Matching Items (5)
Filtering by
- All Subjects: Fatigue
- Creators: Solanki, Kiran
- Creators: Mignolet, Marc
- Status: Published
Description
Aluminum alloys and their composites are attractive materials for applications requiring high strength-to-weight ratios and reasonable cost. Many of these applications, such as those in the aerospace industry, undergo fatigue loading. An understanding of the microstructural damage that occurs in these materials is critical in assessing their fatigue resistance. Two distinct experimental studies were performed to further the understanding of fatigue damage mechanisms in aluminum alloys and their composites, specifically fracture and plasticity. Fatigue resistance of metal matrix composites (MMCs) depends on many aspects of composite microstructure. Fatigue crack growth behavior is particularly dependent on the reinforcement characteristics and matrix microstructure. The goal of this work was to obtain a fundamental understanding of fatigue crack growth behavior in SiC particle-reinforced 2080 Al alloy composites. In situ X-ray synchrotron tomography was performed on two samples at low (R=0.1) and at high (R=0.6) R-ratios. The resulting reconstructed images were used to obtain three-dimensional (3D) rendering of the particles and fatigue crack. Behaviors of the particles and crack, as well as their interaction, were analyzed and quantified. Four-dimensional (4D) visual representations were constructed to aid in the overall understanding of damage evolution. During fatigue crack growth in ductile materials, a plastic zone is created in the region surrounding the crack tip. Knowledge of the plastic zone is important for the understanding of fatigue crack formation as well as subsequent growth behavior. The goal of this work was to quantify the 3D size and shape of the plastic zone in 7075 Al alloys. X-ray synchrotron tomography and Laue microdiffraction were used to non-destructively characterize the volume surrounding a fatigue crack tip. The precise 3D crack profile was segmented from the reconstructed tomography data. Depth-resolved Laue patterns were obtained using differential-aperture X-ray structural microscopy (DAXM), from which peak-broadening characteristics were quantified. Plasticity, as determined by the broadening of diffracted peaks, was mapped in 3D. Two-dimensional (2D) maps of plasticity were directly compared to the corresponding tomography slices. A 3D representation of the plastic zone surrounding the fatigue crack was generated by superimposing the mapped plasticity on the 3D crack profile.
ContributorsHruby, Peter (Author) / Chawla, Nikhilesh (Thesis advisor) / Solanki, Kiran (Committee member) / Liu, Yongming (Committee member) / Arizona State University (Publisher)
Created2014
Description
This dissertation presents methods for addressing research problems that currently can only adequately be solved using Quality Reliability Engineering (QRE) approaches especially accelerated life testing (ALT) of electronic printed wiring boards with applications to avionics circuit boards. The methods presented in this research are generally applicable to circuit boards, but the data generated and their analysis is for high performance avionics. Avionics equipment typically requires 20 years expected life by aircraft equipment manufacturers and therefore ALT is the only practical way of performing life test estimates. Both thermal and vibration ALT induced failure are performed and analyzed to resolve industry questions relating to the introduction of lead-free solder product and processes into high reliability avionics. In chapter 2, thermal ALT using an industry standard failure machine implementing Interconnect Stress Test (IST) that simulates circuit board life data is compared to real production failure data by likelihood ratio tests to arrive at a mechanical theory. This mechanical theory results in a statistically equivalent energy bound such that failure distributions below a specific energy level are considered to be from the same distribution thus allowing testers to quantify parameter setting in IST prior to life testing. In chapter 3, vibration ALT comparing tin-lead and lead-free circuit board solder designs involves the use of the likelihood ratio (LR) test to assess both complete failure data and S-N curves to present methods for analyzing data. Failure data is analyzed using Regression and two-way analysis of variance (ANOVA) and reconciled with the LR test results that indicating that a costly aging pre-process may be eliminated in certain cases. In chapter 4, vibration ALT for side-by-side tin-lead and lead-free solder black box designs are life tested. Commercial models from strain data do not exist at the low levels associated with life testing and need to be developed because testing performed and presented here indicate that both tin-lead and lead-free solders are similar. In addition, earlier failures due to vibration like connector failure modes will occur before solder interconnect failures.
