A series of pyrite thin films were synthesized using a novel sequential evaporation
technique to study the effects of substrate temperature on deposition rate and micro-structure of
the deposited material. Pyrite was deposited in a monolayer-by-monolayer fashion using
sequential evaporation of Fe under high vacuum, followed by sulfidation at high S pressures
(typically > 1 mTorr to 1 Torr). Thin films were synthesized using two different growth processes; a
one-step process in which a constant growth temperature is maintained throughout growth, and a
three-step process in which an initial low temperature seed layer is deposited, followed by a high
temperature layer, and then finished with a low temperature capping layer. Analysis methods to
analyze the properties of the films included Glancing Angle X-Ray Diffraction (GAXRD),
Rutherford Back-scattering Spectroscopy (RBS), Transmission Electron Microscopy (TEM),
Secondary Ion Mass Spectroscopy (SIMS), 2-point IV measurements, and Hall effect
measurements. Our results show that crystallinity of the pyrite thin film improves and grain size
increases with increasing substrate temperature. The sticking coefficient of Fe was found to
increase with increasing growth temperature, indicating that the Fe incorporation into the growing
film is a thermally activated process.
technique to study the effects of substrate temperature on deposition rate and micro-structure of
the deposited material. Pyrite was deposited in a monolayer-by-monolayer fashion using
sequential evaporation of Fe under high vacuum, followed by sulfidation at high S pressures
(typically > 1 mTorr to 1 Torr). Thin films were synthesized using two different growth processes; a
one-step process in which a constant growth temperature is maintained throughout growth, and a
three-step process in which an initial low temperature seed layer is deposited, followed by a high
temperature layer, and then finished with a low temperature capping layer. Analysis methods to
analyze the properties of the films included Glancing Angle X-Ray Diffraction (GAXRD),
Rutherford Back-scattering Spectroscopy (RBS), Transmission Electron Microscopy (TEM),
Secondary Ion Mass Spectroscopy (SIMS), 2-point IV measurements, and Hall effect
measurements. Our results show that crystallinity of the pyrite thin film improves and grain size
increases with increasing substrate temperature. The sticking coefficient of Fe was found to
increase with increasing growth temperature, indicating that the Fe incorporation into the growing
film is a thermally activated process.
ContributorsWertheim, Alex (Author) / Newman, Nathan (Thesis advisor) / Singh, Rakesh (Committee member) / Bertoni, Mariana (Committee member) / Arizona State University (Publisher)
Created2014
Description
Measurements of the geometrical magnetoresistance of a conventional semiconductor, gallium arsenide (GaAs), and a more recently developed semiconductor, iron pyrite (FeS2) were measured in the Corbino disc geometry as a function of magnetic field to determine the carrier mobility (μm). These results were compared with measurements of the Hall mobility (μH) made in the Van der Pauw configuration. The scattering coefficient (ξ), defined as the ratio between magnetoresistance and Hall mobility (μm/μH), was determined experimentally for GaAs and natural pyrite from 300 K to 4.2 K. The effect of contact resistance and heating on the measurement accuracy is discussed.
ContributorsRavi, Aditya (Author) / Newman, Nathan (Thesis advisor) / Singh, Rakesh (Committee member) / Ferry, David K. (Committee member) / Arizona State University (Publisher)
Created2016