ABSTRACT Pre-treated crumb rubber technologies are emerging as a new method to produce asphalt rubber mixtures in the field. A new crumb rubber modifier industrially known as "RuBind" is one such technology. RuBindTM is a "Reacted and Activated Rubber" (RAR) that acts like an elastomeric asphalt extender to improve the engineering properties of the binder and mixtures. It is intended to be used in a dry mixing process with the purpose of simplifying mixing at the asphalt plant. The objectives of this research study were to evaluate the rheological and aging properties of binders modified with RuBindTM and its compatibility with warm mix technology. Two binders were used for this study: Performance Grade (PG) 70-10 and PG 64-22, both modified with 25% by weight of asphalt binder. Laboratory test included: penetration, softening point, viscosity, Dynamic Shear Rheometer (DSR) and Bending Beam Rheometer (BBR). Tests were conducted under original, short and long -term aging conditions. Observations from the test results indicated that there is a better improvement when RuBindTM is added to a softer binder, in this case a PG 64-22. For short-term aging, the modified binder showed a similar aging index compared to the control. However, long term aging was favorable for the modified binders. The DSR results showed that the PG 64-22 binder high temperature would increase to 82 °C, and PG 70-10 would be increased to 76 °C, both favorable results. The intermediate temperatures also showed an improvement in fatigue resistance (as measured by the Superpave PG grading parameter |G*|sinä). Test results at low temperatures did not show a substantial improvement, but the results were favorable showing reduced stiffness with the addition of RuBindTM. The evaluation of warm mix additive using EvothermTM confirmed the manufacturer information that the product should have no negative effects on the binder properties; that is the modified binder can be used in a warm mix process. These results were encouraging and the recommendation was to continue with a follow up study with mixture tests using the RuBindTM modified binders.

Crumb rubber use in asphalt mixtures using wet process technology has been in practice for years in the United States with good performance history; however, it has some drawbacks that include the need for special blending equipment, high rubber-binder temperatures, and longer waiting time at mixing plants. Pre-treated crumb rubber technologies are emerging as a new method to produce asphalt rubber mixtures in the field. A new crumb rubber modifier known as Reacted and Activated Rubber (RAR) is one such technology. RAR (industrially known as “RARX”) acts like an Enhanced Elastomeric Asphalt Extender to improve the engineering properties of the binder and mixtures. It is intended to be used in a dry mixing process with the purpose of simplifying mixing at the asphalt plant. The objective of this research study was first to perform a Superpave mix design for determination of optimum asphalt content with 35% RAR by weight of binder; and secondly, analyse the performance of RAR modified mixtures prepared using the dry process against Crumb Rubber Modified (CRM) mixtures prepared using the wet process by conducting various laboratory tests. Performance Grade (PG) 64-22 binder was used to fabricate RAR and CRM mixtures and Performance Grade (PG) 70-10 was used to fabricate Control mixtures for this study. Laboratory tests included: Dynamic Modulus Test, Flow Number Test, Tensile Strength Ratio, Axial Cyclic Fatigue Test and C* Fracture Test. Observations from test results indicated that RAR mixes prepared through the dry process had excellent fatigue life, moisture resistance and cracking resistance compared to the other mixtures.

Crumb rubber use in asphalt mixtures by means of wet process technology has been in place for several years in the United States with good performance record; however, it has some shortcomings such as maintaining high mixing and compaction temperatures in the field production. Organosilane (OS), a nanotechnology chemical substantially improves the bonding between aggregate and asphalt by modifying the aggregate structure from hydrophilic to hydrophobic contributing to increased moisture resistance of conventional asphalt mixtures. Use of Organosilane also reduces the mixing and compaction temperatures and facilitates similar compaction effort at lower temperatures. The objective of this research study was first to perform a Superpave mix design for Crumb Rubber Modified Binder (CRMB) gap-graded mixture with and without Organosilane; and secondly, analyse the performance of CRMB mixtures with and without Organosilane by conducting various laboratory tests. Performance Grade (PG) 64-22 binder was used to create the gap-graded Hot Mix Asphalt (HMA) mixtures for this study. Laboratory tests included rotational viscometer binder test and mixtures tests: dynamic modulus, flow number, tensile strength ratio, and C* fracture test. Results from the tests indicated that the addition of Organosilane facilitated easier compaction efforts despite reduced mixing and compaction temperatures. Organosilane also modestly increased the moisture susceptibility and resistance to crack propagation yet retaining equal rutting resistance of the CRMB mixtures.

Better methods are necessary to fully account for anthropogenic impacts on ecosystems and the essential services provided by ecosystems that sustain human life. Current methods for assessing sustainability, such as life cycle assessment (LCA), typically focus on easily quantifiable indicators such as air emissions with no accounting for the essential ecosystem benefits that support human or industrial processes. For this reason, more comprehensive, transparent, and robust methods are necessary for holistic understanding of urban technosphere and ecosphere systems, including their interfaces. Incorporating ecosystem service indicators into LCA is an important step in spanning this knowledge gap.

For urban systems, many built environment processes have been investigated but need to be expanded with life cycle assessment for understanding ecosphere impacts. To pilot these new methods, a material inventory of the building infrastructure of Phoenix, Arizona can be coupled with LCA to gain perspective on the impacts assessment for built structures in Phoenix. This inventory will identify the origins of materials stocks, and the solid and air emissions waste associated with their raw material extraction, processing, and construction and identify key areas of future research necessary to fully account for ecosystem services in urban sustainability assessments. Based on this preliminary study, the ecosystem service impacts of metropolitan Phoenix stretch far beyond the county boundaries. A life cycle accounting of the Phoenix’s embedded building materials will inform policy and decision makers, assist with community education, and inform the urban sustainability community of consequences.

Crack sealing is considered one of the least expensive and cost effective maintenance activity used on pavements. In some cases, crack sealing suffers from premature failure due to various material, environmental, and construction issues. A survey that was conducted as part of this study showed that the highest sealant failure year occurring on the second year. Therefore, any attempt to increase the sealants’ service life by addressing and improving the sealant properties and their resistance to failure will benefit the effectiveness of this treatment.

The goal behind this study was to evaluate the potential improvement in performance of hot applied sealant material commonly used in the Phoenix area, and evaluate the performance of using a neat binder modified with crumb rubber (at 5 and 10% by weight of binder) as a low-grade sealing material. The sealants was also modified with crumb rubber at 2.5, and 5% by weight fo the sealant. Six ASTM tests were conducted for the comparison. These tests are the Standard Penetration Test (SPT) and Cone Penetration Test (CPT), Resilience Test, Softening Point Test, Brookfield Viscometer Test, and Dynamic Shear Rheometer (DSR).

The results showed that adding only crumb rubber to a neat binder for its potential use as a crack sealant is inadequate to meet the specifications expected for sealants. However, the modification of the sealant with crumb rubber showed some benefits, such as increased elasticity and decreased temperature susceptibility. A crumb rubber content of 2.5% by weight of the sealant was recommended.

The City of Phoenix Street Transportation Department partnered with the Rob and Melani Walton Sustainability Solutions Service at Arizona State University (ASU) and researchers from various ASU schools to evaluate the effectiveness, performance, and community perception of the new pavement coating. The data collection and analysis occurred across multiple neighborhoods and at varying times across days and/or months over the course of one year (July 15, 2020–July 14, 2021), allowing the team to study the impacts of the surface treatment under various weather conditions.