Matching Items (2)
Filtering by
- All Subjects: chemical engineering
Description
The disordered nature of glass-forming melts results in two features for its dynamics i.e. non-Arrhenius and non-exponential behavior. Their macroscopic properties are studied through observing spatial heterogeneity of the molecular relaxation. Experiments performed in a low-frequency range tracks the flow of energy in time on slow degrees of freedom and transfer to the vibrational heat bath of the liquid, as is the case for microwave heating. High field measurements on supercooled liquids result in generation of fictive temperatures of the absorbing modes which eventually result in elevated true bath temperatures. The absorbed energy allows us to quantify the changes in the 'configurational', real sample, and electrode temperatures. The slow modes absorb energy on the structural relaxation time scale causing the increase of configurational temperature resulting in the rise of dielectric loss. Time-resolved high field dielectric relaxation experiments show the impact of 'configurational heating' for low frequencies of the electric field and samples that are thermally clamped to a thermostat. Relevant thermal behavior of monohydroxy alcohols is considerably different from the cases of simple non-associating liquids, due to their distinct origins of the prominent dielectric loss. Monohydroxy alcohols display very small changes due to observed nonthermal effects without increasing sample temperature. These changes have been reflected in polymers in our measurements.
ContributorsPathak, Ullas (Author) / Richert, Ranko (Thesis advisor) / Dai, Lenore (Thesis advisor) / Nielsen, David (Committee member) / Arizona State University (Publisher)
Created2012
Description
This dissertation provides a fundamental understanding of the impact of bulk polymer properties on the nanometer length scale modulus. The elastic modulus of amorphous organic thin films is examined using a surface wrinkling technique. Potential correlations between thin film behavior and intrinsic properties such as flexibility and chain length are explored. Thermal properties, glass transition temperature (Tg) and the coefficient of thermal expansion, are examined along with the moduli of these thin films. It is found that the nanometer length scale behavior of flexible polymers correlates to its bulk Tg and not the polymers intrinsic size. It is also found that decreases in the modulus of ultrathin flexible films is not correlated with the observed Tg decrease in films of the same thickness. Techniques to circumvent reductions from bulk modulus were also demonstrated. However, as chain flexibility is reduced the modulus becomes thickness independent down to 10 nm. Similarly for this series minor reductions in Tg were obtained. To further understand the impact of the intrinsic size and processing conditions; this wrinkling instability was also utilized to determine the modulus of small organic electronic materials at various deposition conditions. Lastly, this wrinkling instability is exploited for development of poly furfuryl alcohol wrinkles. A two-step wrinkling process is developed via an acid catalyzed polymerization of a drop cast solution of furfuryl alcohol and photo acid generator. The ability to control the surface topology and tune the wrinkle wavelength with processing parameters such as substrate temperature and photo acid generator concentration is also demonstrated. Well-ordered linear, circular, and curvilinear patterns are also obtained by selective ultraviolet exposure and polymerization of the furfuryl alcohol film. As a carbon precursor a thorough understanding of this wrinkling instability can have applications in a wide variety of technologies.
ContributorsTorres, Jessica (Author) / Vogt, Bryan D (Thesis advisor) / Stafford, Christopher M (Committee member) / Richert, Ranko (Committee member) / Rege, Kaushal (Committee member) / Dai, Lenore (Committee member) / Arizona State University (Publisher)
Created2011