Membranes are a key part of pervaporation processes, which is generally a more
efficient process for selective removal of alcohol from water than distillation. It is
necessary that the membranes have high alcohol permeabilities and selectivities.
Polydimethylsiloxane (PDMS) based mixed matrix membranes (MMMs) have
demonstrated very promising results. Zeolitic imidazolate framework-71 (ZIF-71)
demonstrated promising alcohol separation abilities. In this dissertation, we present
fundamental studies on the synthesis of ZIF-71/PDMS MMMs.
Free-standing ZIF-71/ PDMS membranes with 0, 5, 25 and 40 wt % ZIF-71
loadings were prepared and the pervaporation separation for ethanol and 1-butanol from
water was measured. ZIF-71/PDMS MMMs were formed through addition cure and
condensation cure methods. Addition cure method was not compatible with ZIF-71
resulting in membranes with poor mechanical properties, while the condensation cure
method resulted in membranes with good mechanical properties. The 40 wt % ZIF-71
loading PDMS nanocomposite membranes achieved a maximum ethanol/water selectivity
of 0.81 ± 0.04 selectivity and maximum 1-butnaol/water selectivity of 5.64 ± 0.15.
The effects of synthesis time, temperature, and reactant ratio on ZIF-71 particle
size and the effect of particle size on membrane performance were studied. Temperature
had the greatest effect on ZIF-71 particle size as the synthesis temperature varied from -
20 to 35 ºC. The ZIF-71 synthesized had particle diameters ranging from 150 nm to 1
μm. ZIF-71 particle size is critical in ZIF-71/PDMS composite membrane performance
for alcohol removal from water through pervaporation. The membranes made with
micron sized ZIF-71 particles showed higher alcohol/water selectivity than those with
smaller particles. Both alcohol and water permeability increased when larger sized ZIF-
71 particles were incorporated.
ZIF-71 particles were modified with four ligands through solvent assisted linker
exchange (SALE) method: benzimidazole (BIM), 5-methylbenzimidazole (MBIM), 5,6-
dimethylbenzimidazole (DMBIM) and 4-Phenylimidazole (PI). The morphology of ZIF-
71 were maintained after the modification. ZIF-71/PDMS composite membranes with 25
wt% loading modified ZIF-71 particles were made for alcohol/water separation. Better
particle dispersion in PDMS polymer matrix was observed with the ligand modified ZIFs.
For both ethanol/water and 1-butanol/water separations, the alcohol permeability and
alcohol/water selectivity were lowered after the ZIF-71 ligand exchange reaction.
efficient process for selective removal of alcohol from water than distillation. It is
necessary that the membranes have high alcohol permeabilities and selectivities.
Polydimethylsiloxane (PDMS) based mixed matrix membranes (MMMs) have
demonstrated very promising results. Zeolitic imidazolate framework-71 (ZIF-71)
demonstrated promising alcohol separation abilities. In this dissertation, we present
fundamental studies on the synthesis of ZIF-71/PDMS MMMs.
Free-standing ZIF-71/ PDMS membranes with 0, 5, 25 and 40 wt % ZIF-71
loadings were prepared and the pervaporation separation for ethanol and 1-butanol from
water was measured. ZIF-71/PDMS MMMs were formed through addition cure and
condensation cure methods. Addition cure method was not compatible with ZIF-71
resulting in membranes with poor mechanical properties, while the condensation cure
method resulted in membranes with good mechanical properties. The 40 wt % ZIF-71
loading PDMS nanocomposite membranes achieved a maximum ethanol/water selectivity
of 0.81 ± 0.04 selectivity and maximum 1-butnaol/water selectivity of 5.64 ± 0.15.
The effects of synthesis time, temperature, and reactant ratio on ZIF-71 particle
size and the effect of particle size on membrane performance were studied. Temperature
had the greatest effect on ZIF-71 particle size as the synthesis temperature varied from -
20 to 35 ºC. The ZIF-71 synthesized had particle diameters ranging from 150 nm to 1
μm. ZIF-71 particle size is critical in ZIF-71/PDMS composite membrane performance
for alcohol removal from water through pervaporation. The membranes made with
micron sized ZIF-71 particles showed higher alcohol/water selectivity than those with
smaller particles. Both alcohol and water permeability increased when larger sized ZIF-
71 particles were incorporated.