ContributorsJuarez, Joseph Moses (Author) / Montgomery, Douglas C. (Thesis advisor) / Borror, Connie M. (Thesis advisor) / Gel, Esma (Committee member) / Mignolet, Marc (Committee member) / Pan, Rong (Committee member) / Arizona State University (Publisher)
Created2012
Description
In-situ fatigue damage diagnosis and prognosis is a challenging problem for both metallic and composite materials and structures. There are various uncertainties arising from material properties, component geometries, measurement noise, feature extraction techniques, and modeling errors. It is essential to manage and incorporate these uncertainties in order to achieve accurate damage detection and remaining useful life (RUL) prediction.
The aim of this study is to develop an integrated fatigue damage diagnosis and prognosis framework for both metallic and composite materials. First, Lamb waves are used as the in-situ damage detection technique to interrogate the damaged structures. Both experimental and numerical analysis for the Lamb wave propagation within aluminum are conducted. The RUL of lap joints under variable and constant fatigue loading is predicted using the Bayesian updating by incorporating damage detection information and various sources of uncertainties. Following this, the effect of matrix cracking and delamination in composite laminates on the Lamb wave propagation is investigated and a generalized probabilistic delamination size and location detection framework using Bayesian imaging method (BIM) is proposed and validated using the composite fatigue testing data. The RUL of the open-hole specimen is predicted using the overall stiffness degradation under fatigue loading. Next, the adjoint method-based damage detection framework is proposed considering the physics of heat conduction or elastic wave propagation. Different from the classical wave propagation-based method, the received signal under pristine condition is not necessary for estimating the damage information. This method can be successfully used for arbitrary damage location and shape profiling for any materials with higher accuracy and resolution. Finally, some conclusions and future work are generated based on the current investigation.
The aim of this study is to develop an integrated fatigue damage diagnosis and prognosis framework for both metallic and composite materials. First, Lamb waves are used as the in-situ damage detection technique to interrogate the damaged structures. Both experimental and numerical analysis for the Lamb wave propagation within aluminum are conducted. The RUL of lap joints under variable and constant fatigue loading is predicted using the Bayesian updating by incorporating damage detection information and various sources of uncertainties. Following this, the effect of matrix cracking and delamination in composite laminates on the Lamb wave propagation is investigated and a generalized probabilistic delamination size and location detection framework using Bayesian imaging method (BIM) is proposed and validated using the composite fatigue testing data. The RUL of the open-hole specimen is predicted using the overall stiffness degradation under fatigue loading. Next, the adjoint method-based damage detection framework is proposed considering the physics of heat conduction or elastic wave propagation. Different from the classical wave propagation-based method, the received signal under pristine condition is not necessary for estimating the damage information. This method can be successfully used for arbitrary damage location and shape profiling for any materials with higher accuracy and resolution. Finally, some conclusions and future work are generated based on the current investigation.
ContributorsPeng, Tishun (Author) / Liu, Yongming (Thesis advisor) / Chattopadhyay, Aditi (Committee member) / Mignolet, Marc (Committee member) / Papandreou-Suppappola, Antonia (Committee member) / Tang, Pingbo (Committee member) / Arizona State University (Publisher)
Created2016
Description
The use of solar energy to produce power has increased substantially in the past few decades. In an attempt to provide uninterrupted solar power, production plants may find themselves having to operate the systems at temperatures higher than the operational capacity of the materials used in many of their components, which affects the microstructural and mechanical properties of those materials. Failures in components that have been exposed to these excessive temperatures have been observed during operations in the turbine used by AORA Solar Ltd. A particular component of interest was made of a material similar to the Ni-based superalloy Inconel 718 (IN 718), which was observed to have damage that is believed to have been initiated by Foreign Object Damage (FOD) and worsened by the high temperatures in the turbine. The potential links among the observed failure, FOD and the high temperatures of operation are investigated in this study.
