thesis director) / Muhich, Christopher (Committee member) / Materials Science and Engineering Program (Contributor, Contributor) / Watts College of Public Service & Community Solut (Contributor) / Barrett, The Honors College (Contributor)
Created2021-05
147516-Thumbnail Image.png
Description

Lithium ion batteries are quintessential components of modern life. They are used to power smart devices — phones, tablets, laptops, and are rapidly becoming major elements in the automotive industry. Demand projections for lithium are skyrocketing with production struggling to keep up pace. This drive is due mostly to the

Lithium ion batteries are quintessential components of modern life. They are used to power smart devices — phones, tablets, laptops, and are rapidly becoming major elements in the automotive industry. Demand projections for lithium are skyrocketing with production struggling to keep up pace. This drive is due mostly to the rapid adoption of electric vehicles; sales of electric vehicles in 2020 are more than double what they were only a year prior. With such staggering growth it is important to understand how lithium is sourced and what that means for the environment. Will production even be capable of meeting the demand as more industries make use of this valuable element? How will the environmental impact of lithium affect growth? This thesis attempts to answer these questions as the world looks to a decade of rapid growth for lithium ion batteries.

ContributorsMelton, John (Author) / Brian, Jennifer (Thesis director) / Karwat, Darshawn (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2021-05
161284-Thumbnail Image.png
Description
Lithium conducting garnets in the family of Li7La3Zr2O12 (LLZO) are promising lithium conductors for solid-state batteries, due to their high ionic conductivity, thermal stability, and electrochemical stability with metallic lithium. Despite these advantages, LLZO requires a large energy input to synthesize and process. Generally, LLZO is synthesized using solid-state reaction

Lithium conducting garnets in the family of Li7La3Zr2O12 (LLZO) are promising lithium conductors for solid-state batteries, due to their high ionic conductivity, thermal stability, and electrochemical stability with metallic lithium. Despite these advantages, LLZO requires a large energy input to synthesize and process. Generally, LLZO is synthesized using solid-state reaction (SSR) from oxide precursors, requiring high reaction temperatures (900-1000 °C) and producing powder with large particle sizes, necessitating high energy milling to improve sinterability. In this dissertation, two classes of advanced synthesis methods – sol-gel polymer-combustion and molten salt synthesis (MSS) – are employed to obtain LLZO submicron powders at lower temperatures. In the first case, nanopowders of LLZO are obtained in a few hours at 700 °C via a novel polymer combustion process, which can be sintered to dense electrolytes possessing ionic conductivity up to 0.67 mS cm-1 at room temperature. However, the limited throughput of this combustion process motivated the use of molten salt synthesis, wherein a salt mixture is used as a high temperature solvent, allowing faster interdiffusion of atomic species than solid-state reactions. A eutectic mixture of LiCl-KCl allows formation of submicrometer undoped, Al-doped, Ga-doped, and Ta-doped LLZO at 900 °C in 4 h, with total ionic conductivities between 0.23-0.46 mS cm-1. By using a highly basic molten salt medium, Ta-doped LLZO (LLZTO) can be obtained at temperatures as low as 550 °C, with an ionic conductivity of 0.61 mS cm-1. The formation temperature can be further reduced by using Ta-doped, La-excess pyrochlore-type lanthanum zirconate (La2Zr2O7, LZO) as a quasi-single-source precursor, which convert to LLZTO as low as 400 °C upon addition of a Li-source. Further, doped pyrochlores can be blended with a Li-source and directly sintered to a relative density up to 94.7% with high conductivity (0.53 mS cm-1). Finally, a propensity for compositional variation in LLZTO powders and sintered ceramics was observed and for the first time explored in detail. By comparing LLZTO obtained from combustion, MSS, and SSR, a correlation between increased elemental inhomogeneity and reduced ionic conductivity is observed. Implications for garnet-based solid-state batteries and strategies to mitigate elemental inhomogeneity are discussed.
ContributorsWeller, Jon Mark (Author) / Chan, Candace K (Thesis advisor) / Crozier, Peter (Committee member) / Sieradzki, Karl (Committee member) / Arizona State University (Publisher)
Created2021
132562-Thumbnail Image.png
Description
Titanium dioxide is an essential material under research for energy and environmental applications, chiefly through its photocatalytic properties. These properties allow it to be used for water-splitting, detoxification, and photovoltaics, in addition to its conventional uses in pigmentation and sunscreen. Titanium dioxide exists in several polymorphic structures, of

Titanium dioxide is an essential material under research for energy and environmental applications, chiefly through its photocatalytic properties. These properties allow it to be used for water-splitting, detoxification, and photovoltaics, in addition to its conventional uses in pigmentation and sunscreen. Titanium dioxide exists in several polymorphic structures, of which the most common are rutile and anatase. We focused on anatase for the purposes of this research, due to its promising results for hydrolysis.

Anatase exists often in its reduced form (TiO2-x), enabling it to perform redox reactions through the absorption and release of oxygen into/from the crystal lattice. These processes result in structural changes, induced by defects in the material, which can theoretically be observed using advanced characterization methods. In situ electron microscopy is one of such methods, and can provide a window into these structural changes. However, in order to interpret the structural evolution caused by defects in materials, it is often necessary and pertinent to use atomistic simulations to compare the experimental images with models.

In this thesis project, we modeled the defect structures in anatase, around oxygen vacancies and at surfaces, using molecular dynamics, benchmarked with density functional theory. Using a “reactive” forcefield designed for the simulation of interactions between anatase and water that can model and treat bonding through the use of bond orders, different vacancy structures were analyzed and simulated. To compare these theoretical, generated models with experimental data, the “multislice approach” to TEM image simulation was used. We investigated a series of different vacancy configurations and surfaces and generated fingerprints for comparison with TEM experiments. This comparison demonstrated a proof of concept for a technique suggesting the possibility for the identification of oxygen vacancy structures directly from TEM images. This research aims to improve our atomic-level understanding of oxide materials, by providing a methodology for the analysis of vacancy formation from very subtle phenomena in TEM images.
ContributorsShindel, Benjamin Noam (Author) / Crozier, Peter (Thesis director) / Anwar, Shahriar (Committee member) / Singh, Arunima (Committee member) / Materials Science and Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2019-05