ZIF-71 particles were modified with four ligands through solvent assisted linker
exchange (SALE) method: benzimidazole (BIM), 5-methylbenzimidazole (MBIM), 5,6-
dimethylbenzimidazole (DMBIM) and 4-Phenylimidazole (PI). The morphology of ZIF-
71 were maintained after the modification. ZIF-71/PDMS composite membranes with 25
wt% loading modified ZIF-71 particles were made for alcohol/water separation. Better
particle dispersion in PDMS polymer matrix was observed with the ligand modified ZIFs.
For both ethanol/water and 1-butanol/water separations, the alcohol permeability and
alcohol/water selectivity were lowered after the ZIF-71 ligand exchange reaction.
ContributorsYin, Huidan (Author) / Lind, Mary Laura (Thesis advisor) / Mu, Bin (Committee member) / Nielsen, David (Committee member) / Seo, Don (Committee member) / Lin, Jerry (Committee member) / Arizona State University (Publisher)
Created2017
Description
In this research, construction of a model membrane system using Polyvinylidene Chloride-Co Acrylonitrile and Linde Type A zeolites is described. The systems aims to separate out flow through zeolite pores and flow through interfaces between zeolites and polymers through the use of pore filled and pore open zeolites. Permeation tests and salt rejection tests were performed, and the data analyzed to yield approximation of separated flow through zeolites and interfaces. This work concludes the more work is required to bring the model system into a functioning state. New polymer selections and new techniques to produce the membrane system are described for future work.
ContributorsShabilla, Andrew Daniel (Author) / Lind, Mary Laura (Thesis director) / Lin, Jerry (Committee member) / Barrett, The Honors College (Contributor) / Chemical Engineering Program (Contributor)
Created2014-05
Description
Metal-organic frameworks (MOFs) are a new set of porous materials comprised of metals or metal clusters bonded together in a coordination system by organic linkers. They are becoming popular for gas separations due to their abilities to be tailored toward specific applications. Zirconium MOFs in particular are known for their high stability under standard temperature and pressure due to the strength of the Zirconium-Oxygen coordination bond. However, the acid modulator needed to ensure long range order of the product also prevents complete linker deprotonation. This leads to a powder product that cannot easily be incorporated into continuous MOF membranes. This study therefore implemented a new bi-phase synthesis technique with a deprotonating agent to achieve intergrowth in UiO-66 membranes. Crystal intergrowth will allow for effective gas separations and future permeation testing. During experimentation, successful intergrown UiO-66 membranes were synthesized and characterized. The degree of intergrowth and crystal orientations varied with changing deprotonating agent concentration, modulator concentration, and ligand:modulator ratios. Further studies will focus on achieving the same results on porous substrates.
ContributorsClose, Emily Charlotte (Author) / Mu, Bin (Thesis director) / Shan, Bohan (Committee member) / Chemical Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2016-12
Description
Amine-modified solid sorbents and membrane separation are promising technologies for separation and capture of carbon dioxide (CO2) from combustion flue gas. Amine absorption processes are mature, but still have room for improvement. This work focused on the synthesis of amine-modified aerogels and metal-organic framework-5 (MOF-5) membranes for CO2 separation. A series of solid sorbents were synthesized by functionalizing amines on the surface of silica aerogels. This was done by three coating methods: physical adsorption, magnetically assisted impact coating (MAIC) and atomic layer deposition (ALD). CO2 adsorption capacity of the sorbents was measured at room temperature in a Cahn microbalance. The sorbents synthesized by physical adsorption show the largest CO2 adsorption capacity (1.43-1.63 mmol CO2/g). An additional sorbent synthesized by ALD on hydrophilic aerogels at atmospheric pressures shows an adsorption capacity of 1.23 mmol CO2/g. Studies on one amine-modified sorbent show that the powder is of agglomerate bubbling fluidization (ABF) type. The powder is difficult to fluidize and has limited bed expansion. The ultimate goal is to configure the amine-modified sorbents in a micro-jet assisted gas fluidized bed to conduct adsorption studies. MOF-5 membranes were synthesized on α-alumina supports by two methods: in situ synthesis and secondary growth synthesis. Characterization by scanning electron microscope (SEM) imaging and X-ray diffraction (XRD) show that the membranes prepared by both methods have a thickness of 14-16 μm, and a MOF-5 crystal size of 15-25 μm with no apparent orientation. Single gas permeation results indicate that the gas transport through both membranes is determined by a combination of Knudsen diffusion and viscous flow. The contribution of viscous flow indicates that the membranes have defects.