IN718 is a precipitation hardened nickel superalloy with resistance to oxidation and ability to withstand high stresses over a wide range of temperatures. Several studies have been conducted to understand IN 718 tensile and fatigue properties at elevated temperatures (600- 950°C). However, this study focuses on understanding the behavior of IN718 with FOD induced by a stream of 50 μm Alumina particles at a velocity of 200 m/s. under high cycle fatigue at an elevated temperature of 1050 °C. Tensile tests were conducted for both as-received and heat treated (1050 °C in air for 8hrs) samples at room and high temperature. Fatigue tests were performed at heat treated samples at 1050 °C for samples with and without ablation. The test conditions were as similar as possible to the conditions in the AORA turbine. The results of the study provide an insight into tensile properties, fatigue properties and FOD. The results indicated a reduction in fatigue life for the samples with ablation damage, where crack nucleation occurred either at the edge or inside the ablation region and multisite cracking was observed under far field stresses that were the same than for pristine samples, which showed single cracks. Fracture surfaces indicate intergranular fracture, with the presence of secondary cracks and a lack of typical fatigue features, e.g., beach marks which was attributed to environmental effects and creep.
IN718 is a precipitation hardened nickel superalloy with resistance to oxidation and ability to withstand high stresses over a wide range of temperatures. Several studies have been conducted to understand IN 718 tensile and fatigue properties at elevated temperatures (600- 950°C). However, this study focuses on understanding the behavior of IN718 with FOD induced by a stream of 50 μm Alumina particles at a velocity of 200 m/s. under high cycle fatigue at an elevated temperature of 1050 °C. Tensile tests were conducted for both as-received and heat treated (1050 °C in air for 8hrs) samples at room and high temperature. Fatigue tests were performed at heat treated samples at 1050 °C for samples with and without ablation. The test conditions were as similar as possible to the conditions in the AORA turbine. The results of the study provide an insight into tensile properties, fatigue properties and FOD. The results indicated a reduction in fatigue life for the samples with ablation damage, where crack nucleation occurred either at the edge or inside the ablation region and multisite cracking was observed under far field stresses that were the same than for pristine samples, which showed single cracks. Fracture surfaces indicate intergranular fracture, with the presence of secondary cracks and a lack of typical fatigue features, e.g., beach marks which was attributed to environmental effects and creep.
ContributorsShenoy, Sneha (Author) / Peralta, Pedro (Thesis advisor) / Solanki, Kiran (Committee member) / Sieradzki, Karl (Committee member) / Arizona State University (Publisher)
Created2017
Description
In real world applications, materials undergo a simultaneous combination of tension, compression, and torsion as a result of high velocity impact. The split Hopkinson pressure bar (SHPB) is an effective tool for analyzing stress-strain response of materials at high strain rates but currently little can be done to produce a synchronized combination of these varying impacts. This research focuses on fabricating a flange which will be mounted on the incident bar of a SHPB and struck perpendicularly by a pneumatically driven striker thus allowing for torsion without interfering with the simultaneous compression or tension. Analytical calculations are done to determine size specifications of the flange to protect against yielding or failure. Based on these results and other design considerations, the flange and a complementary incident bar are created. Timing can then be established such that the waves impact the specimen at the same time causing simultaneous loading of a specimen. This thesis allows research at Arizona State University to individually incorporate all uniaxial deformation modes (tension, compression, and torsion) at high strain rates as well as combining either of the first two modes with torsion. Introduction of torsion will expand the testing capabilities of the SHPB at ASU and allow for more in depth analysis of the mechanical behavior of materials under impact loading. Combining torsion with tension or compression will promote analysis of a material's adherence to the Von Mises failure criterion. This greater understanding of material behavior can be implemented into models and simulations thereby improving the accuracy with which engineers can design new structures.
ContributorsVotroubek, Edward Daniel (Author) / Solanki, Kiran (Thesis director) / Oswald, Jay (Committee member) / Mechanical and Aerospace Engineering Program (Contributor) / Barrett, The Honors College (Contributor)
Created2016-05