Description
The work presented in this thesis covers the synthesis and characterization of an ionomer that is applicable to zinc-air batteries. Polysulfone polymer is first chloromethylated and then quaternized to create an ion-conducting polymer. Nuclear magnetic resonance (NMR) spectra indicates that the degree of chloromethylation was 114%. The chemical and physical properties that were investigated include: the ionic conductivity, ion exchange capacity, water retention capacity, diameter and thickness swelling ratios, porosity, glass transition temperature, ionic conductivity enhanced by free salt addition, and the concentration and diffusivity of oxygen within the ionomer. It was found that the fully hydrated hydroxide form of the ionomer had a room temperature ionic conductivity of 39.92mS/cm while the chloride form had a room temperature ionic conductivity of 11.80mS/cm. The ion exchange capacity of the ionomer was found to be 1.022mmol/g. The water retention capacity (WRC) of the hydroxide form was found to be 172.6% while the chloride form had a WRC of 67.9%. The hydroxide form of the ionomer had a diameter swelling ratio of 34% and a thickness swelling ratio of 55%. The chloride form had a diameter swelling ratio of 32% and a thickness swelling ratio of 28%. The largest pore size in the ionomer was found to be 32.6nm in diameter. The glass transition temperature of the ionomer is speculated to be 344°C. A definite measurement could not be made. The room temperature ionic conductivity at 50% relative humidity was improved to 12.90mS/cm with the addition of 80% free salt. The concentration and diffusivity of oxygen in the ionomer was found to be 1.3 ±0.2mMol and (0.49 ±0.15)x10-5 cm2/s respectively. The ionomer synthesized in this research had material properties and performance that is comparable to other ionomers reported in the literature. This is an indication that this ionomer is suitable for further study and integration into a zinc-air battery. This thesis is concluded with suggestions for future research that is focused on improving the performance of the ionomer as well as improving the methodology.
ContributorsPadilla, Manuel (Author) / Friesen, Cody A (Thesis advisor) / Buttry, Daniel (Committee member) / Sieradzki, Karl (Committee member) / Arizona State University (Publisher)
Created2012
Description
ABSTRACT The behavior of the fission products, as they are released from fission events during nuclear reaction, plays an important role in nuclear fuel performance. Fission product release can occur through grain boundary (GB) at low burnups; therefore, this study simulates the mass transport of fission gases in a 2-D GB network to look into the effects of GB characteristics on this phenomenon, with emphasis on conditions that can lead to percolation. A finite element model was created based on the microstructure of a depleted UO2 sample characterized by Electron Backscattering Diffraction (EBSD). The GBs were categorized into high (D2), low (D1) and bulk diffusivity (Dbulk) based on their misorientation angles and Coincident Site Lattice (CSL) types. The simulation was run using different diffusivity ratios (D2/Dbulk) ranging from 1 to 10^8. The model was set up in three ways: constant temperature case, temperature gradient effects and window methods that mimic the environments in a Light Water Reactor (LWR). In general, the formation of percolation paths was observed at a ratio higher than 10^4 in the measured GB network, which had a 68% fraction of high diffusivity GBs. The presence of temperature gradient created an uneven concentration distribution and decreased the overall mass flux. Finally, radial temperature and fission gas concentration profiles were obtained for a fuel pellet in operation using an approximate 1-D model. The 100 µm long microstructurally explicit model was used to simulate, to the scale of a real UO2 pellet, the mass transport at different radial positions, with boundary conditions obtained from the profiles. Stronger percolation effects were observed at the intermediate and periphery position of the pellet. The results also showed that highest mass flux happens at the edge of a pellet at steady state to accommodate for the sharp concentration drop.
ContributorsLim, Harn Chyi (Author) / Peralta, Pedro (Thesis advisor) / Dey, Sandwip (Committee member) / Sieradzki, Karl (Committee member) / Arizona State University (Publisher)
Created2011
Description
A full understanding of material behavior is important for the prediction of residual useful life of aerospace structures via computational modeling. In particular, the influence of rolling-induced anisotropy on fatigue properties has not been studied extensively and it is likely to have a meaningful effect. In this work, fatigue behavior of a wrought Al alloy (2024-T351) is studied using notched uniaxial samples with load axes along either the longitudinal or transverse direction, and center notched biaxial samples (cruciforms) with a uniaxial stress state of equivalent amplitude about the bore. Local composition and crystallography were quantified before testing using Energy Dispersive Spectroscopy and Electron Backscattering Diffraction. Interrupted fatigue testing at stresses close to yielding was performed on the samples to nucleate and propagate short cracks and nucleation sites were located and characterized using standard optical and Scanning Electron Microscopy. Results show that crack nucleation occurred due to fractured particles for longitudinal dogbone/cruciform samples; while transverse samples nucleated cracks by debonded and fractured particles. Change in crack nucleation mechanism is attributed to dimensional change of particles with respect to the material axes caused by global anisotropy. Crack nucleation from debonding reduced life till matrix fracture because debonded particles are sharper and generate matrix cracks sooner than their fractured counterparts. Longitudinal samples experienced multisite crack initiation because of reduced cross sectional areas of particles parallel to the loading direction. Conversely the favorable orientation of particles in transverse samples reduced instances of particle fracture eliminating multisite cracking and leading to increased fatigue life. Cyclic tests of cruciform samples showed that crack growth favors longitudinal and transverse directions with few instances of crack growth 45 degrees (diagonal) to the rolling direction. The diagonal crack growth is attributed to stronger influences of local anisotropy on crack nucleation. It was observed that majority of the time crack nucleation is governed by the mixed influences of global and local anisotropies. Measurements of crystal directions parallel to the load on main crack paths revealed directions clustered near the {110} planes and high index directions. This trend is attributed to environmental effects as a result of cyclic testing in air.