ContributorsRosa, Teresa M (Author) / Lin, Jerry (Thesis advisor) / Pfeffer, Robert (Thesis advisor) / Dai, Lenore (Committee member) / Nielsen, David (Committee member) / Arizona State University (Publisher)
Created2010
Description
ABSTRACT
Large-pore metal-organic framework (MOF) membranes offer potential in a number of gas and liquid separations due to their wide and selective adsorption capacities. A key characteristic of a number of MOF and zeolitic imidazolate framework (ZIF) membranes is their highly selective adsorption capacities for CO2. These membranes offer very tangible potential to separate CO2 in a wide array of industrially relevant separation processes, such as the separation from CO2 in flue gas emissions, as well as the sweetening of methane.
By virtue of this, the purpose of this dissertation is to synthesize and characterize two linear large-pore MOF membranes, MOF-5 and ZIF-68, and to study their gas separation properties in binary mixtures of CO¬2/N2 and CO2/CH4. The three main objectives researched are as follows. The first is to study the pervaporation behavior and stability of MOF-5; this is imperative because although MOF-5 exhibits desirable adsorption and separation characteristics, it is very unstable in atmospheric conditions. In determining its stability and behavior in pervaporation, this material can be utilized in conditions wherein atmospheric levels of moisture can be avoided. The second objective is to synthesize, optimize and characterize a linear, more stable MOF membrane, ZIF-68. The final objective is to study in tandem the high-pressure gas separation behavior of MOF-5 and ZIF-68 in binary gas systems of both CO2/N2 and CO2/CH4.
Continuous ZIF-68 membranes were synthesized via the reactive seeding method and the modified reactive seeding method. These membranes, as with the MOF-5 membranes synthesized herein, both showed adherence to Knudsen diffusion, indicating limited defects. Organic solvent experiments indicated that MOF-5 and ZIF-68 were stable in a variety of organic solvents, but both showed reductions in permeation flux of the tested molecules. These reductions were attributed to fouling and found to be cumulative up until a saturation of available bonding sites for molecules was reached and stable pervaporation permeances were reached for both. Gas separation behavior for MOF-5 showed direct dependence on the CO2 partial pressure and the overall feed pressure, while ZIF-68 did not show similar behavior. Differences in separation behavior are attributable to orientation of the ZIF-68 membranes.
Large-pore metal-organic framework (MOF) membranes offer potential in a number of gas and liquid separations due to their wide and selective adsorption capacities. A key characteristic of a number of MOF and zeolitic imidazolate framework (ZIF) membranes is their highly selective adsorption capacities for CO2. These membranes offer very tangible potential to separate CO2 in a wide array of industrially relevant separation processes, such as the separation from CO2 in flue gas emissions, as well as the sweetening of methane.
By virtue of this, the purpose of this dissertation is to synthesize and characterize two linear large-pore MOF membranes, MOF-5 and ZIF-68, and to study their gas separation properties in binary mixtures of CO¬2/N2 and CO2/CH4. The three main objectives researched are as follows. The first is to study the pervaporation behavior and stability of MOF-5; this is imperative because although MOF-5 exhibits desirable adsorption and separation characteristics, it is very unstable in atmospheric conditions. In determining its stability and behavior in pervaporation, this material can be utilized in conditions wherein atmospheric levels of moisture can be avoided. The second objective is to synthesize, optimize and characterize a linear, more stable MOF membrane, ZIF-68. The final objective is to study in tandem the high-pressure gas separation behavior of MOF-5 and ZIF-68 in binary gas systems of both CO2/N2 and CO2/CH4.
Continuous ZIF-68 membranes were synthesized via the reactive seeding method and the modified reactive seeding method. These membranes, as with the MOF-5 membranes synthesized herein, both showed adherence to Knudsen diffusion, indicating limited defects. Organic solvent experiments indicated that MOF-5 and ZIF-68 were stable in a variety of organic solvents, but both showed reductions in permeation flux of the tested molecules. These reductions were attributed to fouling and found to be cumulative up until a saturation of available bonding sites for molecules was reached and stable pervaporation permeances were reached for both. Gas separation behavior for MOF-5 showed direct dependence on the CO2 partial pressure and the overall feed pressure, while ZIF-68 did not show similar behavior. Differences in separation behavior are attributable to orientation of the ZIF-68 membranes.
ContributorsKasik, Alexandra Marie (Author) / Lin, Jerry (Thesis advisor) / Tasooji, Amaneh (Committee member) / Alford, Terry (Committee member) / Arizona State University (Publisher)
Created2015