ContributorsMakaš, Admir (Author) / Peralta, Pedro D. (Thesis advisor) / Davidson, Joseph K. (Committee member) / Sieradzki, Karl (Committee member) / Arizona State University (Publisher)
Created2011
Description
Lithium-ion batteries can fail and catch fire when overcharged, exposed to high temperatures or short-circuited due to the highly flammable organic liquid used in the electrolyte. Using inorganic solid electrolyte materials can potentially improve the safety factor. Additionally, nanostructured electrolyte materials may further enhanced performance by taking advantage of their large aspect ratio. In this work, the synthesis of two promising nanostructured solid electrolyte materials was explored. Amorphous lithium niobate nanowires were synthesized through the decomposition of a niobium-containing complex in a structure-directing solvent using a reflux method. Lithium lanthanum titanate was obtained via solid state reaction with titanium oxide nanowires as the titanium precursor, but the nanowire morphology could not be preserved due to high temperature sintering. Hyperbranched potassium lanthanum titanate was synthesized through hydrothermal route. This was the first time that hyperbranched nanowires with perovskite structure were made without any catalyst or substrate. This result has the potential to be applied to other perovskite materials.
ContributorsYang, Ting (Author) / Chan, Candace K. (Thesis advisor) / Crozier, Peter A. (Committee member) / Sieradzki, Karl (Committee member) / Arizona State University (Publisher)
Created2012
Description
As selenium and chromium are toxic even at low levels, it is very necessary to remove them from drinking water with proper ways. In this work, titanium dioxide based photocatalysts were mainly investigated in detail for their photoreduction ability towards selenate and chromate in aqueous environment. Firstly, photoreduction ability of layered double hydroxide (LDH) nanosheets with commercial TiO2 particle hybrid materials was investigated towards selenate or chromate. The results showed that commercial LDH/TiO2 (P90) composite, homemade LDH nanosheets/TiO2 (P90) composite and also in situ LDH/TiO2 (P25) composite all did not indicate significant improvement on photoreduction performance towards selenate or chromate. Secondly, TiO2 nanosheets material was synthesized with TiS2 as precursor via hydrothermal treatment. Morphology of TiO2 nanosheets were characterized by SEM, AFM and TEM. Photodegradation of MB (methylene blue) with TiO2 nanosheets was performed. In the future, first approach is to synthesize visible-light driven LDH photocatalyst NiFe-LDH nanosheets with TiO2 nanosheets hybrid material for selenate removal. Second approach is to use anion intercalation/insertion via electrochemical process to remove anions in drinking water.
ContributorsJing, Hangkun (Author) / Chan, Candace K. (Thesis advisor) / Sieradzki, Karl (Committee member) / Wang, Qinghua (Committee member) / Arizona State University (Publisher)
Created2018
Description
Structural stability and performance of structural materials is important for energy production, whether renewable or non renewable, to have uninterrupted energy supply, that is economically feasible and safe. High temperature metallic materials used in the turbines of AORA, an Israel-based clean energy producer, often experience high temperature, high stress and foreign object damage (FOD). In this study, efforts were made to study the effects of FOD on the fatigue life of these materials and to understand their failure mechanisms. The foreign objects/debris recovered by AORA were characterized using Powder X-ray Diffraction (XRD) and Energy Dispersive Spectroscopy (EDS) to identify composition and phases. To perform foreign object damage experiment a gas gun was built and results of XRD and EDS were used to select particles to mimic FOD in lab experiments for two materials of interest to AORA: Hastelloy X and SS 347. Electron Backscattering Diffraction, hardness and tensile tests were also performed to characterize microstructure and mechanical properties. Fatigue tests using at high temperature were performed on dog bone samples with and without FOD and the fracture surfaces and well as the regions affected by FOD were analyzed using Scanning Electron Microscopy (SEM) to understand the failure mechanism. The findings of these study indicate that FOD is causing multiple secondary cracks at and around the impact sites, which can potentially grow to coalesce and remove pieces of material, and the multisite damage could also lead to lower fatigue lives, despite the fact that the FOD site was not always the most favorable for initiation of the fatal fatigue crack. It was also seen by the effect of FOD on fatigue life that SS 347 is more susceptible to FOD than Hastelloy X.
ContributorsDobaria, Nirmal (Author) / Peralta, Pedro (Thesis advisor) / Sieradzki, Karl (Committee member) / Solanki, Kiran (Committee member) / Arizona State University (Publisher)
Created2016
Description
The use of solar energy to produce power has increased substantially in the past few decades. In an attempt to provide uninterrupted solar power, production plants may find themselves having to operate the systems at temperatures higher than the operational capacity of the materials used in many of their components, which affects the microstructural and mechanical properties of those materials. Failures in components that have been exposed to these excessive temperatures have been observed during operations in the turbine used by AORA Solar Ltd. A particular component of interest was made of a material similar to the Ni-based superalloy Inconel 718 (IN 718), which was observed to have damage that is believed to have been initiated by Foreign Object Damage (FOD) and worsened by the high temperatures in the turbine. The potential links among the observed failure, FOD and the high temperatures of operation are investigated in this study.
IN718 is a precipitation hardened nickel superalloy with resistance to oxidation and ability to withstand high stresses over a wide range of temperatures. Several studies have been conducted to understand IN 718 tensile and fatigue properties at elevated temperatures (600- 950°C). However, this study focuses on understanding the behavior of IN718 with FOD induced by a stream of 50 μm Alumina particles at a velocity of 200 m/s. under high cycle fatigue at an elevated temperature of 1050 °C. Tensile tests were conducted for both as-received and heat treated (1050 °C in air for 8hrs) samples at room and high temperature. Fatigue tests were performed at heat treated samples at 1050 °C for samples with and without ablation. The test conditions were as similar as possible to the conditions in the AORA turbine. The results of the study provide an insight into tensile properties, fatigue properties and FOD. The results indicated a reduction in fatigue life for the samples with ablation damage, where crack nucleation occurred either at the edge or inside the ablation region and multisite cracking was observed under far field stresses that were the same than for pristine samples, which showed single cracks. Fracture surfaces indicate intergranular fracture, with the presence of secondary cracks and a lack of typical fatigue features, e.g., beach marks which was attributed to environmental effects and creep.
IN718 is a precipitation hardened nickel superalloy with resistance to oxidation and ability to withstand high stresses over a wide range of temperatures. Several studies have been conducted to understand IN 718 tensile and fatigue properties at elevated temperatures (600- 950°C). However, this study focuses on understanding the behavior of IN718 with FOD induced by a stream of 50 μm Alumina particles at a velocity of 200 m/s. under high cycle fatigue at an elevated temperature of 1050 °C. Tensile tests were conducted for both as-received and heat treated (1050 °C in air for 8hrs) samples at room and high temperature. Fatigue tests were performed at heat treated samples at 1050 °C for samples with and without ablation. The test conditions were as similar as possible to the conditions in the AORA turbine. The results of the study provide an insight into tensile properties, fatigue properties and FOD. The results indicated a reduction in fatigue life for the samples with ablation damage, where crack nucleation occurred either at the edge or inside the ablation region and multisite cracking was observed under far field stresses that were the same than for pristine samples, which showed single cracks. Fracture surfaces indicate intergranular fracture, with the presence of secondary cracks and a lack of typical fatigue features, e.g., beach marks which was attributed to environmental effects and creep.
ContributorsShenoy, Sneha (Author) / Peralta, Pedro (Thesis advisor) / Solanki, Kiran (Committee member) / Sieradzki, Karl (Committee member) / Arizona State University (Publisher)
Created2017
Description
Tin (Sn) has a high-specific capacity (993 mAhg-1) as an anode material for Li-ion batteries. To overcome the poor cycling performance issue caused by its large volume expansion and pulverization during the charging and discharging process, many researchers put efforts into it. Most of the strategies are through nanostructured material design and introducing conductive polymer binders that serve as matrix of the active material in anode. This thesis aims for developing a novel method for preparing the anode to improve the capacity retention rate. This would require the anode to have high electrical conductivity, high ionic conductivity, and good mechanical properties, especially elasticity. Here the incorporation of a conducting polymer and a conductive hydrogel in Sn-based anodes using a one-step electrochemical deposition via a 3-electrode cell method is reported: the Sn particles and conductive component can be electrochemically synthesized and simultaneously deposited into a hybrid thin film onto the working electrode directly forming the anode. A well-defined three dimensional network structure consisting of Sn nanoparticles coated by conducting polymers is achieved. Such a conductive polymer-hydrogel network has multiple advantageous features: meshporous polymeric structure can offer the pathway for lithium ion transfer between the anode and electrolyte; the continuous electrically conductive polypyrrole network, with the electrostatic interaction with elastic, porous hydrogel, poly (2-acrylamido-2-methyl-1-propanesulfonic acid-co-acrylonitrile) (PAMPS) as both the crosslinker and doping anion for polypyrrole (PPy) can decrease the volume expansion by creating porous scaffold and softening the system itself. Furthermore, by increasing the amount of PAMPS and creating an interval can improve the cycling performance, resulting in improved capacity retention about 80% after 20 cycles, compared with only 54% of that of the control sample without PAMPS. The cycle is performed under current of 0.1 C.
ContributorsGao, Tianxiang (Author) / He, Ximin (Thesis advisor) / Sieradzki, Karl (Committee member) / Chan, Candace (Committee member) / Arizona State University (Publisher)
Created2015